- 熔體流動速率 [g/10min]: 18.15
- 密度 [g/cm3]: 1.21
- 缺口沖擊強(qiáng)度: 10.0
- 彎曲模量 [MPa]: 4.42
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.21 g/cc | 0.0437 lb/in3 | ISO 1183 | ||
| Melt Flow | 18.15 g/10 min @Load 5.00 kg, Temperature 235 °C | 18.15 g/10 min @Load 11.0 lb, Temperature 455 °F | ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 85.0 MPa | 12300 psi | ISO 527 | ||
| Elongation at Break | 3.5 % | 3.5 % | ISO 527 | ||
| Flexural Modulus | 4.42 GPa | 641 ksi | ISO 178 | ||
| Izod Impact, Notched (ISO) | 10.0 kJ/m2 | 4.76 ft-lb/in2 | ISO 180 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 220 °C | 428 °F | ISO 3146 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 180 °C | 356 °F | ISO 75 | ||
| Processing Properties | Metric | English | Comments | ||
| Zone 1 | 245 - 275 °C | 473 - 527 °F | Rear Zone | ||
| Zone 2 | 260 - 285 °C | 500 - 545 °F | Center Zone | ||
| Zone 3 | 270 - 295 °C | 518 - 563 °F | Front Zone | ||
| Zone 4 | 270 - 295 °C | 518 - 563 °F | Nozzle | ||
| Melt Temperature | 270 - 295 °C | 518 - 563 °F | |||
| Mold Temperature | 80.0 - 95.0 °C | 176 - 203 °F | |||
| Dry Time | 2 - 4 hour | 2 - 4 hour | |||
| Moisture Content | <= 0.080 % | <= 0.080 % | |||
| Descriptive Properties | |||||
| Color | BK 5966 | ||||
| Commercial Status | North America | ||||