- 密度 [g/cm3]: 1.13
- 缺口沖擊強度: 45.0
- 拉伸強度 [MPa]: 20.0
- 彎曲模量 [MPa]: 0.300
- 硬度: 116.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.13 g/cc | 0.0408 lb/in3 | ASTM D792 | ||
| Moisture Absorption at Equilibrium | 1.3 % | 1.3 % | 24 Hours; ASTM D570 | ||
| 2.7 % | 2.7 % | 50% RH; ASTM D570 | |||
| 9.5 % | 9.5 % | Saturation; ASTM D570 | |||
| Linear Mold Shrinkage | 0.0508 cm/cm | 0.0508 in/in | 1/8" bar | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell R | 116 | 116 | ASTM D785 | ||
| Tensile Strength, Yield | 20.0 MPa @Temperature 65.0 °C | 2900 psi @Temperature 149 °F | ASTM D638 | ||
| 72.0 MPa @Temperature 23.0 °C | 10400 psi @Temperature 73.4 °F | ASTM D638 | |||
| 114 MPa @Temperature -40.0 °C | 16500 psi @Temperature -40.0 °F | ASTM D638 | |||
| Elongation at Break | >= 100 % | >= 100 % | ASTM D638 | ||
| Flexural Strength | 15.0 MPa @Temperature 121 °C | 2180 psi @Temperature 250 °F | ASTM D790 | ||
| 20.0 MPa @Temperature 90.0 °C | 2900 psi @Temperature 194 °F | ASTM D790 | |||
| 30.0 MPa @Temperature 65.0 °C | 4350 psi @Temperature 149 °F | ASTM D790 | |||
| 100 MPa @Temperature 23.0 °C | 14500 psi @Temperature 73.4 °F | ASTM D790 | |||
| 154 MPa @Temperature -40.0 °C | 22300 psi @Temperature -40.0 °F | ASTM D790 | |||
| Flexural Modulus | 0.300 GPa @Temperature 121 °C | 43.5 ksi @Temperature 250 °F | ASTM D790 | ||
| 0.360 GPa @Temperature 90.0 °C | 52.2 ksi @Temperature 194 °F | ASTM D790 | |||
| 0.530 GPa @Temperature 65.0 °C | 76.9 ksi @Temperature 149 °F | ASTM D790 | |||
| 2.69 GPa @Temperature 23.0 °C | 390 ksi @Temperature 73.4 °F | ASTM D790 | |||
| 2.76 GPa @Temperature -40.0 °C | 400 ksi @Temperature -40.0 °F | ASTM D790 | |||
| Izod Impact, Notched (ISO) | 45.0 kJ/m2 @Temperature -40.0 °C | 21.4 ft-lb/in2 @Temperature -40.0 °F | ASTM D256 | ||
| 55.0 kJ/m2 @Temperature 23.0 °C | 26.2 ft-lb/in2 @Temperature 73.4 °F | ASTM D256 | |||
| Dart Drop, Total Energy | 67.8 J | 50.0 ft-lb | BASF | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 0.740 μm/m-°C | 0.411 μin/in-°F | ASTM E831 | ||
| Melting Point | 220 °C | 428 °F | ASTM D3418 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 60.0 °C | 140 °F | ASTM D648 | ||
| Processing Properties | Metric | English | Comments | ||
| Dry Time | 2 - 4 hour | 2 - 4 hour | |||
| Moisture Content | <= 0.20 % | <= 0.20 % | |||
| Descriptive Properties | |||||
| Commercial Status | North America | ||||