- 吸水率 [%]: 0.8
- 彎曲模量 [MPa]: 6.50
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.40 g/cc | 1.40 g/cc | ISO 1183 |
| Water Absorption | 0.80 % @Time 86400 sec | 0.80 % @Time 24.0 hour | ISO 62 |
| Moisture Absorption at Equilibrium | 1.8 % | 1.8 % | 50% RH; ISO 62 |
| Linear Mold Shrinkage | 0.0040 cm/cm @Thickness 2.00 mm | 0.0040 in/in @Thickness 0.0787 in | ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.0090 cm/cm @Thickness 2.00 mm | 0.0090 in/in @Thickness 0.0787 in | ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 150 MPa | 21800 psi | ISO 527 |
| Elongation at Break | 6.0 % | 6.0 % | ISO 527 |
| Tensile Modulus | 7.90 GPa | 1150 ksi | ISO 527 |
| Flexural Strength | 205 MPa | 29700 psi | ISO 178 |
| Flexural Modulus | 6.50 GPa | 943 ksi | ISO 178 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 264 °C | 507 °F | ISO 3146 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 280 - 310 °C | 536 - 590 °F | |
| Melt Temperature | 285 - 305 °C | 545 - 581 °F | |
| Mold Temperature | 65.0 - 95.0 °C | 149 - 203 °F | |
| Injection Pressure | 55.0 - 140 MPa | 7980 - 20300 psi | |
| Hold Pressure | 55.0 - 140 MPa | 7980 - 20300 psi | |
| Back Pressure | 0.200 - 1.00 MPa | 29.0 - 145 psi | |
| Clamp Pressure | 29.43 - 68.67 MPa | 4268 - 9960 psi | |
| Cushion | 0.300 - 0.640 cm | 0.118 - 0.252 in | |
| Screw Speed | 60 - 120 rpm | 60 - 120 rpm | |