Ascend Performance Materials Vydyne? R633 Nylon 66 Copolymer, 33% Glass Filled, Conditioned (2.5% Mo

Ascend Performance Materials Vydyne? R633 Nylon 66 Copolymer, 33% Glass Filled, Conditioned (2.5% Mo 物性表: Ascend Performance Materials Vydyne? R633 Nylon 66 Copolymer, 33% Glass Filled, Conditioned (2.5% Mo物性表及特性介紹,Ascend Performance Materials Vydyne? R633 Nylon 66 Copolymer, 33% Glass Filled, Conditioned (2.5% Mo注塑參數(shù)詳情,如需Ascend Performance Materials Vydyne? R633 Nylon 66 Copolymer, 33% Glass Filled, Conditioned (2.5% Mo下載, 可到相關(guān)下載區(qū)下載

吸水率 [%]: 1.3
彎曲模量 [MPa]: 6.80

Physical Properties	Metric	English	Comments

Specific Gravity	1.39 g/cc	1.39 g/cc	ISO 1183
Water Absorption	1.3 % @Time 86400 sec	1.3 % @Time 24.0 hour	ISO 62
Moisture Absorption at Equilibrium	2.3 %	2.3 %	50% RH; ISO 62
Linear Mold Shrinkage	0.0040 cm/cm @Thickness 2.00 mm	0.0040 in/in @Thickness 0.0787 in	ISO 294-4
Linear Mold Shrinkage, Transverse	0.0090 cm/cm @Thickness 2.00 mm	0.0090 in/in @Thickness 0.0787 in	ISO 294-4

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	130 MPa	18900 psi	ISO 527
Elongation at Break	6.0 %	6.0 %	ISO 527
Tensile Modulus	8.00 GPa	1160 ksi	ISO 527
Flexural Strength	195 MPa	28300 psi	ISO 178
Flexural Modulus	6.80 GPa	986 ksi	ISO 178

Thermal Properties	Metric	English	Comments
Melting Point	233 °C	451 °F	ISO 3146

Processing Properties	Metric	English	Comments
Processing Temperature	280 - 310 °C	536 - 590 °F
Melt Temperature	285 - 305 °C	545 - 581 °F
Mold Temperature	65.0 - 95.0 °C	149 - 203 °F
Injection Pressure	55.0 - 140 MPa	7980 - 20300 psi
Hold Pressure	55.0 - 140 MPa	7980 - 20300 psi
Back Pressure	0.200 - 1.00 MPa	29.0 - 145 psi
Clamp Pressure	29.43 - 68.67 MPa	4268 - 9960 psi
Cushion	0.300 - 0.640 cm	0.118 - 0.252 in
Screw Speed	60 - 120 rpm	60 - 120 rpm

關(guān)鍵詞:
供應(yīng)
PA66
33% Glass Filled
Ascend Performance Materials Vydyne? R633 Nylon 66 Copolymer
Conditioned (2.5% Mo

轉(zhuǎn)載請(qǐng)注明: 轉(zhuǎn)自中國(guó)塑膠原料之家 http://www.spnmy.cn/wuxingbiao/

本文鏈接: http://www.spnmy.cn/yuanliaoku/show-45557.html

免責(zé)聲明: 本文 Ascend Performance Materials Vydyne? R633 Nylon 66 Copolymer, 33% Glass Filled, Conditioned (2.5% Mo 僅代表作者個(gè)人觀點(diǎn)，中國(guó)塑膠原料之家無(wú)關(guān)。中國(guó)塑膠原料之家網(wǎng)所轉(zhuǎn)載的內(nèi)容，其版權(quán)均由原作者和資料提供方所擁有！如因作品版權(quán)問(wèn)題需要處理，請(qǐng)與我們聯(lián)絡(luò)

該類別其他物性信息