- 吸水率 [%]: 1.1
- 拉伸強度 [MPa]: 73.0
- 彎曲模量 [MPa]: 2.30
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.48 g/cc | 1.48 g/cc | ISO 1183 |
| Water Absorption | 1.1 % @Time 86400 sec | 1.1 % @Time 24.0 hour | ISO 62 |
| Moisture Absorption at Equilibrium | 1.6 % | 1.6 % | 50% RH; ISO 62 |
| Linear Mold Shrinkage | 0.010 cm/cm @Thickness 2.00 mm | 0.010 in/in @Thickness 0.0787 in | ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.011 cm/cm @Thickness 2.00 mm | 0.011 in/in @Thickness 0.0787 in | ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 73.0 MPa | 10600 psi | ISO 527 |
| Elongation at Break | 30 % | 30 % | ISO 527 |
| Elongation at Yield | 16 % | 16 % | ISO 527 |
| Tensile Modulus | 2.60 GPa | 377 ksi | ISO 527 |
| Flexural Strength | 50.0 MPa | 7250 psi | ISO 178 |
| Flexural Modulus | 2.30 GPa | 334 ksi | ISO 178 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 258 °C | 496 °F | ISO 3146 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 280 - 310 °C | 536 - 590 °F | |
| Melt Temperature | 285 - 305 °C | 545 - 581 °F | |
| Mold Temperature | 65.0 - 95.0 °C | 149 - 203 °F | |
| Injection Pressure | 55.0 - 140 MPa | 7980 - 20300 psi | |
| Hold Pressure | 55.0 - 140 MPa | 7980 - 20300 psi | |
| Back Pressure | 0.200 - 1.00 MPa | 29.0 - 145 psi | |
| Clamp Pressure | 29.43 - 68.67 MPa | 4268 - 9960 psi | |
| Cushion | 0.300 - 0.640 cm | 0.118 - 0.252 in | |
| Screw Speed | 40 - 120 rpm | 40 - 120 rpm | |