- 熔體流動速率 [g/10min]: 4.5
- 拉伸強度 [MPa]: 68.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Flow | 4.5 g/10 min @Load 2.16 kg, Temperature 235 °C | 4.5 g/10 min @Load 4.76 lb, Temperature 455 °F | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 68.0 MPa | 9860 psi | 50 mm/min |
| Elongation at Break | 15 % | 15 % | Nominal Strain; 50 mm/min |
| Elongation at Yield | 4.0 % | 4.0 % | 50 mm/min |
| Tensile Modulus | 3.32 GPa | 482 ksi | 1 mm/min |
| Charpy Impact Unnotched | 8.50 J/cm2 | 40.5 ft-lb/in2 | |
| 9.17 J/cm2 @Temperature -30.0 °C | 43.6 ft-lb/in2 @Temperature -22.0 °F | ||
| Charpy Impact, Notched | 1.06 J/cm2 | 5.04 ft-lb/in2 | |
| 0.550 J/cm2 @Temperature -30.0 °C | 2.62 ft-lb/in2 @Temperature -22.0 °F | ||
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 65.0 μm/m-°C @Temperature 20.0 °C | 36.1 μin/in-°F @Temperature 68.0 °F | |