- 熔體流動速率 [g/10min]: 9.0
- 密度 [g/cm3]: 1.07
- 拉伸強度 [MPa]: 21.0
- 彎曲模量 [MPa]: 1.345
- 熱變形溫度 [℃]: 186.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Bulk Density | 0.460 g/cc | 0.0166 lb/in3 | ASTM D1895 | ||
| Density | 1.07 g/cc | 0.0387 lb/in3 | Sintered Part; ASTM D792 | ||
| Particle Size | 95 μm | 95 μm | Average D50; Laser Diffraction | ||
| 45 - 151 μm | 45 - 151 μm | Range (D10 to D90); Laser Diffraction | |||
| Melt Flow | 9.0 g/10 min @Load 5.00 kg, Temperature 235 °C | 9.0 g/10 min @Load 11.0 lb, Temperature 455 °F | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 39.0 MPa | 5660 psi | Z direction; ASTM D638 | ||
| 46.0 MPa | 6670 psi | XY direction; ASTM D638 | |||
| Tensile Strength, Yield | 21.0 MPa | 3050 psi | Z direction; ASTM D638 | ||
| 26.0 MPa | 3770 psi | XY direction; ASTM D638 | |||
| Elongation at Break | 21 % | 21 % | Z direction; ASTM D638 | ||
| 38 % | 38 % | XY direction; ASTM D638 | |||
| Flexural Modulus | 1.345 GPa | 195.1 ksi | ASTM D790 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 189 °C | 372 °F | ASTM D3418 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 186 °C | 367 °F | ASTM D648 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 70.0 °C | 158 °F | ASTM D648 | ||
| Descriptive Properties | |||||
| Color | White | ||||
| Flammability, 12 Sec. Burn | Pass | FAR 25.853 | |||
| Flammability, 60 Sec. Burn | Pass | FAR 25.853 | |||
| Smoke Density | Pass | ||||