- 密度 [g/cm3]: 1.21
- 吸水率 [%]: 0.4
- 缺口沖擊強度: 0.534
- 斷裂伸長率 [%]: 215
- 彎曲強度 [MPa]: 137.0
- 彎曲模量 [MPa]: 0.0000193
- 硬度: 97.0
- 熱變形溫度 [℃]: 240.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.21 - 1.57 g/cc | 0.0437 - 0.0567 lb/in3 | Average value: 1.30 g/cc Grade Count:27 |
| Filler Content | 25.0 - 30.0 % | 25.0 - 30.0 % | Average value: 29.2 % Grade Count:13 |
| Water Absorption | 0.400 - 2.40 % | 0.400 - 2.40 % | Average value: 0.751 % Grade Count:13 |
| Moisture Absorption at Equilibrium | 1.70 - 2.30 % | 1.70 - 2.30 % | Average value: 1.92 % Grade Count:4 |
| Viscosity Measurement | 0.110 - 145 | 0.110 - 145 | Average value: 96.8 Grade Count:3 |
| Linear Mold Shrinkage | 0.000200 - 0.0150 cm/cm | 0.000200 - 0.0150 in/in | Average value: 0.00263 cm/cm Grade Count:24 |
| Linear Mold Shrinkage, 6.35 mm section | 0.00200 cm/cm | 0.00200 in/in | Average value: 0.00200 cm/cm Grade Count:4 |
| Linear Mold Shrinkage, Transverse | 0.00400 - 0.0120 cm/cm | 0.00400 - 0.0120 in/in | Average value: 0.00726 cm/cm Grade Count:8 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 97.0 - 120 | 97.0 - 120 | Average value: 116 Grade Count:7 |
| Tensile Strength, Ultimate | 137 - 300 MPa | 19900 - 43500 psi | Average value: 213 MPa Grade Count:25 |
| 105 - 260 MPa @Temperature -40.0 - 120 °C | 15200 - 37700 psi @Temperature -40.0 - 248 °F | Average value: 163 MPa Grade Count:2 | |
| Elongation at Break | 1.00 - 4.00 % | 1.00 - 4.00 % | Average value: 2.30 % Grade Count:24 |
| Modulus of Elasticity | 16.0 - 33.1 GPa | 2320 - 4800 ksi | Average value: 21.5 GPa Grade Count:20 |
| Flexural Yield Strength | 215 - 420 MPa | 31200 - 60900 psi | Average value: 316 MPa Grade Count:21 |
| 140 - 337 MPa @Temperature -40.0 - 80.0 °C | 20300 - 48900 psi @Temperature -40.0 - 176 °F | Average value: 252 MPa Grade Count:1 | |
| Flexural Modulus | 0.0000193 - 29.0 GPa | 0.00280 - 4200 ksi | Average value: 15.9 GPa Grade Count:23 |
| 7.20 - 19.0 GPa @Temperature -40.0 - 120 °C | 1040 - 2760 ksi @Temperature -40.0 - 248 °F | Average value: 11.9 GPa Grade Count:2 | |
| Compressive Yield Strength | 152 - 172 MPa | 22000 - 25000 psi | Average value: 164 MPa Grade Count:4 |
| Izod Impact, Notched | 0.534 - 2.40 J/cm | 1.00 - 4.50 ft-lb/in | Average value: 1.22 J/cm Grade Count:18 |
| 0.550 - 0.800 J/cm @Temperature -40.0 - -20.0 °C | 1.03 - 1.50 ft-lb/in @Temperature -40.0 - -4.00 °F | Average value: 0.667 J/cm Grade Count:2 | |
| Izod Impact, Unnotched | 6.41 - 10.1 J/cm | 12.0 - 19.0 ft-lb/in | Average value: 8.26 J/cm Grade Count:12 |
| Izod Impact, Notched (ISO) | 6.50 - 10.0 kJ/m2 | 3.09 - 4.76 ft-lb/in2 | Average value: 8.12 kJ/m2 Grade Count:3 |
| Charpy Impact Unnotched | 2.30 - 9.00 J/cm2 | 10.9 - 42.8 ft-lb/in2 | Average value: 5.10 J/cm2 Grade Count:7 |
| 1.60 - 8.50 J/cm2 @Temperature -40.0 - -20.0 °C | 7.61 - 40.5 ft-lb/in2 @Temperature -40.0 - -4.00 °F | Average value: 3.94 J/cm2 Grade Count:5 | |
| Charpy Impact, Notched | 0.600 - 1.80 J/cm2 | 2.86 - 8.57 ft-lb/in2 | Average value: 0.986 J/cm2 Grade Count:6 |
| 0.500 - 1.00 J/cm2 @Temperature -40.0 - -20.0 °C | 2.38 - 4.76 ft-lb/in2 @Temperature -40.0 - -4.00 °F | Average value: 0.800 J/cm2 Grade Count:3 | |
| Dart Drop, Total Energy | 6.19 - 12.2 J @Temperature -20.0 - -20.0 °C | 4.57 - 9.00 ft-lb @Temperature -4.00 - -4.00 °F | Average value: 9.19 J Grade Count:1 |
| 6.19 - 12.2 J @Thickness 3.18 - 3.18 mm | 4.57 - 9.00 ft-lb @Thickness 0.125 - 0.125 in | Average value: 9.19 J Grade Count:1 | |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 0.0100 - 100000 ohm-cm | 0.0100 - 100000 ohm-cm | Average value: 7290 ohm-cm Grade Count:14 |
| Surface Resistance | 10.0 - 100000 ohm | 10.0 - 100000 ohm | Average value: 13900 ohm Grade Count:7 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 6.00 - 25.0 μm/m-°C | 3.33 - 13.9 μin/in-°F | Average value: 16.8 μm/m-°C Grade Count:7 |
| Melting Point | 221 - 263 °C | 430 - 505 °F | Average value: 255 °C Grade Count:10 |
| Deflection Temperature at 0.46 MPa (66 psi) | 240 - 260 °C | 464 - 500 °F | Average value: 257 °C Grade Count:10 |
| Deflection Temperature at 1.8 MPa (264 psi) | 230 - 260 °C | 446 - 500 °F | Average value: 252 °C Grade Count:21 |
| Vicat Softening Point | 230 - 254 °C | 446 - 489 °F | Average value: 241 °C Grade Count:4 |
| Flammability, UL94 | HB - V-0 | HB - V-0 | Grade Count:15 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 270 - 300 °C | 518 - 572 °F | Average value: 284 °C Grade Count:5 |
| Melt Temperature | 260 - 320 °C | 500 - 608 °F | Average value: 286 °C Grade Count:15 |
| Mold Temperature | 60.0 - 140 °C | 140 - 284 °F | Average value: 88.2 °C Grade Count:20 |
| Drying Temperature | 79.4 - 107 °C | 175 - 225 °F | Average value: 83.6 °C Grade Count:13 |
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | Average value: 3.88 hour Grade Count:8 |
| Moisture Content | 0.150 - 0.200 % | 0.150 - 0.200 % | Average value: 0.187 % Grade Count:9 |
| Dew Point | -28.9 - -17.8 °C | -20.0 - 0.000 °F | Average value: -19.6 °C Grade Count:6 |
| Injection Pressure | 30.0 - 124 MPa | 4350 - 18000 psi | Average value: 93.1 MPa Grade Count:13 |