Ascend Performance Materials Vydyne? R220/R228 Nylon 66, 40% Mineral Reinforced, Dry as Molded

Ascend Performance Materials Vydyne? R220/R228 Nylon 66, 40% Mineral Reinforced, Dry as Molded 物性表: Ascend Performance Materials Vydyne? R220/R228 Nylon 66, 40% Mineral Reinforced, Dry as Molded物性表及特性介紹,Ascend Performance Materials Vydyne? R220/R228 Nylon 66, 40% Mineral Reinforced, Dry as Molded注塑參數(shù)詳情,如需Ascend Performance Materials Vydyne? R220/R228 Nylon 66, 40% Mineral Reinforced, Dry as Molded下載, 可到相關(guān)下載區(qū)下載

吸水率 [%]: 1.1
缺口沖擊強(qiáng)度: 9.0
拉伸強(qiáng)度 [MPa]: 103.0
彎曲模量 [MPa]: 6.10
熱變形溫度 [℃]: 222.0

Physical Properties	Metric	English	Comments

Specific Gravity	1.48 g/cc	1.48 g/cc	ISO 1183
Water Absorption	1.1 % @Time 86400 sec	1.1 % @Time 24.0 hour	ISO 62
Moisture Absorption at Equilibrium	1.6 %	1.6 %	50% RH; ISO 62
Linear Mold Shrinkage	0.010 cm/cm @Thickness 2.00 mm	0.010 in/in @Thickness 0.0787 in	ISO 294-4
Linear Mold Shrinkage, Transverse	0.011 cm/cm @Thickness 2.00 mm	0.011 in/in @Thickness 0.0787 in	ISO 294-4

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	103 MPa	14900 psi	ISO 527
Elongation at Break	15 %	15 %	ISO 527
Elongation at Yield	9.0 %	9.0 %	ISO 527
Tensile Modulus	6.90 GPa	1000 ksi	ISO 527
Flexural Strength	124 MPa	18000 psi	ISO 178
Flexural Modulus	6.10 GPa	885 ksi	ISO 178
Poissons Ratio	0.35	0.35	ISO 527
Shear Modulus	2.56 GPa	371 ksi	Calculated
Izod Impact, Notched (ISO)	9.00 kJ/m2	4.28 ft-lb/in2	ISO 180
Charpy Impact Unnotched	10.9 J/cm2 @Temperature -30.0 °C	51.9 ft-lb/in2 @Temperature -22.0 °F	ISO 179
	14.3 J/cm2 @Temperature 23.0 °C	68.1 ft-lb/in2 @Temperature 73.4 °F	ISO 179
Charpy Impact, Notched	0.620 J/cm2 @Temperature -30.0 °C	2.95 ft-lb/in2 @Temperature -22.0 °F	ISO 179
	0.740 J/cm2 @Temperature 23.0 °C	3.52 ft-lb/in2 @Temperature 73.4 °F	ISO 179

Electrical Properties	Metric	English	Comments
Volume Resistivity	5.50e+16 ohm-cm @Thickness 3.00 mm	5.50e+16 ohm-cm @Thickness 0.118 in	IEC 60093
Dielectric Strength	15.0 kV/mm @Thickness 3.00 mm	381 kV/in @Thickness 0.118 in	IEC 60243
Arc Resistance	60 - 120 sec @Thickness 3.00 mm	60 - 120 sec @Thickness 0.118 in	UL 746A
Comparative Tracking Index	>= 600 V @Thickness 3.00 mm	>= 600 V @Thickness 0.118 in	IEC 60112
Hot Wire Ignition, HWI	7.0 - 15 sec @Thickness 0.750 mm	7.0 - 15 sec @Thickness 0.0295 in	UL 746A
	7.0 - 15 sec @Thickness 1.50 mm	7.0 - 15 sec @Thickness 0.0591 in	UL 746A
	15 - 30 sec @Thickness 3.00 mm	15 - 30 sec @Thickness 0.118 in	UL 746A
High Amp Arc Ignition, HAI	>= 120 arcs @Thickness 3.00 mm	>= 120 arcs @Thickness 0.118 in	UL 746A
	>= 120 arcs @Thickness 0.750 mm	>= 120 arcs @Thickness 0.0295 in	UL 746A
	>= 120 arcs @Thickness 1.50 mm	>= 120 arcs @Thickness 0.0591 in	UL 746A
High Voltage Arc-Tracking Rate, HVTR	10.0 - 25.4 mm/min @Thickness 3.00 mm	0.394 - 1.00 in/min @Thickness 0.118 in	UL 746A

Thermal Properties	Metric	English	Comments
CTE, linear	6.00 μm/m-°C @Thickness 2.00 mm, Temperature 23.0 - 55.0 °C	3.33 μin/in-°F @Thickness 0.0787 in, Temperature 73.4 - 131 °F	ISO 11359
CTE, linear, Transverse to Flow	6.30 μm/m-°C @Thickness 2.00 mm, Temperature 23.0 - 55.0 °C	3.50 μin/in-°F @Thickness 0.0787 in, Temperature 73.4 - 131 °F	ISO 11359
Melting Point	258 °C	496 °F	ISO 3146
Deflection Temperature at 0.46 MPa (66 psi)	222 °C	432 °F	ISO 75
Deflection Temperature at 1.8 MPa (264 psi)	118 °C	244 °F	ISO 75
Vicat Softening Point	238 °C @Load 5.10 kg	460 °F @Load 11.2 lb	ISO 306
UL RTI, Electrical	105 °C @Thickness 3.00 mm	221 °F @Thickness 0.118 in	UL 746B
	105 °C @Thickness 0.750 mm	221 °F @Thickness 0.0295 in	UL 746B
	105 °C @Thickness 1.50 mm	221 °F @Thickness 0.0591 in	UL 746B
UL RTI, Mechanical with Impact	90.0 °C @Thickness 3.00 mm	194 °F @Thickness 0.118 in	UL 746B
	90.0 °C @Thickness 0.750 mm	194 °F @Thickness 0.0295 in	UL 746B
	90.0 °C @Thickness 1.50 mm	194 °F @Thickness 0.0591 in	UL 746B
UL RTI, Mechanical without Impact	105 °C @Thickness 3.00 mm	221 °F @Thickness 0.118 in	UL 746B
	105 °C @Thickness 0.750 mm	221 °F @Thickness 0.0295 in	UL 746B
	105 °C @Thickness 1.50 mm	221 °F @Thickness 0.0591 in	UL 746B
Flammability, UL94	HB @Thickness 3.00 mm	HB @Thickness 0.118 in
	HB @Thickness 0.750 mm	HB @Thickness 0.0295 in
	HB @Thickness 1.50 mm	HB @Thickness 0.0591 in

Processing Properties	Metric	English	Comments
Processing Temperature	280 - 310 °C	536 - 590 °F
Melt Temperature	285 - 305 °C	545 - 581 °F
Mold Temperature	65.0 - 95.0 °C	149 - 203 °F
Injection Pressure	55.0 - 140 MPa	7980 - 20300 psi
Hold Pressure	55.0 - 140 MPa	7980 - 20300 psi
Back Pressure	0.200 - 1.00 MPa	29.0 - 145 psi
Clamp Pressure	29.43 - 68.67 MPa	4268 - 9960 psi
Cushion	0.300 - 0.640 cm	0.118 - 0.252 in
Screw Speed	40 - 120 rpm	40 - 120 rpm

關(guān)鍵詞:
供應(yīng)
40% mineral reinforced
Dry as Molded
PA66
Ascend Performance Materials Vydyne? R220/R228 Nylon 66

轉(zhuǎn)載請(qǐng)注明: 轉(zhuǎn)自中國(guó)塑膠原料之家 http://www.spnmy.cn/wuxingbiao/

本文鏈接: http://www.spnmy.cn/yuanliaoku/show-45559.html

免責(zé)聲明: 本文 Ascend Performance Materials Vydyne? R220/R228 Nylon 66, 40% Mineral Reinforced, Dry as Molded 僅代表作者個(gè)人觀點(diǎn)，中國(guó)塑膠原料之家無(wú)關(guān)。中國(guó)塑膠原料之家網(wǎng)所轉(zhuǎn)載的內(nèi)容，其版權(quán)均由原作者和資料提供方所擁有！如因作品版權(quán)問(wèn)題需要處理，請(qǐng)與我們聯(lián)絡(luò)