- 吸水率 [%]: 0.1
- 缺口沖擊強(qiáng)度: 1.49
- 拉伸強(qiáng)度 [MPa]: 107.0
- 彎曲模量 [MPa]: 5.86
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.24 g/cc | 1.24 g/cc | Method A; ASTM D792 |
| Water Absorption | 0.10 % | 0.10 % | at 24 hrs; ASTM D570 |
| Linear Mold Shrinkage | 0.0020 - 0.0030 cm/cm | 0.0020 - 0.0030 in/in | ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0070 - 0.0080 cm/cm | 0.0070 - 0.0080 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 106 MPa | 15400 psi | ASTM D638 |
| Tensile Strength, Yield | 107 MPa | 15500 psi | ASTM D638 |
| Elongation at Break | 4.7 % | 4.7 % | ASTM D638 |
| Elongation at Yield | 4.2 % | 4.2 % | ASTM D638 |
| Tensile Modulus | 6.55 GPa | 950 ksi | ASTM D638 |
| Flexural Strength | 165 MPa | 23900 psi | ASTM D790 |
| Flexural Modulus | 5.86 GPa | 850 ksi | ASTM D790 |
| Izod Impact, Notched | 1.49 J/cm @Thickness 3.18 mm | 2.79 ft-lb/in @Thickness 0.125 in | ASTM D256 |
| Izod Impact, Unnotched | 9.50 J/cm @Thickness 3.18 mm | 17.8 ft-lb/in @Thickness 0.125 in | ASTM D256 |
| Izod Impact, Notched (ISO) | 15.0 kJ/m2 | 7.14 ft-lb/in2 | ISO 180 |
| Izod Impact, Unnotched (ISO) | 58.1 kJ/m2 | 27.6 ft-lb/in2 | ISO 180 |
| Falling Dart Impact | 13.0 J | 9.59 ft-lb | ASTM D3763 |
| Impact Test | 3.61 J | 2.66 ft-lb | Multi-Axial Instrumented Impact Energy; ISO 6603-2 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 43.0 μm/m-°C @Temperature 20.0 °C | 23.9 μin/in-°F @Temperature 68.0 °F | TMA; ASTM E831 |
| CTE, linear, Transverse to Flow | 110 μm/m-°C @Temperature 20.0 °C | 61.1 μin/in-°F @Temperature 68.0 °F | TMA; ASTM E831 |
| Deflection Temperature at 1.8 MPa (264 psi) | 164 °C | 327 °F | Unannealed; ASTM D648 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 227 - 235 °C | 441 - 455 °F | |
| Mold Temperature | 71.1 - 82.2 °C | 160 - 180 °F | |
| Drying Temperature | 82.2 °C | 180 °F | |
| Dry Time | 4 hour | 4 hour | |
| Moisture Content | 0.020 % | 0.020 % | Suggested |
| Back Pressure | 0.172 - 0.345 MPa | 24.9 - 50.0 psi | |