- 熔體流動速率 [g/10min]: 2.2
- 密度 [g/cm3]: 1.42
- 吸水率 [%]: 1.1
- 彎曲強度 [MPa]: 146.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.42 g/cc | 0.0513 lb/in3 | |
| Water Absorption | 1.1 % | 1.1 % | |
| Melt Flow | 2.2 g/10 min @Load 2.16 kg, Temperature 235 °C | 2.2 g/10 min @Load 4.76 lb, Temperature 455 °F | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 146 MPa | 21200 psi | 5 mm/min |
| Elongation at Break | 4.0 % | 4.0 % | 5 mm/min |
| Tensile Modulus | 12.4 GPa | 1800 ksi | 1 mm/min |
| Charpy Impact Unnotched | 6.69 J/cm2 | 31.8 ft-lb/in2 | |
| 7.50 J/cm2 @Temperature -30.0 °C | 35.7 ft-lb/in2 @Temperature -22.0 °F | ||
| Charpy Impact, Notched | 1.21 J/cm2 | 5.76 ft-lb/in2 | |
| 1.02 J/cm2 @Temperature -30.0 °C | 4.85 ft-lb/in2 @Temperature -22.0 °F | ||
| Thermal Properties | Metric | English | Comments |
| Melting Point | 183 °C | 361 °F | 10°C/min |
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | |
| HB @Thickness 3.10 mm | HB @Thickness 0.122 in | ||