- 熔體流動速率 [g/10min]: 1.0
- 密度 [g/cm3]: 1.2
- 吸水率 [%]: 0.3
- 缺口沖擊強度: 0.481
- 拉伸強度 [MPa]: 55.0
- 斷裂伸長率 [%]: 75.0
- 彎曲強度 [MPa]: 9.9
- 彎曲模量 [MPa]: 2.45
- 硬度: 111.0
- 熱變形溫度 [℃]: 238.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.20 - 1.72 g/cc | 0.0434 - 0.0621 lb/in3 | Average value: 1.45 g/cc Grade Count:279 |
| Filler Content | 35.0 - 46.0 % | 35.0 - 46.0 % | Average value: 40.0 % Grade Count:57 |
| Water Absorption | 0.300 - 7.60 % | 0.300 - 7.60 % | Average value: 2.05 % Grade Count:143 |
| Moisture Absorption at Equilibrium | 0.170 - 2.30 % | 0.170 - 2.30 % | Average value: 1.42 % Grade Count:67 |
| Water Absorption at Saturation | 3.50 - 8.00 % | 3.50 - 8.00 % | Average value: 5.03 % Grade Count:26 |
| Additive Loading | 35.0 - 40.0 % | 35.0 - 40.0 % | Average value: 38.3 % Grade Count:3 |
| Viscosity | 20.0 - 404000 cP @Temperature 275 - 315 °C | 20.0 - 404000 cP @Temperature 527 - 599 °F | Average value: 128000 cP Grade Count:4 |
| 20.0 - 404000 cP @Shear Rate 10.0 - 7000 1/s | 20.0 - 404000 cP @Shear Rate 10.0 - 7000 1/s | Average value: 128000 cP Grade Count:4 | |
| Viscosity Measurement | 0.400 - 150 | 0.400 - 150 | Average value: 124 Grade Count:20 |
| Viscosity Test | 140 - 150 cm3/g | 140 - 150 cm3/g | Average value: 144 cm3/g Grade Count:9 |
| Linear Mold Shrinkage | 0.000300 - 0.0200 cm/cm | 0.000300 - 0.0200 in/in | Average value: 0.00415 cm/cm Grade Count:213 |
| Linear Mold Shrinkage, 6.35 mm section | 0.00300 - 0.00500 cm/cm | 0.00300 - 0.00500 in/in | Average value: 0.00460 cm/cm Grade Count:10 |
| Linear Mold Shrinkage, Transverse | 0.000300 - 0.0180 cm/cm | 0.000300 - 0.0180 in/in | Average value: 0.00790 cm/cm Grade Count:82 |
| Melt Flow | 1.00 - 56.4 g/10 min | 1.00 - 56.4 g/10 min | Average value: 27.9 g/10 min Grade Count:27 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 80.0 - 105 | 80.0 - 105 | Average value: 96.1 Grade Count:32 |
| Hardness, Rockwell R | 111 - 125 | 111 - 125 | Average value: 121 Grade Count:58 |
| Hardness, Shore D | 80.0 - 86.0 | 80.0 - 86.0 | Average value: 82.7 Grade Count:5 |
| Ball Indentation Hardness | 130 - 310 MPa | 18900 - 45000 psi | Average value: 246 MPa Grade Count:12 |
| Tensile Strength, Ultimate | 9.90 - 253 MPa | 1440 - 36700 psi | Average value: 161 MPa Grade Count:212 |
| 72.0 - 269.585 MPa @Temperature -40.0 - 121 °C | 10400 - 39100.1 psi @Temperature -40.0 - 250 °F | Average value: 97.9 MPa Grade Count:10 | |
| 72.5 - 112.5 MPa @Temperature 130 - 175 °C | 10500 - 16320 psi @Temperature 266 - 347 °F | Average value: 97.9 MPa Grade Count:4 | |
| 72.5 - 112.5 MPa @Time 1.80e+7 - 7.20e+7 sec | 10500 - 16320 psi @Time 5000 - 20000 hour | Average value: 97.9 MPa Grade Count:4 | |
| 4.99 - 400 MPa @Strain 0.100 - 10.0 % | 724 - 58000 psi @Strain 0.100 - 10.0 % | Average value: 97.9 MPa Grade Count:9 | |
| 4.99 - 400 MPa @Temperature -40.0 - 200 °C | 724 - 58000 psi @Temperature -40.0 - 392 °F | Average value: 97.9 MPa Grade Count:9 | |
| Tensile Strength, Yield | 55.0 - 230 MPa | 7980 - 33400 psi | Average value: 178 MPa Grade Count:87 |
| Elongation at Break | 1.00 - 35.0 % | 1.00 - 35.0 % | Average value: 3.39 % Grade Count:246 |
| 2.00 - 2.90 % @Temperature -40.0 - 121 °C | 2.00 - 2.90 % @Temperature -40.0 - 250 °F | Average value: 2.40 % Grade Count:4 | |
| Elongation at Yield | 1.80 - 20.0 % | 1.80 - 20.0 % | Average value: 4.22 % Grade Count:30 |
| Modulus of Elasticity | 0.400 - 16.0 GPa | 58.0 - 2320 ksi | Average value: 11.0 GPa Grade Count:166 |
| 4.308 - 14.479 GPa @Temperature -40.0 - 150 °C | 624.8 - 2100.0 ksi @Temperature -40.0 - 302 °F | Average value: 7.86 GPa Grade Count:6 | |
| Flexural Yield Strength | 75.0 - 366 MPa | 10900 - 53100 psi | Average value: 269 MPa Grade Count:209 |
| 130 - 388.175 MPa @Temperature -40.0 - 121 °C | 18900 - 56300.1 psi @Temperature -40.0 - 250 °F | Average value: 225 MPa Grade Count:8 | |
| Flexural Modulus | 2.45 - 14.0 GPa | 355 - 2030 ksi | Average value: 9.97 GPa Grade Count:236 |
| 4.40 - 14.0 GPa @Temperature -40.0 - 121 °C | 638 - 2030 ksi @Temperature -40.0 - 250 °F | Average value: 7.22 GPa Grade Count:12 | |
| Compressive Yield Strength | 145 - 276 MPa | 21000 - 40000 psi | Average value: 214 MPa Grade Count:11 |
| Shear Strength | 72.0 - 93.0 MPa | 10400 - 13500 psi | Average value: 83.4 MPa Grade Count:10 |
| Izod Impact, Notched | 0.481 - 4.64 J/cm | 0.900 - 8.70 ft-lb/in | Average value: 1.54 J/cm Grade Count:134 |
| 0.750 - 4.64493 J/cm @Temperature -40.0 - 149 °C | 1.41 - 8.70186 ft-lb/in @Temperature -40.0 - 300 °F | Average value: 1.79 J/cm Grade Count:8 | |
| Izod Impact, Unnotched | 7.47 - 16.0 J/cm | 14.0 - 30.0 ft-lb/in | Average value: 11.6 J/cm Grade Count:47 |
| Izod Impact, Notched (ISO) | 2.50 - 66.0 kJ/m2 | 1.19 - 31.4 ft-lb/in2 | Average value: 14.2 kJ/m2 Grade Count:88 |
| 8.50 - 64.0 kJ/m2 @Temperature -40.0 - -30.0 °C | 4.04 - 30.5 ft-lb/in2 @Temperature -40.0 - -22.0 °F | Average value: 14.2 kJ/m2 Grade Count:20 | |
| Izod Impact, Unnotched (ISO) | 47.0 - 105 kJ/m2 | 22.4 - 50.0 ft-lb/in2 | Average value: 77.1 kJ/m2 Grade Count:16 |
| 43.0 - 105 kJ/m2 @Temperature -40.0 - -30.0 °C | 20.5 - 50.0 ft-lb/in2 @Temperature -40.0 - -22.0 °F | Average value: 71.3 kJ/m2 Grade Count:10 | |
| Charpy Impact Unnotched | 2.50 J/cm2 - NB | 11.9 ft-lb/in2 - NB | Average value: 8.08 J/cm2 Grade Count:125 |
| 2.40 - 999.9 J/cm2 @Temperature -40.0 - 30.0 °C | 11.4 - 4759 ft-lb/in2 @Temperature -40.0 - 86.0 °F | Average value: 6.68 J/cm2 Grade Count:59 | |
| Charpy Impact, Notched | 0.220 - 3.60 J/cm2 | 1.05 - 17.1 ft-lb/in2 | Average value: 1.51 J/cm2 Grade Count:128 |
| 0.500 - 20.0 J/cm2 @Temperature -40.0 - 30.0 °C | 2.38 - 95.2 ft-lb/in2 @Temperature -40.0 - 86.0 °F | Average value: 1.34 J/cm2 Grade Count:61 | |
| Dart Drop, Total Energy | 5.35 - 13.9 J @Temperature -20.0 - -20.0 °C | 3.95 - 10.3 ft-lb @Temperature -4.00 - -4.00 °F | Average value: 9.63 J Grade Count:1 |
| 5.35 - 13.9 J @Thickness 3.18 - 3.18 mm | 3.95 - 10.3 ft-lb @Thickness 0.125 - 0.125 in | Average value: 9.63 J Grade Count:1 | |
| Puncture Energy | 3.20 - 5.90 J | 2.36 - 4.35 ft-lb | Average value: 4.22 J Grade Count:3 |
| 2.60 - 17.8 J @Temperature -30.0 - -30.0 °C | 1.92 - 13.1 ft-lb @Temperature -22.0 - -22.0 °F | Average value: 4.89 J Grade Count:4 | |
| Tensile Creep Modulus, 1 hour | 0.000 - 10800 MPa | 0.000 - 1.57e+6 psi | Average value: 2880 MPa Grade Count:12 |
| 0.000 - 45.0 MPa @Temperature 60.0 - 100 °C | 0.000 - 6530 psi @Temperature 140 - 212 °F | Average value: 18.3 MPa Grade Count:1 | |
| 0.000 - 45.0 MPa @Strain 0.000 - 0.658 % | 0.000 - 6530 psi @Strain 0.000 - 0.658 % | Average value: 18.3 MPa Grade Count:1 | |
| Tensile Creep Modulus, 1000 hours | 0.000 - 7960 MPa | 0.000 - 1.15e+6 psi | Average value: 2040 MPa Grade Count:16 |
| 0.000 - 45.0 MPa @Temperature 60.0 - 100 °C | 0.000 - 6530 psi @Temperature 140 - 212 °F | Average value: 18.3 MPa Grade Count:1 | |
| 0.000 - 45.0 MPa @Strain 0.000 - 1.24 % | 0.000 - 6530 psi @Strain 0.000 - 1.24 % | Average value: 18.3 MPa Grade Count:1 | |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+10 - 2.00e+18 ohm-cm | 1.00e+10 - 2.00e+18 ohm-cm | Average value: 2.39e+16 ohm-cm Grade Count:136 |
| Surface Resistance | 1.00e+9 - 4.80e+15 ohm | 1.00e+9 - 4.80e+15 ohm | Average value: 2.08e+14 ohm Grade Count:83 |
| Dielectric Constant | 3.00 - 10.0 | 3.00 - 10.0 | Average value: 4.43 Grade Count:58 |
| Dielectric Strength | 16.1 - 90.0 kV/mm | 410 - 2290 kV/in | Average value: 34.1 kV/mm Grade Count:103 |
| Dissipation Factor | 0.00200 - 0.300 | 0.00200 - 0.300 | Average value: 0.0574 Grade Count:63 |
| Dielectric Loss Index | 0.0150 - 0.150 | 0.0150 - 0.150 | Average value: 0.0825 Grade Count:4 |
| Arc Resistance | 110 - 180 sec | 110 - 180 sec | Average value: 126 sec Grade Count:8 |
| Comparative Tracking Index | 250 - 600 V | 250 - 600 V | Average value: 502 V Grade Count:96 |
| Hot Wire Ignition, HWI | 2.00 - 30.0 sec | 2.00 - 30.0 sec | Average value: 9.70 sec Grade Count:3 |
| High Amp Arc Ignition, HAI | 0.000 - 120 arcs | 0.000 - 120 arcs | Average value: 72.0 arcs Grade Count:3 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 0.150 - 500 μm/m-°C | 0.0833 - 278 μin/in-°F | Average value: 67.8 μm/m-°C Grade Count:85 |
| 500 - 500 μm/m-°C @Temperature 55.0 - 160 °C | 278 - 278 μin/in-°F @Temperature 131 - 320 °F | Average value: 500 μm/m-°C Grade Count:1 | |
| CTE, linear, Transverse to Flow | 0.600 - 100 μm/m-°C | 0.333 - 55.6 μin/in-°F | Average value: 59.7 μm/m-°C Grade Count:33 |
| 128 - 128 μm/m-°C @Temperature 55.0 - 160 °C | 71.1 - 71.1 μin/in-°F @Temperature 131 - 320 °F | Average value: 128 μm/m-°C Grade Count:1 | |
| Specific Heat Capacity | 1.40 - 1.50 J/g-°C | 0.335 - 0.359 BTU/lb-°F | Average value: 1.48 J/g-°C Grade Count:11 |
| Thermal Conductivity | 0.340 - 0.519 W/m-K | 2.36 - 3.60 BTU-in/hr-ft2-°F | Average value: 0.386 W/m-K Grade Count:15 |
| Melting Point | 220 - 325 °C | 428 - 617 °F | Average value: 261 °C Grade Count:136 |
| Maximum Service Temperature, Air | 65.0 - 250 °C | 149 - 482 °F | Average value: 171 °C Grade Count:37 |
| Deflection Temperature at 0.46 MPa (66 psi) | 238 - 297 °C | 460 - 567 °F | Average value: 256 °C Grade Count:138 |
| Deflection Temperature at 1.8 MPa (264 psi) | 100 - 280 °C | 212 - 536 °F | Average value: 247 °C Grade Count:235 |
| Deflection Temperature at 8.0 MPa | 155 - 240 °C | 311 - 464 °F | Average value: 198 °C Grade Count:12 |
| Vicat Softening Point | 200 - 260 °C | 392 - 500 °F | Average value: 241 °C Grade Count:42 |
| Glass Transition Temp, Tg | 80.0 °C | 176 °F | Average value: 80.0 °C Grade Count:5 |
| UL RTI, Electrical | 115 - 140 °C | 239 - 284 °F | Average value: 134 °C Grade Count:6 |
| UL RTI, Mechanical with Impact | 120 - 130 °C | 248 - 266 °F | Average value: 125 °C Grade Count:4 |
| UL RTI, Mechanical without Impact | 130 - 140 °C | 266 - 284 °F | Average value: 138 °C Grade Count:4 |
| Flammability, UL94 | HB - 5VB | HB - 5VB | Grade Count:160 |
| Oxygen Index | 21.0 - 46.5 % | 21.0 - 46.5 % | Average value: 25.8 % Grade Count:38 |
| Glow Wire Test | 600 - 960 °C | 1110 - 1760 °F | Average value: 758 °C Grade Count:38 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 70.0 - 310 °C | 158 - 590 °F | Average value: 195 °C Grade Count:25 |
| Feed Temperature | 20.0 - 280 °C | 68.0 - 536 °F | Average value: 199 °C Grade Count:35 |
| Nozzle Temperature | 263 - 304 °C | 505 - 580 °F | Average value: 283 °C Grade Count:17 |
| Die Temperature | 300 - 320 °C | 572 - 608 °F | Average value: 311 °C Grade Count:6 |
| Melt Temperature | 230 - 320 °C | 446 - 608 °F | Average value: 285 °C Grade Count:132 |
| Mold Temperature | 50.0 - 135 °C | 122 - 275 °F | Average value: 87.1 °C Grade Count:138 |
| Drying Temperature | 70.0 - 130 °C | 158 - 266 °F | Average value: 81.2 °C Grade Count:103 |
| Dry Time | 2.00 - 12.0 hour | 2.00 - 12.0 hour | Average value: 3.71 hour Grade Count:73 |
| 2.00 - 4.00 hour @Temperature 79.4 - 79.4 °C | 2.00 - 4.00 hour @Temperature 175 - 175 °F | Average value: 3.00 hour Grade Count:3 | |
| Moisture Content | 0.0200 - 0.200 % | 0.0200 - 0.200 % | Average value: 0.175 % Grade Count:99 |
| Dew Point | -30.0 - -17.8 °C | -22.0 - 0.000 °F | Average value: -20.9 °C Grade Count:19 |
| Injection Pressure | 4.96 - 150 MPa | 720 - 21800 psi | Average value: 87.8 MPa Grade Count:52 |
| Hold Pressure | 50.0 - 140 MPa | 7250 - 20300 psi | Average value: 76.1 MPa Grade Count:12 |
| Back Pressure | 0.000 - 3.00 MPa | 0.000 - 435 psi | Average value: 1.04 MPa Grade Count:18 |
| Shot Size | 30.0 - 80.0 % | 30.0 - 80.0 % | Average value: 55.0 % Grade Count:3 |
| Cushion | 0.300 - 0.650 cm | 0.118 - 0.256 in | Average value: 0.556 cm Grade Count:4 |
| Screw Speed | 20.0 - 120 rpm | 20.0 - 120 rpm | Average value: 52.7 rpm Grade Count:15 |
| Hot-Working Temperature | 300 - 315 °C | 572 - 599 °F | Average value: 308 °C Grade Count:4 |