- 密度 [g/cm3]: 1.14
- 吸水率 [%]: 1.3
- 缺口沖擊強度: 0.534
- 彎曲模量 [MPa]: 3.03
- 熱變形溫度 [℃]: 238.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.14 g/cc | 0.0412 lb/in3 | ASTM D792 | ||
| Water Absorption | 1.3 % | 1.3 % | 24 hrs; ASTM D570 | ||
| Linear Mold Shrinkage | 0.015 cm/cm | 0.015 in/in | 0.125 in; ASTM D955 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell M | 85 | 85 | ASTM D785 | ||
| Tensile Strength at Break | 82.7 MPa | 12000 psi | ASTM D638 | ||
| Elongation at Break | 30 % | 30 % | ASTM D638 | ||
| Flexural Strength | 114 MPa | 16500 psi | ASTM D790 | ||
| Flexural Modulus | 3.03 GPa | 440 ksi | ASTM D790 | ||
| Izod Impact, Notched | 0.534 J/cm | 1.00 ft-lb/in | 73°F; ASTM D256 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | ASTM D257 | ||
| Dielectric Constant | 3.7 @Frequency 100 Hz | 3.7 @Frequency 100 Hz | ASTM D150 | ||
| Dielectric Strength | 22.6 kV/mm | 575 kV/in | ASTM D149 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 82.8 μm/m-°C @Temperature 20.0 °C | 46.0 μin/in-°F @Temperature 68.0 °F | ASTM D696 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 238 °C | 460 °F | Unannealed; ASTM D648 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 87.8 °C | 190 °F | Unannealed; ASTM D648 | ||
| Flammability, UL94 | V-2 | V-2 | 0.0280 in, ALL | ||
| V-2 | V-2 | 0.0591 in, ALL | |||
| V-2 | V-2 | 0.118 in, ALL | |||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 271 - 293 °C | 520 - 560 °F | |||
| Mold Temperature | 48.9 - 93.3 °C | 120 - 200 °F | |||
| Drying Temperature | 73.9 °C | 165 °F | |||
| Dry Time | 2 - 4 hour | 2 - 4 hour | |||
| Moisture Content | 0.20 % | 0.20 % | |||
| Back Pressure | 0.345 - 0.689 MPa | 50.0 - 100 psi | |||
| Screw Speed | 40 - 140 rpm | 40 - 140 rpm | |||
| Descriptive Properties | |||||
| Holding Pressure | 400 to 1400 psi | ||||
| Injection Rate | Fast | ||||
Materials flagged as discontinued () are no longer part of the manufacturer’s standard product line according to our latest information. These materials may be available by special order, in distribution inventory, or reinstated as an active product. Data sheets from materials that are no longer available remain in MatWeb to assist users in finding replacement materials.