- 密度 [g/cm3]: 1.0
- 吸水率 [%]: 1.3
- 拉伸強度 [MPa]: 18.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.00 g/cc | 0.0361 lb/in3 | |
| Water Absorption | 1.3 % | 1.3 % | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 18.0 MPa @Strain 50.0 % | 2610 psi @Strain 50.0 % | 50 mm/min |
| Elongation at Break | >= 50 % | >= 50 % | Nominal Strain; 50 mm/min |
| Tensile Modulus | 0.195 GPa | 28.3 ksi | 1 mm/min |
| Charpy Impact Unnotched | NB | NB | |
| NB | NB | Low Temp | |
| Charpy Impact, Notched | NB | NB | |
| 1.80 J/cm2 @Temperature -30.0 °C | 8.57 ft-lb/in2 @Temperature -22.0 °F | ||
| Thermal Properties | Metric | English | Comments |
| Melting Point | 175 °C | 347 °F | 10°C/min |
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | |
| HB @Thickness 3.10 mm | HB @Thickness 0.122 in | ||