- 熔體流動速率 [g/10min]: 17.7
- 密度 [g/cm3]: 3.8
- 彎曲強度 [MPa]: 34.0
- 熱變形溫度 [℃]: 170.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 3.80 g/cc | 0.137 lb/in3 | |
| Melt Flow | 17.7 g/10 min @Load 5.00 kg, Temperature 235 °C | 17.7 g/10 min @Load 11.0 lb, Temperature 455 °F | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 34.0 MPa | 4930 psi | 5 mm/min |
| Elongation at Break | 4.0 % | 4.0 % | 5 mm/min |
| Tensile Modulus | 4.60 GPa | 667 ksi | 1 mm/min |
| Charpy Impact Unnotched | 1.69 J/cm2 | 8.04 ft-lb/in2 | |
| 1.96 J/cm2 @Temperature -30.0 °C | 9.33 ft-lb/in2 @Temperature -22.0 °F | ||
| Charpy Impact, Notched | 0.390 J/cm2 | 1.86 ft-lb/in2 | |
| 0.380 J/cm2 @Temperature -30.0 °C | 1.81 ft-lb/in2 @Temperature -22.0 °F | ||
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 10000 ohm-cm | 10000 ohm-cm | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 70.0 μm/m-°C @Temperature 20.0 °C | 38.9 μin/in-°F @Temperature 68.0 °F | |
| Melting Point | 183 °C | 361 °F | (Dry) |
| Deflection Temperature at 0.46 MPa (66 psi) | 170 °C | 338 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 100 °C | 212 °F | |
| Vicat Softening Point | 170 °C | 338 °F | 50°C/hr; 50N |
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | |
| HB @Thickness 3.10 mm | HB @Thickness 0.122 in | ||