- 熔體流動速率 [g/10min]: 0.8
- 密度 [g/cm3]: 1.0
- 吸水率 [%]: 0.23
- 缺口沖擊強度: 0.4
- 拉伸強度 [MPa]: 15.0
- 斷裂伸長率 [%]: 51.7
- 彎曲強度 [MPa]: 40.0
- 彎曲模量 [MPa]: 0.380
- 硬度: 105.0
- 熱變形溫度 [℃]: 70.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.00 - 1.05 g/cc | 0.0361 - 0.0379 lb/in3 | Average value: 1.03 g/cc Grade Count:36 |
| Water Absorption | 0.230 - 1.90 % | 0.230 - 1.90 % | Average value: 1.26 % Grade Count:19 |
| Moisture Absorption at Equilibrium | 0.750 - 1.10 % | 0.750 - 1.10 % | Average value: 0.943 % Grade Count:7 |
| Linear Mold Shrinkage | 0.00400 - 0.0180 cm/cm | 0.00400 - 0.0180 in/in | Average value: 0.0114 cm/cm Grade Count:4 |
| Melt Flow | 0.800 - 56.0 g/10 min | 0.800 - 56.0 g/10 min | Average value: 16.7 g/10 min Grade Count:18 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 105 - 110 | 105 - 110 | Average value: 107 Grade Count:6 |
| Tensile Strength, Ultimate | 40.0 - 68.9 MPa | 5800 - 10000 psi | Average value: 52.3 MPa Grade Count:14 |
| Tensile Strength, Yield | 15.0 - 44.0 MPa | 2180 - 6380 psi | Average value: 35.1 MPa Grade Count:25 |
| Elongation at Break | 10.0 - 400 % | 10.0 - 400 % | Average value: 126 % Grade Count:37 |
| Elongation at Yield | 5.00 - 42.0 % | 5.00 - 42.0 % | Average value: 17.1 % Grade Count:24 |
| Modulus of Elasticity | 0.185 - 1.80 GPa | 26.8 - 261 ksi | Average value: 1.08 GPa Grade Count:30 |
| Flexural Yield Strength | 51.7 - 89.6 MPa | 7500 - 13000 psi | Average value: 77.0 MPa Grade Count:3 |
| Flexural Modulus | 0.380 - 1.38 GPa | 55.1 - 200 ksi | Average value: 0.985 GPa Grade Count:11 |
| Izod Impact, Notched | 0.400 - 8.01 J/cm | 0.749 - 15.0 ft-lb/in | Average value: 2.40 J/cm Grade Count:9 |
| 0.260 - 0.260 J/cm @Temperature -40.0 - -40.0 °C | 0.487 - 0.487 ft-lb/in @Temperature -40.0 - -40.0 °F | Average value: 0.260 J/cm Grade Count:1 | |
| Izod Impact, Unnotched | 6.41 - 5340 J/cm | 12.0 - 10000 ft-lb/in | Average value: 6.41 J/cm Grade Count:3 |
| Charpy Impact Unnotched | 1000 J/cm2 - NB | 4760 ft-lb/in2 - NB | Grade Count:19 |
| 999.9 - 999.9 J/cm2 @Temperature -30.0 - -30.0 °C | 4759 - 4759 ft-lb/in2 @Temperature -22.0 - -22.0 °F | Grade Count:2 | |
| Charpy Impact, Notched | 0.730 J/cm2 - NB | 3.47 ft-lb/in2 - NB | Average value: 1.88 J/cm2 Grade Count:18 |
| 0.490 - 2.42 J/cm2 @Temperature -30.0 - -30.0 °C | 2.33 - 11.5 ft-lb/in2 @Temperature -22.0 - -22.0 °F | Average value: 1.17 J/cm2 Grade Count:18 | |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+11 - 2.00e+15 ohm-cm | 1.00e+11 - 2.00e+15 ohm-cm | Average value: 2.79e+14 ohm-cm Grade Count:13 |
| Surface Resistance | 5.00e+11 - 1.00e+14 ohm | 5.00e+11 - 1.00e+14 ohm | Average value: 6.72e+13 ohm Grade Count:9 |
| Dielectric Constant | 3.10 - 4.00 | 3.10 - 4.00 | Average value: 3.55 Grade Count:4 |
| Dielectric Strength | 19.7 - 40.0 kV/mm | 500 - 1020 kV/in | Average value: 29.2 kV/mm Grade Count:13 |
| Dissipation Factor | 0.000325 - 0.0500 | 0.000325 - 0.0500 | Average value: 0.00538 Grade Count:7 |
| Comparative Tracking Index | 600 V | 600 V | Average value: 600 V Grade Count:6 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 85.0 - 120 μm/m-°C | 47.2 - 66.7 μin/in-°F | Average value: 96.4 μm/m-°C Grade Count:14 |
| Thermal Conductivity | 0.230 - 0.346 W/m-K | 1.60 - 2.40 BTU-in/hr-ft2-°F | Average value: 0.276 W/m-K Grade Count:4 |
| Melting Point | 175 - 191 °C | 347 - 376 °F | Average value: 183 °C Grade Count:31 |
| Maximum Service Temperature, Air | 80.0 - 150 °C | 176 - 302 °F | Average value: 103 °C Grade Count:3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 70.0 - 150 °C | 158 - 302 °F | Average value: 140 °C Grade Count:20 |
| Deflection Temperature at 1.8 MPa (264 psi) | 40.0 - 55.0 °C | 104 - 131 °F | Average value: 49.8 °C Grade Count:24 |
| Vicat Softening Point | 140 - 160 °C | 284 - 320 °F | Average value: 154 °C Grade Count:11 |
| Flammability, UL94 | HB - V-2 | HB - V-2 | Grade Count:22 |
| Oxygen Index | 22.0 - 25.0 % | 22.0 - 25.0 % | Average value: 24.0 % Grade Count:3 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 216 - 282 °C | 420 - 540 °F | Average value: 251 °C Grade Count:3 |
| Mold Temperature | 25.0 - 65.6 °C | 77.0 - 150 °F | Average value: 49.4 °C Grade Count:4 |
| Drying Temperature | 79.4 - 80.0 °C | 175 - 176 °F | Average value: 79.8 °C Grade Count:3 |
| Injection Pressure | 68.9 - 103 MPa | 10000 - 15000 psi | Average value: 86.2 MPa Grade Count:3 |