- 密度 [g/cm3]: 1.35
- 缺口沖擊強(qiáng)度: 1.05
- 彎曲模量 [MPa]: 8.48
- 硬度: 121.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.35 g/cc | 0.0488 lb/in3 | ASTM D792 | ||
| Moisture Absorption at Equilibrium | 1.1 % | 1.1 % | 24 Hours | ||
| 1.9 % | 1.9 % | 50% RH | |||
| 6.7 % | 6.7 % | Saturation | |||
| Linear Mold Shrinkage | 0.00762 cm/cm | 0.00762 in/in | 1/8" bar | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell R | 121 | 121 | ASTM D785 | ||
| Tensile Strength at Break | 165 MPa | 23900 psi | ASTM D638 | ||
| Elongation at Break | 3.0 % | 3.0 % | ASTM D638 | ||
| Flexural Strength | 235 MPa | 34100 psi | ASTM D790 | ||
| Flexural Modulus | 8.48 GPa | 1230 ksi | ASTM D790 | ||
| Izod Impact, Notched | 1.05 J/cm | 1.97 ft-lb/in | ASTM D256 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | >= 1.00e+13 ohm-cm | >= 1.00e+13 ohm-cm | IEC 60093 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 0.380 μm/m-°C | 0.211 μin/in-°F | ASTM E831 | ||
| Melting Point | 220 °C | 428 °F | ISO 3146 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 205 °C | 401 °F | ASTM D648 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 270 - 295 °C | 518 - 563 °F | |||
| Mold Temperature | 80.0 - 90.0 °C | 176 - 194 °F | |||
| Dry Time | 2 - 4 hour | 2 - 4 hour | |||
| Moisture Content | 0.10 % | 0.10 % | |||
| Descriptive Properties | |||||
| Color | Black | ||||
| Commercial Status | North America | ||||