- 密度 [g/cm3]: 1.09
- 缺口沖擊強度: 0.534
- 斷裂伸長率 [%]: 44.8
- 彎曲強度 [MPa]: 34.5
- 彎曲模量 [MPa]: 1.38
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.09 - 1.15 g/cc | 0.0394 - 0.0415 lb/in3 | Average value: 1.11 g/cc Grade Count:5 |
| Linear Mold Shrinkage | 0.0130 - 0.0250 cm/cm | 0.0130 - 0.0250 in/in | Average value: 0.0156 cm/cm Grade Count:5 |
| Linear Mold Shrinkage, 6.35 mm section | 0.0160 - 0.0200 cm/cm | 0.0160 - 0.0200 in/in | Average value: 0.0185 cm/cm Grade Count:4 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 34.5 - 48.3 MPa | 5000 - 7000 psi | Average value: 40.7 MPa Grade Count:5 |
| Elongation at Break | 10.0 % | 10.0 % | Average value: 10.0 % Grade Count:5 |
| Modulus of Elasticity | 1.38 - 1.72 GPa | 200 - 250 ksi | Average value: 1.54 GPa Grade Count:5 |
| Flexural Yield Strength | 44.8 - 55.2 MPa | 6500 - 8000 psi | Average value: 49.6 MPa Grade Count:5 |
| Flexural Modulus | 1.38 - 1.72 GPa | 200 - 250 ksi | Average value: 1.59 GPa Grade Count:5 |
| Izod Impact, Notched | 0.534 - 0.747 J/cm | 1.00 - 1.40 ft-lb/in | Average value: 0.651 J/cm Grade Count:5 |
| Izod Impact, Unnotched | 10.7 - 5340 J/cm | 20.0 - 10000 ft-lb/in | Average value: 12.0 J/cm Grade Count:5 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 48.9 - 54.4 °C | 120 - 130 °F | Average value: 51.1 °C Grade Count:5 |
| Flammability, UL94 | HB | HB | Grade Count:4 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 216 - 282 °C | 420 - 540 °F | Average value: 243 °C Grade Count:4 |
| Mold Temperature | 37.8 - 104 °C | 100 - 220 °F | Average value: 71.7 °C Grade Count:5 |
| Injection Pressure | 68.9 - 103 MPa | 10000 - 15000 psi | Average value: 86.2 MPa Grade Count:5 |