- 密度 [g/cm3]: 1.6
- 吸水率 [%]: 0.35
- 缺口沖擊強度: 0.95
- 拉伸強度 [MPa]: 148.0
- 斷裂伸長率 [%]: 234
- 彎曲強度 [MPa]: 165.0
- 彎曲模量 [MPa]: 11.7
- 硬度: 115.0
- 熱變形溫度 [℃]: 220.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.60 - 1.85 g/cc | 0.0578 - 0.0668 lb/in3 | Average value: 1.70 g/cc Grade Count:46 |
| Filler Content | 60.0 % | 60.0 % | Average value: 60.0 % Grade Count:10 |
| Water Absorption | 0.350 - 3.60 % | 0.350 - 3.60 % | Average value: 1.07 % Grade Count:30 |
| Moisture Absorption at Equilibrium | 1.00 - 1.20 % | 1.00 - 1.20 % | Average value: 1.09 % Grade Count:8 |
| Water Absorption at Saturation | 3.20 - 3.70 % | 3.20 - 3.70 % | Average value: 3.43 % Grade Count:3 |
| Linear Mold Shrinkage | 0.000500 - 0.0200 cm/cm | 0.000500 - 0.0200 in/in | Average value: 0.00214 cm/cm Grade Count:36 |
| Linear Mold Shrinkage, Transverse | 0.00100 - 0.00800 cm/cm | 0.00100 - 0.00800 in/in | Average value: 0.00526 cm/cm Grade Count:14 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 88.0 - 100 | 88.0 - 100 | Average value: 94.0 Grade Count:4 |
| Hardness, Rockwell R | 115 - 122 | 115 - 122 | Average value: 120 Grade Count:16 |
| Ball Indentation Hardness | 360 - 420 MPa | 52200 - 60900 psi | Average value: 375 MPa Grade Count:4 |
| Tensile Strength, Ultimate | 165 - 318 MPa | 23900 - 46100 psi | Average value: 248 MPa Grade Count:25 |
| 127 - 353.701 MPa @Temperature -40.0 - 121 °C | 18400 - 51300.1 psi @Temperature -40.0 - 250 °F | Average value: 147 MPa Grade Count:3 | |
| 95.0 - 130 MPa @Temperature 130 - 175 °C | 13800 - 18900 psi @Temperature 266 - 347 °F | Average value: 147 MPa Grade Count:2 | |
| 95.0 - 130 MPa @Time 1.80e+7 - 7.20e+7 sec | 13800 - 18900 psi @Time 5000 - 20000 hour | Average value: 147 MPa Grade Count:2 | |
| Tensile Strength, Yield | 148 - 285 MPa | 21500 - 41300 psi | Average value: 223 MPa Grade Count:21 |
| 144.79 - 144.79 MPa @Temperature 93.3 - 93.3 °C | 21000 - 21000 psi @Temperature 200 - 200 °F | Average value: 145 MPa Grade Count:1 | |
| Elongation at Break | 1.00 - 4.00 % | 1.00 - 4.00 % | Average value: 1.86 % Grade Count:41 |
| 1.80 - 2.20 % @Temperature -40.0 - 121 °C | 1.80 - 2.20 % @Temperature -40.0 - 250 °F | Average value: 1.98 % Grade Count:2 | |
| Modulus of Elasticity | 10.3 - 28.0 GPa | 1500 - 4060 ksi | Average value: 20.8 GPa Grade Count:25 |
| 11.9 - 20.8566 GPa @Temperature -40.0 - 121 °C | 1730 - 3025.05 ksi @Temperature -40.0 - 250 °F | Average value: 14.9 GPa Grade Count:2 | |
| Flexural Yield Strength | 234 - 461 MPa | 33900 - 66900 psi | Average value: 357 MPa Grade Count:37 |
| 227.527 - 544.686 MPa @Temperature -40.0 - 121 °C | 33000.1 - 79000.1 psi @Temperature -40.0 - 250 °F | Average value: 344 MPa Grade Count:2 | |
| Flexural Modulus | 11.7 - 22.8 GPa | 1700 - 3300 ksi | Average value: 18.0 GPa Grade Count:37 |
| 8.70 - 19.3053 GPa @Temperature -40.0 - 121 °C | 1260 - 2800.04 ksi @Temperature -40.0 - 250 °F | Average value: 12.5 GPa Grade Count:4 | |
| Izod Impact, Notched | 0.950 - 6.62 J/cm | 1.78 - 12.4 ft-lb/in | Average value: 2.45 J/cm Grade Count:31 |
| 1.30 - 7.68816 J/cm @Temperature -40.0 - 149 °C | 2.44 - 14.4031 ft-lb/in @Temperature -40.0 - 300 °F | Average value: 4.51 J/cm Grade Count:2 | |
| Izod Impact, Unnotched | 10.7 - 5340 J/cm | 20.0 - 10000 ft-lb/in | Average value: 24.7 J/cm Grade Count:17 |
| Izod Impact, Notched (ISO) | 11.0 - 30.0 kJ/m2 | 5.23 - 14.3 ft-lb/in2 | Average value: 15.9 kJ/m2 Grade Count:5 |
| Charpy Impact Unnotched | 6.00 - 15.0 J/cm2 | 28.6 - 71.4 ft-lb/in2 | Average value: 8.65 J/cm2 Grade Count:13 |
| 6.00 - 9.70 J/cm2 @Temperature -40.0 - 30.0 °C | 28.6 - 46.2 ft-lb/in2 @Temperature -40.0 - 86.0 °F | Average value: 7.59 J/cm2 Grade Count:11 | |
| Charpy Impact, Notched | 1.10 - 5.40 J/cm2 | 5.24 - 25.7 ft-lb/in2 | Average value: 1.95 J/cm2 Grade Count:13 |
| 1.00 - 4.60 J/cm2 @Temperature -30.0 - 30.0 °C | 4.76 - 21.9 ft-lb/in2 @Temperature -22.0 - 86.0 °F | Average value: 1.39 J/cm2 Grade Count:10 | |
| Dart Drop, Total Energy | 7.85 - 16.4 J @Temperature -20.0 - -20.0 °C | 5.79 - 12.1 ft-lb @Temperature -4.00 - -4.00 °F | Average value: 12.1 J Grade Count:1 |
| 7.85 - 16.4 J @Thickness 3.18 - 3.18 mm | 5.79 - 12.1 ft-lb @Thickness 0.125 - 0.125 in | Average value: 12.1 J Grade Count:1 | |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+9 - 1.00e+16 ohm-cm | 1.00e+9 - 1.00e+16 ohm-cm | Average value: 5.00e+14 ohm-cm Grade Count:21 |
| Surface Resistance | 1.00e+10 - 1.00e+16 ohm | 1.00e+10 - 1.00e+16 ohm | Average value: 5.68e+14 ohm Grade Count:18 |
| Dielectric Strength | 19.7 - 35.0 kV/mm | 500 - 889 kV/in | Average value: 24.0 kV/mm Grade Count:18 |
| Comparative Tracking Index | 500 - 600 V | 500 - 600 V | Average value: 575 V Grade Count:6 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 10.0 - 27.0 μm/m-°C | 5.56 - 15.0 μin/in-°F | Average value: 20.3 μm/m-°C Grade Count:22 |
| CTE, linear, Transverse to Flow | 40.0 μm/m-°C | 22.2 μin/in-°F | Average value: 40.0 μm/m-°C Grade Count:5 |
| Thermal Conductivity | 0.300 - 0.548 W/m-K | 2.08 - 3.80 BTU-in/hr-ft2-°F | Average value: 0.424 W/m-K Grade Count:4 |
| Melting Point | 220 - 325 °C | 428 - 617 °F | Average value: 271 °C Grade Count:16 |
| Maximum Service Temperature, Air | 140 - 250 °C | 284 - 482 °F | Average value: 199 °C Grade Count:4 |
| Deflection Temperature at 0.46 MPa (66 psi) | 220 - 262 °C | 428 - 504 °F | Average value: 255 °C Grade Count:12 |
| Deflection Temperature at 1.8 MPa (264 psi) | 210 - 300 °C | 410 - 572 °F | Average value: 255 °C Grade Count:41 |
| Deflection Temperature at 8.0 MPa | 180 - 250 °C | 356 - 482 °F | Average value: 223 °C Grade Count:6 |
| Vicat Softening Point | 255 - 257 °C | 491 - 495 °F | Average value: 256 °C Grade Count:3 |
| Flammability, UL94 | HB | HB | Grade Count:18 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 70.0 - 300 °C | 158 - 572 °F | Average value: 176 °C Grade Count:8 |
| Feed Temperature | 20.0 - 265 °C | 68.0 - 509 °F | Average value: 82.5 °C Grade Count:7 |
| Nozzle Temperature | 271 - 304 °C | 520 - 580 °F | Average value: 285 °C Grade Count:3 |
| Die Temperature | 300 - 320 °C | 572 - 608 °F | Average value: 313 °C Grade Count:3 |
| Melt Temperature | 260 - 320 °C | 500 - 608 °F | Average value: 290 °C Grade Count:14 |
| Mold Temperature | 65.6 - 124 °C | 150 - 255 °F | Average value: 90.4 °C Grade Count:17 |
| Drying Temperature | 70.0 - 100 °C | 158 - 212 °F | Average value: 80.4 °C Grade Count:12 |
| Dry Time | 2.00 - 12.0 hour | 2.00 - 12.0 hour | Average value: 3.60 hour Grade Count:10 |
| 2.00 - 4.00 hour @Temperature 79.4 - 79.4 °C | 2.00 - 4.00 hour @Temperature 175 - 175 °F | Average value: 3.00 hour Grade Count:1 | |
| Moisture Content | 0.120 - 0.200 % | 0.120 - 0.200 % | Average value: 0.170 % Grade Count:10 |
| Dew Point | -30.0 - -17.8 °C | -22.0 - 0.000 °F | Average value: -25.6 °C Grade Count:3 |
| Injection Pressure | 4.96 - 150 MPa | 720 - 21800 psi | Average value: 82.5 MPa Grade Count:8 |
| Hold Pressure | 50.0 - 100 MPa | 7250 - 14500 psi | Average value: 71.0 MPa Grade Count:5 |
| Back Pressure | 0.345 - 3.00 MPa | 50.0 - 435 psi | Average value: 1.93 MPa Grade Count:4 |
| Screw Speed | 20.0 - 100 rpm | 20.0 - 100 rpm | Average value: 42.8 rpm Grade Count:4 |