- 熔體流動速率 [g/10min]: 4.5
- 拉伸強度 [MPa]: 65.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Flow | 4.5 g/10 min @Load 2.16 kg, Temperature 235 °C | 4.5 g/10 min @Load 4.76 lb, Temperature 455 °F | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 65.0 MPa | 9430 psi | 50 mm/min |
| Elongation at Break | 17.3 % | 17.3 % | Nominal Strain; 50 mm/min |
| Elongation at Yield | 4.0 % | 4.0 % | 50 mm/min |
| Tensile Modulus | 2.87 GPa | 416 ksi | 1 mm/min |
| Charpy Impact Unnotched | 10.2 J/cm2 | 48.5 ft-lb/in2 | |
| 10.0 J/cm2 @Temperature -30.0 °C | 47.6 ft-lb/in2 @Temperature -22.0 °F | ||
| Charpy Impact, Notched | 1.00 J/cm2 | 4.76 ft-lb/in2 | |
| 0.440 J/cm2 @Temperature -30.0 °C | 2.09 ft-lb/in2 @Temperature -22.0 °F | ||
| Thermal Properties | Metric | English | Comments |
| UL RTI, Electrical | 65.0 °C | 149 °F | |
| UL RTI, Mechanical with Impact | 65.0 °C | 149 °F | |
| UL RTI, Mechanical without Impact | 65.0 °C | 149 °F | |