- 熔體流動速率 [g/10min]: 11.2
- 密度 [g/cm3]: 1.05
- 吸水率 [%]: 1.6
- 拉伸強(qiáng)度 [MPa]: 27.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.05 g/cc | 0.0379 lb/in3 | |
| Water Absorption | 1.6 % | 1.6 % | |
| Melt Flow | 11.2 g/10 min @Load 2.16 kg, Temperature 235 °C | 11.2 g/10 min @Load 4.76 lb, Temperature 455 °F | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 27.0 MPa | 3920 psi | 50 mm/min |
| Elongation at Break | >= 50 % | >= 50 % | Nominal Strain; 50 mm/min |
| Elongation at Yield | 42 % | 42 % | 50 mm/min |
| Tensile Modulus | 0.405 GPa | 58.7 ksi | 1 mm/min |
| Electrical Properties | Metric | English | Comments |
| Dissipation Factor | 0.000363 @Frequency 1e+6 Hz | 0.000363 @Frequency 1e+6 Hz | |
| 0.000988 @Frequency 100 Hz | 0.000988 @Frequency 100 Hz | ||
| Thermal Properties | Metric | English | Comments |
| Melting Point | 175 °C | 347 °F | 10°C/min |
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | |
| HB @Thickness 3.10 mm | HB @Thickness 0.122 in | ||