- 熔體流動速率 [g/10min]: 5.7
- 密度 [g/cm3]: 1.03
- 拉伸強度 [MPa]: 37.0
- 熱變形溫度 [℃]: 145.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.03 g/cc | 0.0372 lb/in3 | |
| Melt Flow | 5.7 g/10 min @Load 10.0 kg, Temperature 235 °C | 5.7 g/10 min @Load 22.0 lb, Temperature 455 °F | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 37.0 MPa | 5370 psi | 50 mm/min |
| Elongation at Break | >= 50 % | >= 50 % | Nominal Strain; 50 mm/min |
| Elongation at Yield | 6.0 % | 6.0 % | 50 mm/min |
| Tensile Modulus | 1.28 GPa | 186 ksi | 1 mm/min |
| Charpy Impact Unnotched | NB | NB | |
| NB | NB | Low Temp | |
| Charpy Impact, Notched | 1.49 J/cm2 | 7.09 ft-lb/in2 | |
| 1.32 J/cm2 @Temperature -30.0 °C | 6.28 ft-lb/in2 @Temperature -22.0 °F | ||
| Electrical Properties | Metric | English | Comments |
| Dielectric Strength | 30.0 kV/mm | 762 kV/in | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 85.0 μm/m-°C @Temperature 20.0 °C | 47.2 μin/in-°F @Temperature 68.0 °F | |
| Melting Point | 183 °C | 361 °F | (Dry) |
| Deflection Temperature at 0.46 MPa (66 psi) | 145 °C | 293 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 50.0 °C | 122 °F | |
| Vicat Softening Point | 160 °C | 320 °F | 50°C/hr; 50N |