- 熔體流動速率 [g/10min]: 7.9
- 密度 [g/cm3]: 1.08
- 拉伸強度 [MPa]: 27.0
- 熱變形溫度 [℃]: 147.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.08 g/cc | 0.0390 lb/in3 | |
| Melt Flow | 7.9 g/10 min @Load 2.16 kg, Temperature 235 °C | 7.9 g/10 min @Load 4.76 lb, Temperature 455 °F | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 27.0 MPa | 3920 psi | 50 mm/min |
| Elongation at Break | >= 50 % | >= 50 % | Nominal Strain; 50 mm/min |
| Elongation at Yield | 35 % | 35 % | 50 mm/min |
| Tensile Modulus | 0.580 GPa | 84.1 ksi | 1 mm/min |
| Charpy Impact Unnotched | NB | NB | |
| NB | NB | Low Temp | |
| Charpy Impact, Notched | NB | NB | |
| 0.420 J/cm2 @Temperature -30.0 °C | 2.00 ft-lb/in2 @Temperature -22.0 °F | ||
| Electrical Properties | Metric | English | Comments |
| Dielectric Strength | 18.0 kV/mm | 457 kV/in | |
| Comparative Tracking Index | 600 V | 600 V | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 110 μm/m-°C @Temperature 20.0 °C | 61.1 μin/in-°F @Temperature 68.0 °F | |
| Melting Point | 178 °C | 352 °F | (Dry) |
| Deflection Temperature at 0.46 MPa (66 psi) | 147 °C | 297 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 55.0 °C | 131 °F | |
| Vicat Softening Point | 136 °C | 277 °F | 50°C/hr; 50N |
| Flammability, UL94 | V-2 @Thickness 1.60 mm | V-2 @Thickness 0.0630 in | |
| V-2 @Thickness 3.20 mm | V-2 @Thickness 0.126 in | ||
| Oxygen Index | 27 % | 27 % | |