- 熔體流動(dòng)速率 [g/10min]: 95.1
- 拉伸強(qiáng)度 [MPa]: 48.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Flow | 95.1 g/10 min @Load 2.16 kg, Temperature 235 °C | 95.1 g/10 min @Load 4.76 lb, Temperature 455 °F | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 48.0 MPa | 6960 psi | 50 mm/min |
| Elongation at Break | >= 50 % | >= 50 % | Nominal Strain; 50 mm/min |
| Elongation at Yield | 5.0 % | 5.0 % | 50 mm/min |
| Tensile Modulus | 1.92 GPa | 278 ksi | 1 mm/min |
| Charpy Impact Unnotched | NB | NB | |
| Charpy Impact, Notched | 0.490 J/cm2 | 2.33 ft-lb/in2 | |
| 0.480 J/cm2 @Temperature -30.0 °C | 2.28 ft-lb/in2 @Temperature -22.0 °F | ||
| Thermal Properties | Metric | English | Comments |
| Flammability, UL94 | V-0 @Thickness 0.800 mm | V-0 @Thickness 0.0315 in | |
| V-0 @Thickness 1.60 mm | V-0 @Thickness 0.0630 in | ||
| Oxygen Index | 33 % | 33 % | |