- 密度 [g/cm3]: 1.07
- 拉伸強度 [MPa]: 55.0
- 彎曲模量 [MPa]: 1.69
- 硬度: 78.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.07 g/cc | 0.0387 lb/in3 | ASTM D792 | ||
| Moisture Absorption at Equilibrium | 1.1 % | 1.1 % | 24 Hours; ASTM D570 | ||
| 1.9 % | 1.9 % | 50% RH; ASTM D570 | |||
| 6.7 % | 6.7 % | Saturation; ASTM D570 | |||
| Linear Mold Shrinkage | 0.03556 cm/cm | 0.03556 in/in | 1/8" bar | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell R | 78 | 78 | ASTM D785 | ||
| Tensile Strength, Yield | 55.0 MPa | 7980 psi | ASTM D638 | ||
| Elongation at Break | >= 100 % | >= 100 % | ASTM D638 | ||
| Elongation at Yield | 5.0 % | 5.0 % | ASTM D638 | ||
| Flexural Strength | 66.0 MPa | 9570 psi | ASTM D790 | ||
| Flexural Modulus | 1.69 GPa | 245 ksi | ASTM D790 | ||
| Izod Impact, Notched (ISO) | NB | NB | ASTM D256 | ||
| Dart Drop, Total Energy | 285 J | 210 ft-lb | BASF | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | >= 1.00e+13 ohm-cm | >= 1.00e+13 ohm-cm | ASTM D257 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 1.06 μm/m-°C | 0.589 μin/in-°F | ASTM E831 | ||
| Melting Point | 220 °C | 428 °F | ASTM D3418 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 55.0 °C | 131 °F | ASTM D648 | ||
| UL RTI, Electrical | 105 °C @Thickness 1.50 mm | 221 °F @Thickness 0.0591 in | 746B | ||
| UL RTI, Mechanical with Impact | 105 °C @Thickness 1.50 mm | 221 °F @Thickness 0.0591 in | 746B | ||
| UL RTI, Mechanical without Impact | 105 °C @Thickness 1.50 mm | 221 °F @Thickness 0.0591 in | 746B | ||
| Flammability, UL94 | HB @Thickness 1.50 mm | HB @Thickness 0.0591 in | |||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 240 - 270 °C | 464 - 518 °F | |||
| Mold Temperature | 80.0 - 95.0 °C | 176 - 203 °F | |||
| Dry Time | 2 - 4 hour | 2 - 4 hour | |||
| Moisture Content | <= 0.20 % | <= 0.20 % | |||
| Descriptive Properties | |||||
| Color | BK 102 | ||||
| Commercial Status | North America | ||||