- 熔體流動速率 [g/10min]: 10.0
- 密度 [g/cm3]: 1.11
- 吸水率 [%]: 0.3
- 缺口沖擊強度: 0.21
- 拉伸強度 [MPa]: 40.7
- 斷裂伸長率 [%]: 50.0
- 彎曲強度 [MPa]: 35.9
- 彎曲模量 [MPa]: 1.38
- 硬度: 90.0
- 熱變形溫度 [℃]: 155.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.11 - 1.65 g/cc | 0.0401 - 0.0596 lb/in3 | Average value: 1.30 g/cc Grade Count:111 |
| Filler Content | 10.0 - 30.0 % | 10.0 - 30.0 % | Average value: 18.3 % Grade Count:3 |
| Water Absorption | 0.300 - 8.50 % | 0.300 - 8.50 % | Average value: 0.887 % Grade Count:80 |
| Moisture Absorption at Equilibrium | 0.300 - 2.80 % | 0.300 - 2.80 % | Average value: 1.24 % Grade Count:5 |
| Water Absorption at Saturation | 5.00 - 6.00 % | 5.00 - 6.00 % | Average value: 5.50 % Grade Count:3 |
| Viscosity Measurement | 145 | 145 | Average value: 145 Grade Count:3 |
| Linear Mold Shrinkage | 0.00180 - 0.0400 cm/cm | 0.00180 - 0.0400 in/in | Average value: 0.0151 cm/cm Grade Count:108 |
| Linear Mold Shrinkage, 6.35 mm section | 0.0180 - 0.0300 cm/cm | 0.0180 - 0.0300 in/in | Average value: 0.0210 cm/cm Grade Count:15 |
| Linear Mold Shrinkage, Transverse | 0.00450 - 0.0400 cm/cm | 0.00450 - 0.0400 in/in | Average value: 0.0171 cm/cm Grade Count:11 |
| Melt Flow | 10.0 - 14.3 g/10 min | 10.0 - 14.3 g/10 min | Average value: 12.4 g/10 min Grade Count:3 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 78.0 - 90.0 | 78.0 - 90.0 | Average value: 85.7 Grade Count:3 |
| Hardness, Rockwell R | 90.0 - 122 | 90.0 - 122 | Average value: 108 Grade Count:40 |
| Tensile Strength, Ultimate | 35.9 - 170 MPa | 5200 - 24700 psi | Average value: 63.8 MPa Grade Count:83 |
| 27.0 - 113 MPa @Temperature 60.0 - 120 °C | 3920 - 16400 psi @Temperature 140 - 248 °F | Average value: 63.4 MPa Grade Count:3 | |
| Tensile Strength, Yield | 40.7 - 181 MPa | 5900 - 26200 psi | Average value: 114 MPa Grade Count:35 |
| 131 - 131 MPa @Temperature 93.3 - 93.3 °C | 19000 - 19000 psi @Temperature 200 - 200 °F | Average value: 131 MPa Grade Count:1 | |
| Elongation at Break | 2.00 - 40.0 % | 2.00 - 40.0 % | Average value: 6.71 % Grade Count:88 |
| Elongation at Yield | 2.20 - 40.0 % | 2.20 - 40.0 % | Average value: 7.36 % Grade Count:24 |
| Modulus of Elasticity | 1.65 - 10.0 GPa | 240 - 1450 ksi | Average value: 2.75 GPa Grade Count:65 |
| Flexural Yield Strength | 50.0 - 303 MPa | 7250 - 44000 psi | Average value: 115 MPa Grade Count:106 |
| Flexural Modulus | 1.38 - 11.0 GPa | 200 - 1600 ksi | Average value: 3.76 GPa Grade Count:108 |
| 0.600 - 8.96318 GPa @Temperature 60.0 - 120 °C | 87.0 - 1300.02 ksi @Temperature 140 - 248 °F | Average value: 4.10 GPa Grade Count:4 | |
| Compressive Yield Strength | 30.3 - 68.9 MPa | 4400 - 10000 psi | Average value: 46.5 MPa Grade Count:10 |
| Izod Impact, Notched | 0.210 - 2.67 J/cm | 0.393 - 5.00 ft-lb/in | Average value: 0.774 J/cm Grade Count:94 |
| 0.300 - 1.20 J/cm @Temperature -40.0 - -20.0 °C | 0.562 - 2.25 ft-lb/in @Temperature -40.0 - -4.00 °F | Average value: 0.692 J/cm Grade Count:3 | |
| Izod Impact, Unnotched | 1.60 J/cm - NB | 3.00 ft-lb/in - NB | Average value: 8.74 J/cm Grade Count:56 |
| Izod Impact, Notched (ISO) | 2.00 - 13.0 kJ/m2 | 0.952 - 6.19 ft-lb/in2 | Average value: 4.38 kJ/m2 Grade Count:9 |
| 11.0 - 11.0 kJ/m2 @Temperature -30.0 - -30.0 °C | 5.23 - 5.23 ft-lb/in2 @Temperature -22.0 - -22.0 °F | Average value: 11.0 kJ/m2 Grade Count:1 | |
| Izod Impact, Unnotched (ISO) | 10.0 - 80.0 kJ/m2 | 4.76 - 38.1 ft-lb/in2 | Average value: 34.7 kJ/m2 Grade Count:9 |
| 70.0 - 70.0 kJ/m2 @Temperature -30.0 - -30.0 °C | 33.3 - 33.3 ft-lb/in2 @Temperature -22.0 - -22.0 °F | Average value: 70.0 kJ/m2 Grade Count:1 | |
| Charpy Impact Unnotched | 2.50 J/cm2 - NB | 11.9 ft-lb/in2 - NB | Average value: 6.18 J/cm2 Grade Count:19 |
| 2.40 J/cm2 - NB @Temperature -40.0 - -20.0 °C | 11.4 ft-lb/in2 - NB @Temperature -40.0 - -4.00 °F | Average value: 4.44 J/cm2 Grade Count:15 | |
| Charpy Impact, Notched | 0.400 - 1.40 J/cm2 | 1.90 - 6.66 ft-lb/in2 | Average value: 0.780 J/cm2 Grade Count:9 |
| 0.400 - 0.800 J/cm2 @Temperature -40.0 - -30.0 °C | 1.90 - 3.81 ft-lb/in2 @Temperature -40.0 - -22.0 °F | Average value: 0.625 J/cm2 Grade Count:3 | |
| Falling Dart Impact | 0.570 - 4.10 J | 0.420 - 3.02 ft-lb | Average value: 2.55 J Grade Count:5 |
| Coefficient of Friction | 0.0700 - 0.500 | 0.0700 - 0.500 | Average value: 0.208 Grade Count:32 |
| Coefficient of Friction, Static | 0.0600 - 0.390 | 0.0600 - 0.390 | Average value: 0.157 Grade Count:32 |
| K (wear) Factor | 12.1 - 359 x 10-8 mm3/N-M | 6.00 - 178 x 10-10 in3-min/ft-lb-hr | Average value: 73.2 x 10-8 mm3/N-M Grade Count:20 |
| Limiting Pressure Velocity | 0.333 - 0.701 MPa-m/sec | 9500 - 20000 psi-ft/min | Average value: 0.587 MPa-m/sec Grade Count:11 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+14 - 1.00e+16 ohm-cm | 1.00e+14 - 1.00e+16 ohm-cm | Average value: 1.57e+15 ohm-cm Grade Count:65 |
| Surface Resistance | 1.00e+9 - 1.00e+13 ohm | 1.00e+9 - 1.00e+13 ohm | Average value: 1.54e+12 ohm Grade Count:13 |
| Insulation Resistance | 1.00e+9 - 1.00e+12 ohm | 1.00e+9 - 1.00e+12 ohm | Average value: 8.42e+11 ohm Grade Count:12 |
| Dielectric Constant | 3.60 - 3.70 | 3.60 - 3.70 | Average value: 3.63 Grade Count:6 |
| Dielectric Strength | 17.3 - 23.6 kV/mm | 440 - 600 kV/in | Average value: 19.9 kV/mm Grade Count:33 |
| Dissipation Factor | 0.0100 - 0.0200 | 0.0100 - 0.0200 | Average value: 0.0161 Grade Count:9 |
| Comparative Tracking Index | 550 - 600 V | 550 - 600 V | Average value: 583 V Grade Count:6 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 18.0 - 82.8 μm/m-°C | 10.0 - 46.0 μin/in-°F | Average value: 53.1 μm/m-°C Grade Count:52 |
| Thermal Conductivity | 0.230 - 0.418 W/m-K | 1.60 - 2.90 BTU-in/hr-ft2-°F | Average value: 0.255 W/m-K Grade Count:16 |
| Melting Point | 254 - 275 °C | 490 - 527 °F | Average value: 259 °C Grade Count:11 |
| Maximum Service Temperature, Air | 90.0 - 160 °C | 194 - 320 °F | Average value: 126 °C Grade Count:17 |
| Deflection Temperature at 0.46 MPa (66 psi) | 155 - 268 °C | 311 - 514 °F | Average value: 224 °C Grade Count:51 |
| Deflection Temperature at 1.8 MPa (264 psi) | 63.0 - 260 °C | 145 - 500 °F | Average value: 131 °C Grade Count:99 |
| Vicat Softening Point | 200 - 250 °C | 392 - 482 °F | Average value: 235 °C Grade Count:16 |
| Flammability, UL94 | HB - V-0 | HB - V-0 | Grade Count:68 |
| Oxygen Index | 26.0 - 27.0 % | 26.0 - 27.0 % | Average value: 26.3 % Grade Count:3 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 270 - 300 °C | 518 - 572 °F | Average value: 287 °C Grade Count:34 |
| Nozzle Temperature | 280 - 300 °C | 536 - 572 °F | Average value: 290 °C Grade Count:14 |
| Melt Temperature | 260 - 310 °C | 500 - 590 °F | Average value: 293 °C Grade Count:48 |
| Mold Temperature | 49.0 - 121 °C | 120 - 250 °F | Average value: 90.2 °C Grade Count:65 |
| Drying Temperature | 75.0 - 105 °C | 167 - 221 °F | Average value: 85.1 °C Grade Count:48 |
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | Average value: 3.86 hour Grade Count:29 |
| Moisture Content | 0.200 % | 0.200 % | Average value: 0.200 % Grade Count:30 |
| Dew Point | -17.8 °C | 0.000 °F | Average value: -17.8 °C Grade Count:22 |
| Injection Pressure | 4.96 - 124 MPa | 720 - 18000 psi | Average value: 97.0 MPa Grade Count:39 |
| Back Pressure | 0.000 - 0.345 MPa | 0.000 - 50.0 psi | Average value: 0.248 MPa Grade Count:8 |