- 缺口沖擊強(qiáng)度: 2670.0
- 彎曲模量 [MPa]: 4.10
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 11.0 g/cc | 11.0 g/cc | Internal Method |
| Linear Mold Shrinkage | 0.0090 - 0.010 cm/cm | 0.0090 - 0.010 in/in | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength | 35.0 MPa | 5080 psi | ISO 527 |
| Elongation at Break | 2.0 % | 2.0 % | ISO 527 |
| Tensile Modulus | 3.00 GPa | 435 ksi | ISO 527 |
| Flexural Modulus | 4.10 GPa | 595 ksi | ISO 178 |
| Izod Impact, Notched | 2670 J/cm | 5000 ft-lb/in | ASTM D256 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 265 - 290 °C | 509 - 554 °F | |
| Mold Temperature | 65.0 - 90.0 °C | 149 - 194 °F | |
| Drying Temperature | 80.0 °C | 176 °F | |
| Dry Time | 4 - 6 hour | 4 - 6 hour | |
| Moisture Content | <= 0.20 % | <= 0.20 % | target |