- 吸水率 [%]: 1.0
- 彎曲模量 [MPa]: 3.15
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.22 g/cc | 1.22 g/cc | ISO 1183 |
| Water Absorption | 1.0 % @Time 86400 sec | 1.0 % @Time 24.0 hour | ISO 62 |
| Moisture Absorption at Equilibrium | 2.2 % | 2.2 % | 50% RH; ISO 62 |
| Linear Mold Shrinkage | 0.0050 cm/cm @Thickness 2.00 mm | 0.0050 in/in @Thickness 0.0787 in | ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.010 cm/cm @Thickness 2.00 mm | 0.010 in/in @Thickness 0.0787 in | ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 75.0 MPa | 10900 psi | ISO 527 |
| Elongation at Break | 13 % | 13 % | ISO 527 |
| Tensile Modulus | 3.90 GPa | 566 ksi | ISO 527 |
| Flexural Strength | 106 MPa | 15400 psi | ISO 178 |
| Flexural Modulus | 3.15 GPa | 457 ksi | ISO 178 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 260 °C | 500 °F | ISO 3146 |