- 熔體流動速率 [g/10min]: 7.0
- 密度 [g/cm3]: 1.24
- 拉伸強度 [MPa]: 39.0
- 熱變形溫度 [℃]: 165.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.24 g/cc | 0.0448 lb/in3 | |
| Melt Flow | 7.0 g/10 min @Load 2.16 kg, Temperature 235 °C | 7.0 g/10 min @Load 4.76 lb, Temperature 455 °F | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 39.0 MPa | 5660 psi | 50 mm/min |
| Elongation at Break | 40 % | 40 % | Nominal Strain; 50 mm/min |
| Elongation at Yield | 4.0 % | 4.0 % | 50 mm/min |
| Tensile Modulus | 1.94 GPa | 281 ksi | 1 mm/min |
| Charpy Impact Unnotched | NB | NB | |
| 7.33 J/cm2 @Temperature -30.0 °C | 34.9 ft-lb/in2 @Temperature -22.0 °F | ||
| Charpy Impact, Notched | 0.510 J/cm2 | 2.43 ft-lb/in2 | |
| 0.460 J/cm2 @Temperature -30.0 °C | 2.19 ft-lb/in2 @Temperature -22.0 °F | ||
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | |
| Surface Resistance | 1.00e+14 ohm | 1.00e+14 ohm | |
| Dielectric Strength | 40.0 kV/mm | 1020 kV/in | |
| Comparative Tracking Index | 600 V | 600 V | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 70.0 μm/m-°C @Temperature 20.0 °C | 38.9 μin/in-°F @Temperature 68.0 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 165 °C | 329 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 60.0 °C | 140 °F | |
| Vicat Softening Point | 165 °C | 329 °F | 50°C/hr; 50N |
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | |
| HB @Thickness 3.10 mm | HB @Thickness 0.122 in | ||