- 密度 [g/cm3]: 1.13
- 拉伸強度 [MPa]: 33.0
- 彎曲模量 [MPa]: 0.685
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.13 g/cc | 0.0408 lb/in3 | ASTM D792 | ||
| Moisture Absorption at Equilibrium | 1.3 % | 1.3 % | 24 Hours; ASTM D570 | ||
| 2.7 % | 2.7 % | 50% RH; ASTM D570 | |||
| 9.5 % | 9.5 % | Saturation; ASTM D570 | |||
| Linear Mold Shrinkage | 0.0508 cm/cm | 0.0508 in/in | 1/8" bar | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 33.0 MPa @Temperature 23.0 °C | 4790 psi @Temperature 73.4 °F | ASTM D638 | ||
| 100 MPa @Temperature -40.0 °C | 14500 psi @Temperature -40.0 °F | ASTM D638 | |||
| Elongation at Break | >= 100 % | >= 100 % | ASTM D638 | ||
| Flexural Strength | 32.0 MPa @Temperature 23.0 °C | 4640 psi @Temperature 73.4 °F | ASTM D790 | ||
| 145 MPa @Temperature -40.0 °C | 21000 psi @Temperature -40.0 °F | ASTM D790 | |||
| Flexural Modulus | 0.685 GPa @Temperature 23.0 °C | 99.4 ksi @Temperature 73.4 °F | ASTM D790 | ||
| 2.26 GPa @Temperature -40.0 °C | 328 ksi @Temperature -40.0 °F | ASTM D790 | |||
| Processing Properties | Metric | English | Comments | ||
| Dry Time | 2 - 4 hour | 2 - 4 hour | |||
| Moisture Content | <= 0.20 % | <= 0.20 % | |||
| Descriptive Properties | |||||
| Commercial Status | North America | ||||