- 熔體流動速率 [g/10min]: 7.0
- 密度 [g/cm3]: 1.24
- 吸水率 [%]: 1.3
- 拉伸強度 [MPa]: 42.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.24 g/cc | 0.0448 lb/in3 | |
| Water Absorption | 1.3 % | 1.3 % | |
| Melt Flow | 7.0 g/10 min @Load 2.16 kg, Temperature 235 °C | 7.0 g/10 min @Load 4.76 lb, Temperature 455 °F | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 42.0 MPa | 6090 psi | 50 mm/min |
| Elongation at Break | 37 % | 37 % | Nominal Strain; 50 mm/min |
| Elongation at Yield | 4.0 % | 4.0 % | 50 mm/min |
| Tensile Modulus | 2.10 GPa | 305 ksi | 1 mm/min |
| Charpy Impact Unnotched | 5.16 J/cm2 | 24.6 ft-lb/in2 | |
| 5.81 J/cm2 @Temperature -30.0 °C | 27.7 ft-lb/in2 @Temperature -22.0 °F | ||
| Charpy Impact, Notched | 0.500 J/cm2 | 2.38 ft-lb/in2 | |
| 0.470 J/cm2 @Temperature -30.0 °C | 2.24 ft-lb/in2 @Temperature -22.0 °F | ||
| Thermal Properties | Metric | English | Comments |
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | |
| HB @Thickness 3.10 mm | HB @Thickness 0.122 in | ||