- 熔體流動(dòng)速率 [g/10min]: 27.5
- 密度 [g/cm3]: 1.11
- 拉伸強(qiáng)度 [MPa]: 43.0
- 熱變形溫度 [℃]: 156.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.11 g/cc | 0.0401 lb/in3 | |
| Melt Flow | 27.5 g/10 min @Load 2.16 kg, Temperature 235 °C | 27.5 g/10 min @Load 4.76 lb, Temperature 455 °F | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 43.0 MPa | 6240 psi | 50 mm/min |
| Elongation at Break | >= 50 % | >= 50 % | Nominal Strain; 50 mm/min |
| Elongation at Yield | 6.0 % | 6.0 % | 50 mm/min |
| Tensile Modulus | 1.86 GPa | 270 ksi | 1 mm/min |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | |
| Surface Resistance | 1.00e+14 ohm | 1.00e+14 ohm | |
| Dielectric Strength | 20.0 kV/mm | 508 kV/in | |
| Comparative Tracking Index | 600 V | 600 V | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 100 μm/m-°C @Temperature 20.0 °C | 55.6 μin/in-°F @Temperature 68.0 °F | |
| Melting Point | 183 °C | 361 °F | (Dry) |
| Deflection Temperature at 0.46 MPa (66 psi) | 156 °C | 313 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 52.0 °C | 126 °F | |
| Vicat Softening Point | 165 °C | 329 °F | 50°C/hr; 50N |
| Flammability, UL94 | V-2 @Thickness 1.60 mm | V-2 @Thickness 0.0630 in | |
| V-2 @Thickness 3.20 mm | V-2 @Thickness 0.126 in | ||
| Oxygen Index | 30 % | 30 % | |