- 熔體流動速率 [g/10min]: 2.2
- 密度 [g/cm3]: 1.22
- 彎曲強度 [MPa]: 108.0
- 熱變形溫度 [℃]: 178.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.22 g/cc | 0.0441 lb/in3 | |
| Melt Flow | 2.2 g/10 min @Load 2.16 kg, Temperature 235 °C | 2.2 g/10 min @Load 4.76 lb, Temperature 455 °F | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 108 MPa | 15700 psi | 5 mm/min |
| Elongation at Break | 5.0 % | 5.0 % | 5 mm/min |
| Tensile Modulus | 7.30 GPa | 1060 ksi | 1 mm/min |
| Charpy Impact Unnotched | 7.40 J/cm2 | 35.2 ft-lb/in2 | |
| 8.29 J/cm2 @Temperature -30.0 °C | 39.5 ft-lb/in2 @Temperature -22.0 °F | ||
| Charpy Impact, Notched | 1.25 J/cm2 | 5.95 ft-lb/in2 | |
| 0.990 J/cm2 @Temperature -30.0 °C | 4.71 ft-lb/in2 @Temperature -22.0 °F | ||
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 2.00e+13 ohm-cm | 2.00e+13 ohm-cm | |
| Surface Resistance | 6.00e+12 ohm | 6.00e+12 ohm | |
| Dielectric Strength | 22.0 kV/mm | 559 kV/in | |
| Comparative Tracking Index | 300 V | 300 V | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 50.0 μm/m-°C @Temperature 20.0 °C | 27.8 μin/in-°F @Temperature 68.0 °F | |
| Melting Point | 183 °C | 361 °F | (Dry) |
| Deflection Temperature at 0.46 MPa (66 psi) | 178 °C | 352 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 170 °C | 338 °F | |
| Vicat Softening Point | 170 °C | 338 °F | 50°C/hr; 50N |
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | |
| HB @Thickness 3.10 mm | HB @Thickness 0.122 in | ||