- 熔體流動速率 [g/10min]: 1.0
- 密度 [g/cm3]: 1.15
- 吸水率 [%]: 0.3
- 缺口沖擊強度: 0.27
- 拉伸強度 [MPa]: 58.0
- 斷裂伸長率 [%]: 90.0
- 彎曲強度 [MPa]: 50.0
- 彎曲模量 [MPa]: 3.70
- 硬度: 115.0
- 熱變形溫度 [℃]: 177.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.15 - 1.76 g/cc | 0.0415 - 0.0636 lb/in3 | Average value: 1.45 g/cc Grade Count:140 |
| Filler Content | 10.0 - 35.0 % | 10.0 - 35.0 % | Average value: 24.9 % Grade Count:18 |
| Water Absorption | 0.300 - 7.00 % | 0.300 - 7.00 % | Average value: 2.15 % Grade Count:61 |
| Moisture Absorption at Equilibrium | 0.170 - 2.20 % | 0.170 - 2.20 % | Average value: 1.48 % Grade Count:31 |
| Water Absorption at Saturation | 3.90 - 7.00 % | 3.90 - 7.00 % | Average value: 5.58 % Grade Count:5 |
| Additive Loading | 20.0 - 35.0 % | 20.0 - 35.0 % | Average value: 26.9 % Grade Count:7 |
| Viscosity Measurement | 0.360 - 1.22 | 0.360 - 1.22 | Average value: 0.666 Grade Count:8 |
| Viscosity Test | 127 - 150 cm3/g | 127 - 150 cm3/g | Average value: 141 cm3/g Grade Count:9 |
| Linear Mold Shrinkage | 0.00100 - 0.0200 cm/cm | 0.00100 - 0.0200 in/in | Average value: 0.00513 cm/cm Grade Count:120 |
| Linear Mold Shrinkage, 6.35 mm section | 0.00350 - 0.00850 cm/cm | 0.00350 - 0.00850 in/in | Average value: 0.00558 cm/cm Grade Count:12 |
| Linear Mold Shrinkage, Transverse | 0.00530 - 0.0140 cm/cm | 0.00530 - 0.0140 in/in | Average value: 0.00894 cm/cm Grade Count:33 |
| Melt Flow | 1.00 - 53.6 g/10 min | 1.00 - 53.6 g/10 min | Average value: 13.8 g/10 min Grade Count:20 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 55.0 - 100 | 55.0 - 100 | Average value: 87.2 Grade Count:10 |
| Hardness, Rockwell R | 115 - 122 | 115 - 122 | Average value: 120 Grade Count:28 |
| Hardness, Shore D | 80.0 - 90.0 | 80.0 - 90.0 | Average value: 85.8 Grade Count:4 |
| Tensile Strength, Ultimate | 50.0 - 200 MPa | 7250 - 29000 psi | Average value: 129 MPa Grade Count:96 |
| Tensile Strength, Yield | 58.0 - 180 MPa | 8410 - 26100 psi | Average value: 125 MPa Grade Count:47 |
| Elongation at Break | 1.00 - 13.2 % | 1.00 - 13.2 % | Average value: 2.99 % Grade Count:112 |
| Elongation at Yield | 1.40 - 7.80 % | 1.40 - 7.80 % | Average value: 3.14 % Grade Count:14 |
| Modulus of Elasticity | 3.90 - 16.0 GPa | 566 - 2320 ksi | Average value: 8.82 GPa Grade Count:70 |
| Flexural Yield Strength | 90.0 - 283 MPa | 13100 - 41000 psi | Average value: 191 MPa Grade Count:119 |
| Flexural Modulus | 3.70 - 12.4 GPa | 537 - 1800 ksi | Average value: 7.76 GPa Grade Count:107 |
| Compressive Yield Strength | 103 - 128 MPa | 15000 - 18500 psi | Average value: 117 MPa Grade Count:3 |
| Izod Impact, Notched | 0.270 - 1.33 J/cm | 0.506 - 2.50 ft-lb/in | Average value: 0.775 J/cm Grade Count:78 |
| 0.69407 - 0.69407 J/cm @Temperature -40.0 - -40.0 °C | 1.3003 - 1.3003 ft-lb/in @Temperature -40.0 - -40.0 °F | Average value: 0.694 J/cm Grade Count:1 | |
| Izod Impact, Unnotched | 3.20 - 8.54 J/cm | 6.00 - 16.0 ft-lb/in | Average value: 6.74 J/cm Grade Count:24 |
| Izod Impact, Notched (ISO) | 3.00 - 20.0 kJ/m2 | 1.43 - 9.52 ft-lb/in2 | Average value: 8.85 kJ/m2 Grade Count:30 |
| 6.00 - 11.0 kJ/m2 @Temperature -30.0 - -30.0 °C | 2.86 - 5.23 ft-lb/in2 @Temperature -22.0 - -22.0 °F | Average value: 7.50 kJ/m2 Grade Count:10 | |
| Izod Impact, Unnotched (ISO) | 40.0 - 50.0 kJ/m2 | 19.0 - 23.8 ft-lb/in2 | Average value: 45.6 kJ/m2 Grade Count:6 |
| 39.0 - 47.0 kJ/m2 @Temperature -30.0 - -30.0 °C | 18.6 - 22.4 ft-lb/in2 @Temperature -22.0 - -22.0 °F | Average value: 42.7 kJ/m2 Grade Count:5 | |
| Charpy Impact Unnotched | 2.00 J/cm2 - NB | 9.52 ft-lb/in2 - NB | Average value: 5.52 J/cm2 Grade Count:43 |
| 3.20 - 8.00 J/cm2 @Temperature -30.0 - -20.0 °C | 15.2 - 38.1 ft-lb/in2 @Temperature -22.0 - -4.00 °F | Average value: 5.40 J/cm2 Grade Count:22 | |
| Charpy Impact, Notched | 0.400 - 1.80 J/cm2 | 1.90 - 8.57 ft-lb/in2 | Average value: 1.00 J/cm2 Grade Count:40 |
| 0.200 - 10.0 J/cm2 @Temperature -30.0 - -20.0 °C | 0.952 - 47.6 ft-lb/in2 @Temperature -22.0 - -4.00 °F | Average value: 1.31 J/cm2 Grade Count:19 | |
| Taber Abrasion, mg/1000 Cycles | 24.0 - 29.0 | 24.0 - 29.0 | Average value: 25.7 Grade Count:3 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1000 - 1.00e+18 ohm-cm | 1000 - 1.00e+18 ohm-cm | Average value: 3.59e+16 ohm-cm Grade Count:71 |
| Surface Resistance | 100000 - 4.00e+14 ohm | 100000 - 4.00e+14 ohm | Average value: 2.45e+13 ohm Grade Count:47 |
| Dielectric Constant | 3.00 - 8.70 | 3.00 - 8.70 | Average value: 3.90 Grade Count:36 |
| Dielectric Strength | 14.0 - 111 kV/mm | 356 - 2820 kV/in | Average value: 49.9 kV/mm Grade Count:53 |
| Dissipation Factor | 0.00800 - 0.200 | 0.00800 - 0.200 | Average value: 0.0362 Grade Count:17 |
| Arc Resistance | 130 sec | 130 sec | Average value: 130 sec Grade Count:3 |
| Comparative Tracking Index | 225 - 600 V | 225 - 600 V | Average value: 476 V Grade Count:47 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 15.0 - 500 μm/m-°C | 8.33 - 278 μin/in-°F | Average value: 118 μm/m-°C Grade Count:20 |
| CTE, linear, Transverse to Flow | 39.0 - 83.0 μm/m-°C | 21.7 - 46.1 μin/in-°F | Average value: 70.0 μm/m-°C Grade Count:5 |
| Specific Heat Capacity | 1.40 - 1.50 J/g-°C | 0.335 - 0.359 BTU/lb-°F | Average value: 1.45 J/g-°C Grade Count:4 |
| Thermal Conductivity | 0.317 - 2.20 W/m-K | 2.20 - 15.3 BTU-in/hr-ft2-°F | Average value: 0.745 W/m-K Grade Count:9 |
| Melting Point | 220 - 263 °C | 428 - 505 °F | Average value: 258 °C Grade Count:64 |
| Maximum Service Temperature, Air | 100 - 240 °C | 212 - 464 °F | Average value: 165 °C Grade Count:20 |
| Deflection Temperature at 0.46 MPa (66 psi) | 177 - 260 °C | 350 - 500 °F | Average value: 248 °C Grade Count:59 |
| Deflection Temperature at 1.8 MPa (264 psi) | 78.0 - 252 °C | 172 - 486 °F | Average value: 226 °C Grade Count:110 |
| Vicat Softening Point | 230 - 255 °C | 446 - 491 °F | Average value: 249 °C Grade Count:23 |
| Flammability, UL94 | HB - 5VA | HB - 5VA | Grade Count:136 |
| Flammability Test | 12.0 - 30.0 | 12.0 - 30.0 | Average value: 17.8 Grade Count:5 |
| Oxygen Index | 25.0 - 38.0 % | 25.0 - 38.0 % | Average value: 30.9 % Grade Count:10 |
| Glow Wire Test | 650 - 960 °C | 1200 - 1760 °F | Average value: 898 °C Grade Count:39 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 250 - 310 °C | 482 - 590 °F | Average value: 281 °C Grade Count:33 |
| Feed Temperature | 60.0 - 275 °C | 140 - 527 °F | Average value: 94.7 °C Grade Count:9 |
| Nozzle Temperature | 250 - 300 °C | 482 - 572 °F | Average value: 272 °C Grade Count:15 |
| Melt Temperature | 230 - 310 °C | 446 - 590 °F | Average value: 275 °C Grade Count:61 |
| Mold Temperature | 45.0 - 121 °C | 113 - 250 °F | Average value: 81.7 °C Grade Count:83 |
| Drying Temperature | 71.0 - 130 °C | 160 - 266 °F | Average value: 86.1 °C Grade Count:61 |
| Dry Time | 2.00 - 6.00 hour | 2.00 - 6.00 hour | Average value: 4.01 hour Grade Count:41 |
| 2.00 - 6.00 hour @Temperature 80.0 - 80.0 °C | 2.00 - 6.00 hour @Temperature 176 - 176 °F | Average value: 4.00 hour Grade Count:1 | |
| Moisture Content | 0.0300 - 1.80 % | 0.0300 - 1.80 % | Average value: 0.257 % Grade Count:39 |
| Dew Point | -17.8 °C | 0.000 °F | Average value: -17.8 °C Grade Count:9 |
| Injection Pressure | 34.5 - 138 MPa | 5000 - 20000 psi | Average value: 96.5 MPa Grade Count:51 |
| Hold Pressure | 50.0 - 100 MPa | 7250 - 14500 psi | Average value: 75.0 MPa Grade Count:6 |
| Screw Speed | 30.0 - 200 rpm | 30.0 - 200 rpm | Average value: 96.7 rpm Grade Count:3 |