- 密度 [g/cm3]: 1.1
- 缺口沖擊強(qiáng)度: 180.0
- 拉伸強(qiáng)度 [MPa]: 70.0
- 彎曲模量 [MPa]: 2.39
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.10 g/cc | 0.0397 lb/in3 | ASTM D792 | ||
| Moisture Absorption at Equilibrium | 2.4 % | 2.4 % | 50% RH; ASTM D570 | ||
| 8.6 % | 8.6 % | Saturation; ASTM D570 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 70.0 MPa | 10200 psi | ASTM D638 | ||
| Elongation at Break | 70 % | 70 % | ASTM D638 | ||
| Elongation at Yield | 4.0 % | 4.0 % | ASTM D638 | ||
| Flexural Strength | 95.0 MPa | 13800 psi | ASTM D790 | ||
| Flexural Modulus | 2.39 GPa | 347 ksi | ASTM D790 | ||
| Izod Impact, Notched (ISO) | 180 kJ/m2 | 85.7 ft-lb/in2 | ISO 179 | ||
| Dart Drop, Total Energy | 201 J | 148 ft-lb | BASF | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 220 °C | 428 °F | ASTM D3418 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 60.0 °C | 140 °F | ASTM D648 | ||
| UL RTI, Electrical | 65.0 °C @Thickness 1.50 mm | 149 °F @Thickness 0.0591 in | 746B | ||
| UL RTI, Mechanical with Impact | 65.0 °C @Thickness 1.50 mm | 149 °F @Thickness 0.0591 in | 746B | ||
| UL RTI, Mechanical without Impact | 65.0 °C @Thickness 1.50 mm | 149 °F @Thickness 0.0591 in | 746B | ||
| Flammability, UL94 | HB @Thickness 1.50 mm | HB @Thickness 0.0591 in | |||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 240 - 285 °C | 464 - 545 °F | |||
| Mold Temperature | 65.0 - 80.0 °C | 149 - 176 °F | |||
| Dry Time | 2 - 4 hour | 2 - 4 hour | |||
| Moisture Content | <= 0.15 % | <= 0.15 % | |||
| Descriptive Properties | |||||
| Commercial Status | North America | ||||