- 熔體流動速率 [g/10min]: 29.8
- 密度 [g/cm3]: 1.03
- 拉伸強度 [MPa]: 40.0
- 熱變形溫度 [℃]: 150.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.03 g/cc | 0.0372 lb/in3 | |
| Melt Flow | 29.8 g/10 min @Load 2.16 kg, Temperature 235 °C | 29.8 g/10 min @Load 4.76 lb, Temperature 455 °F | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 40.0 MPa | 5800 psi | 50 mm/min |
| Elongation at Break | >= 50 % | >= 50 % | Nominal Strain; 50 mm/min |
| Elongation at Yield | 10 % | 10 % | 50 mm/min |
| Tensile Modulus | 1.44 GPa | 209 ksi | 1 mm/min |
| Charpy Impact Unnotched | NB | NB | |
| NB | NB | Low Temp | |
| Charpy Impact, Notched | 1.40 J/cm2 | 6.66 ft-lb/in2 | |
| 1.06 J/cm2 @Temperature -30.0 °C | 5.04 ft-lb/in2 @Temperature -22.0 °F | ||
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | |
| Surface Resistance | 1.00e+14 ohm | 1.00e+14 ohm | |
| Dielectric Strength | 30.0 kV/mm | 762 kV/in | |
| Comparative Tracking Index | 600 V | 600 V | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 90.0 μm/m-°C @Temperature 20.0 °C | 50.0 μin/in-°F @Temperature 68.0 °F | |
| Melting Point | 183 °C | 361 °F | (Dry) |
| Deflection Temperature at 0.46 MPa (66 psi) | 150 °C | 302 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 55.0 °C | 131 °F | |
| Vicat Softening Point | 160 °C | 320 °F | 50°C/hr; 50N |
| UL RTI, Electrical | 65.0 °C | 149 °F | |
| UL RTI, Mechanical with Impact | 65.0 °C | 149 °F | |
| UL RTI, Mechanical without Impact | 65.0 °C | 149 °F | |
| Flammability, UL94 | V-2 @Thickness 1.60 mm | V-2 @Thickness 0.0630 in | |
| V-2 @Thickness 3.20 mm | V-2 @Thickness 0.126 in | ||
| Oxygen Index | 25 % | 25 % | |