- 熔體流動速率 [g/10min]: 2.2
- 密度 [g/cm3]: 1.22
- 吸水率 [%]: 1.2
- 彎曲強度 [MPa]: 110.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.22 g/cc | 0.0441 lb/in3 | |
| Water Absorption | 1.2 % | 1.2 % | |
| Melt Flow | 2.2 g/10 min @Load 2.16 kg, Temperature 235 °C | 2.2 g/10 min @Load 4.76 lb, Temperature 455 °F | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 110 MPa | 16000 psi | 5 mm/min |
| Elongation at Break | 5.0 % | 5.0 % | 5 mm/min |
| Tensile Modulus | 7.69 GPa | 1120 ksi | 1 mm/min |
| Charpy Impact Unnotched | 7.80 J/cm2 | 37.1 ft-lb/in2 | |
| 8.49 J/cm2 @Temperature -30.0 °C | 40.4 ft-lb/in2 @Temperature -22.0 °F | ||
| Charpy Impact, Notched | 1.27 J/cm2 | 6.04 ft-lb/in2 | |
| 0.940 J/cm2 @Temperature -30.0 °C | 4.47 ft-lb/in2 @Temperature -22.0 °F | ||
| Electrical Properties | Metric | English | Comments |
| Dissipation Factor | 0.00046 @Frequency 1e+6 Hz | 0.00046 @Frequency 1e+6 Hz | |
| 0.000517 @Frequency 100 Hz | 0.000517 @Frequency 100 Hz | ||
| Thermal Properties | Metric | English | Comments |
| Melting Point | 183 °C | 361 °F | 10°C/min |
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | |
| HB @Thickness 3.10 mm | HB @Thickness 0.122 in | ||