- 熔體流動速率 [g/10min]: 11.2
- 密度 [g/cm3]: 1.05
- 拉伸強度 [MPa]: 25.0
- 熱變形溫度 [℃]: 130.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.05 g/cc | 0.0379 lb/in3 | |
| Melt Flow | 11.2 g/10 min @Load 2.16 kg, Temperature 235 °C | 11.2 g/10 min @Load 4.76 lb, Temperature 455 °F | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 25.0 MPa | 3630 psi | 50 mm/min |
| Elongation at Break | >= 50 % | >= 50 % | Nominal Strain; 50 mm/min |
| Elongation at Yield | 30 % | 30 % | 50 mm/min |
| Tensile Modulus | 0.375 GPa | 54.4 ksi | 1 mm/min |
| Charpy Impact Unnotched | NB | NB | |
| NB | NB | Low Temp | |
| Charpy Impact, Notched | NB | NB | |
| 0.660 J/cm2 @Temperature -30.0 °C | 3.14 ft-lb/in2 @Temperature -22.0 °F | ||
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+11 ohm-cm | 1.00e+11 ohm-cm | |
| Surface Resistance | 5.00e+11 ohm | 5.00e+11 ohm | |
| Dielectric Strength | 23.0 kV/mm | 584 kV/in | |
| Comparative Tracking Index | 600 V | 600 V | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 110 μm/m-°C @Temperature 20.0 °C | 61.1 μin/in-°F @Temperature 68.0 °F | |
| Melting Point | 175 °C | 347 °F | (Dry) |
| Deflection Temperature at 0.46 MPa (66 psi) | 130 °C | 266 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 45.0 °C | 113 °F | |
| Vicat Softening Point | 140 °C | 284 °F | 50°C/hr; 50N |
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | |
| HB @Thickness 3.10 mm | HB @Thickness 0.122 in | ||