- 吸水率 [%]: 0.85
- 彎曲模量 [MPa]: 5.70
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.32 g/cc | 1.32 g/cc | ISO 1183 |
| Water Absorption | 0.85 % @Time 86400 sec | 0.85 % @Time 24.0 hour | ISO 62 |
| Moisture Absorption at Equilibrium | 2.0 % | 2.0 % | 50% RH; ISO 62 |
| Linear Mold Shrinkage | 0.0040 cm/cm @Thickness 2.00 mm | 0.0040 in/in @Thickness 0.0787 in | ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.0090 cm/cm @Thickness 2.00 mm | 0.0090 in/in @Thickness 0.0787 in | ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 117 MPa | 17000 psi | ISO 527 |
| Elongation at Break | 7.0 % | 7.0 % | ISO 527 |
| Tensile Modulus | 5.50 GPa | 798 ksi | ISO 527 |
| Flexural Strength | 150 MPa | 21800 psi | ISO 178 |
| Flexural Modulus | 5.70 GPa | 827 ksi | ISO 178 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 260 °C | 500 °F | ISO 3146 |