- 熔體流動速率 [g/10min]: 1.8
- 密度 [g/cm3]: 1.26
- 彎曲強度 [MPa]: 112.0
- 熱變形溫度 [℃]: 180.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.26 g/cc | 0.0455 lb/in3 | |
| Melt Flow | 1.8 g/10 min @Load 2.16 kg, Temperature 235 °C | 1.8 g/10 min @Load 4.76 lb, Temperature 455 °F | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 112 MPa | 16200 psi | 5 mm/min |
| Elongation at Break | 8.0 % | 8.0 % | 5 mm/min |
| Tensile Modulus | 7.80 GPa | 1130 ksi | 1 mm/min |
| Charpy Impact Unnotched | 8.24 J/cm2 | 39.2 ft-lb/in2 | |
| 8.39 J/cm2 @Temperature -30.0 °C | 39.9 ft-lb/in2 @Temperature -22.0 °F | ||
| Charpy Impact, Notched | 2.06 J/cm2 | 9.80 ft-lb/in2 | |
| 1.20 J/cm2 @Temperature -30.0 °C | 5.71 ft-lb/in2 @Temperature -22.0 °F | ||
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 7.00e+13 ohm-cm | 7.00e+13 ohm-cm | |
| Surface Resistance | 1.00e+14 ohm | 1.00e+14 ohm | |
| Dielectric Strength | 45.0 kV/mm | 1140 kV/in | |
| Comparative Tracking Index | 600 V | 600 V | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 50.0 μm/m-°C @Temperature 20.0 °C | 27.8 μin/in-°F @Temperature 68.0 °F | |
| Melting Point | 183 °C | 361 °F | (Dry) |
| Deflection Temperature at 0.46 MPa (66 psi) | 180 °C | 356 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 175 °C | 347 °F | |
| Vicat Softening Point | 170 °C | 338 °F | 50°C/hr; 50N |
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | |
| HB @Thickness 3.10 mm | HB @Thickness 0.122 in | ||
| Oxygen Index | 22 % | 22 % | |