- 熔體流動速率 [g/10min]: 1.0
- 密度 [g/cm3]: 1.09
- 吸水率 [%]: 0.35
- 缺口沖擊強度: 0.32
- 拉伸強度 [MPa]: 10.3
- 斷裂伸長率 [%]: 43.0
- 彎曲強度 [MPa]: 3.0
- 彎曲模量 [MPa]: 0.483
- 硬度: 95.0
- 熱變形溫度 [℃]: 204.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.09 - 1.70 g/cc | 0.0394 - 0.0614 lb/in3 | Average value: 1.23 g/cc Grade Count:204 |
| Filler Content | 5.00 - 15.0 % | 5.00 - 15.0 % | Average value: 11.6 % Grade Count:55 |
| Water Absorption | 0.350 - 8.00 % | 0.350 - 8.00 % | Average value: 1.95 % Grade Count:112 |
| Moisture Absorption at Equilibrium | 1.80 - 3.00 % | 1.80 - 3.00 % | Average value: 2.22 % Grade Count:19 |
| Water Absorption at Saturation | 5.50 - 8.00 % | 5.50 - 8.00 % | Average value: 6.97 % Grade Count:12 |
| Viscosity | 67000 - 308000 cP @Temperature 275 - 315 °C | 67000 - 308000 cP @Temperature 527 - 599 °F | Average value: 158000 cP Grade Count:1 |
| 67000 - 308000 cP @Shear Rate 500 - 7000 1/s | 67000 - 308000 cP @Shear Rate 500 - 7000 1/s | Average value: 158000 cP Grade Count:1 | |
| Viscosity Measurement | 0.420 - 145 | 0.420 - 145 | Average value: 71.1 Grade Count:11 |
| Viscosity Test | 148 - 150 cm3/g | 148 - 150 cm3/g | Average value: 149 cm3/g Grade Count:3 |
| Linear Mold Shrinkage | 0.00120 - 0.0200 cm/cm | 0.00120 - 0.0200 in/in | Average value: 0.00724 cm/cm Grade Count:177 |
| Linear Mold Shrinkage, 6.35 mm section | 0.00800 - 0.0160 cm/cm | 0.00800 - 0.0160 in/in | Average value: 0.0114 cm/cm Grade Count:10 |
| Linear Mold Shrinkage, Transverse | 0.00500 - 0.0150 cm/cm | 0.00500 - 0.0150 in/in | Average value: 0.00973 cm/cm Grade Count:38 |
| Melt Flow | 1.00 - 80.0 g/10 min | 1.00 - 80.0 g/10 min | Average value: 25.0 g/10 min Grade Count:9 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 70.0 - 95.0 | 70.0 - 95.0 | Average value: 86.6 Grade Count:15 |
| Hardness, Rockwell R | 95.0 - 122 | 95.0 - 122 | Average value: 116 Grade Count:84 |
| Hardness, Shore D | 73.0 - 81.0 | 73.0 - 81.0 | Average value: 76.0 Grade Count:3 |
| Ball Indentation Hardness | 102 - 165 MPa | 14800 - 23900 psi | Average value: 139 MPa Grade Count:5 |
| Tensile Strength, Ultimate | 3.00 - 135 MPa | 435 - 19600 psi | Average value: 73.0 MPa Grade Count:146 |
| 35.0 - 57.5 MPa @Temperature 130 - 175 °C | 5080 - 8340 psi @Temperature 266 - 347 °F | Average value: 49.9 MPa Grade Count:2 | |
| 35.0 - 57.5 MPa @Time 1.80e+7 - 7.20e+7 sec | 5080 - 8340 psi @Time 5000 - 20000 hour | Average value: 49.9 MPa Grade Count:2 | |
| 1.30 - 165 MPa @Strain 0.100 - 20.0 % | 189 - 23900 psi @Strain 0.100 - 20.0 % | Average value: 49.9 MPa Grade Count:6 | |
| 1.30 - 165 MPa @Temperature -40.0 - 150 °C | 189 - 23900 psi @Temperature -40.0 - 302 °F | Average value: 49.9 MPa Grade Count:6 | |
| Tensile Strength, Yield | 10.3 - 252 MPa | 1500 - 36500 psi | Average value: 101 MPa Grade Count:67 |
| Elongation at Break | 1.50 - 20.0 % | 1.50 - 20.0 % | Average value: 5.05 % Grade Count:181 |
| Elongation at Yield | 2.75 - 50.0 % | 2.75 - 50.0 % | Average value: 7.23 % Grade Count:16 |
| Modulus of Elasticity | 1.79 - 36.5 GPa | 260 - 5290 ksi | Average value: 5.01 GPa Grade Count:76 |
| 1.641 - 6.113 GPa @Temperature -40.0 - 150 °C | 238.0 - 886.6 ksi @Temperature -40.0 - 302 °F | Average value: 3.56 GPa Grade Count:1 | |
| Flexural Yield Strength | 43.0 - 407 MPa | 6240 - 59000 psi | Average value: 147 MPa Grade Count:159 |
| Flexural Modulus | 0.483 - 36.2 GPa | 70.0 - 5250 ksi | Average value: 4.78 GPa Grade Count:191 |
| Compressive Yield Strength | 89.6 - 172 MPa | 13000 - 24900 psi | Average value: 122 MPa Grade Count:3 |
| Shear Modulus | 0.130 - 1.471 GPa @Temperature -50.0 - 250 °C | 18.9 - 213.4 ksi @Temperature -58.0 - 482 °F | Average value: 0.666 GPa Grade Count:1 |
| Shear Strength | 42.0 - 76.0 MPa | 6090 - 11000 psi | Average value: 62.7 MPa Grade Count:9 |
| Izod Impact, Notched | 0.320 - 5.34 J/cm | 0.600 - 10.0 ft-lb/in | Average value: 0.897 J/cm Grade Count:152 |
| 0.69407 - 0.69407 J/cm @Temperature -40.0 - -40.0 °C | 1.3003 - 1.3003 ft-lb/in @Temperature -40.0 - -40.0 °F | Average value: 1.08 J/cm Grade Count:1 | |
| 1.0678 - 1.33475 J/cm @Temperature -40.0 - -40.0 °C | 2.0004 - 2.50053 ft-lb/in @Temperature -40.0 - -40.0 °F | Average value: 1.08 J/cm Grade Count:10 | |
| 1.0678 - 1.33475 J/cm @Thickness 3.17 - 3.17 mm | 2.0004 - 2.50053 ft-lb/in @Thickness 0.125 - 0.125 in | Average value: 1.08 J/cm Grade Count:10 | |
| Izod Impact, Unnotched | 2.67 - 5340 J/cm | 5.00 - 10000 ft-lb/in | Average value: 5.36 J/cm Grade Count:46 |
| Izod Impact, Notched (ISO) | 3.00 - 18.0 kJ/m2 | 1.43 - 8.57 ft-lb/in2 | Average value: 8.34 kJ/m2 Grade Count:36 |
| 3.00 - 12.0 kJ/m2 @Temperature -40.0 - 0.000 °C | 1.43 - 5.71 ft-lb/in2 @Temperature -40.0 - 32.0 °F | Average value: 6.02 kJ/m2 Grade Count:14 | |
| Izod Impact, Unnotched (ISO) | 35.0 - 100 kJ/m2 | 16.7 - 47.6 ft-lb/in2 | Average value: 60.0 kJ/m2 Grade Count:8 |
| 28.0 - 90.0 kJ/m2 @Temperature -30.0 - -30.0 °C | 13.3 - 42.8 ft-lb/in2 @Temperature -22.0 - -22.0 °F | Average value: 52.3 kJ/m2 Grade Count:6 | |
| Charpy Impact Unnotched | 2.00 J/cm2 - NB | 9.52 ft-lb/in2 - NB | Average value: 5.35 J/cm2 Grade Count:42 |
| 2.40 - 9.00 J/cm2 @Temperature -40.0 - -20.0 °C | 11.4 - 42.8 ft-lb/in2 @Temperature -40.0 - -4.00 °F | Average value: 4.69 J/cm2 Grade Count:26 | |
| Charpy Impact, Notched | 0.400 - 1.80 J/cm2 | 1.90 - 8.57 ft-lb/in2 | Average value: 0.862 J/cm2 Grade Count:49 |
| 0.200 - 1.20 J/cm2 @Temperature -40.0 - -20.0 °C | 0.952 - 5.71 ft-lb/in2 @Temperature -40.0 - -4.00 °F | Average value: 0.577 J/cm2 Grade Count:32 | |
| Tensile Creep Modulus, 1 hour | 0.000 - 4030 MPa | 0.000 - 585000 psi | Average value: 1050 MPa Grade Count:5 |
| 0.000 - 20.0 MPa @Temperature 80.0 - 80.0 °C | 0.000 - 2900 psi @Temperature 176 - 176 °F | Average value: 8.75 MPa Grade Count:1 | |
| 0.000 - 20.0 MPa @Strain 0.000 - 0.833 % | 0.000 - 2900 psi @Strain 0.000 - 0.833 % | Average value: 8.75 MPa Grade Count:1 | |
| Tensile Creep Modulus, 1000 hours | 0.000 - 3180 MPa | 0.000 - 461000 psi | Average value: 587 MPa Grade Count:5 |
| 0.000 - 20.0 MPa @Temperature 80.0 - 80.0 °C | 0.000 - 2900 psi @Temperature 176 - 176 °F | Average value: 8.75 MPa Grade Count:1 | |
| 0.000 - 20.0 MPa @Strain 0.000 - 1.11 % | 0.000 - 2900 psi @Strain 0.000 - 1.11 % | Average value: 8.75 MPa Grade Count:1 | |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 10.0 - 1.00e+17 ohm-cm | 10.0 - 1.00e+17 ohm-cm | Average value: 2.73e+15 ohm-cm Grade Count:89 |
| Surface Resistance | 10.0 - 1.00e+15 ohm | 10.0 - 1.00e+15 ohm | Average value: 1.24e+14 ohm Grade Count:32 |
| Static Decay | 0.100 - 2.00 sec | 0.100 - 2.00 sec | Average value: 1.62 sec Grade Count:5 |
| Dielectric Constant | 3.10 - 9.80 | 3.10 - 9.80 | Average value: 4.46 Grade Count:16 |
| Dielectric Strength | 15.0 - 111 kV/mm | 381 - 2820 kV/in | Average value: 26.2 kV/mm Grade Count:58 |
| Dissipation Factor | 0.00650 - 0.250 | 0.00650 - 0.250 | Average value: 0.0515 Grade Count:17 |
| Dielectric Loss Index | 0.0150 - 0.150 | 0.0150 - 0.150 | Average value: 0.0825 Grade Count:4 |
| Arc Resistance | 0.000 - 120 sec | 0.000 - 120 sec | Average value: 80.0 sec Grade Count:4 |
| Comparative Tracking Index | 250 - 600 V | 250 - 600 V | Average value: 531 V Grade Count:30 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 4.00 - 500 μm/m-°C | 2.22 - 278 μin/in-°F | Average value: 192 μm/m-°C Grade Count:65 |
| 500 - 500 μm/m-°C @Temperature 55.0 - 160 °C | 278 - 278 μin/in-°F @Temperature 131 - 320 °F | Average value: 500 μm/m-°C Grade Count:6 | |
| CTE, linear, Transverse to Flow | 9.50 - 130 μm/m-°C | 5.28 - 72.2 μin/in-°F | Average value: 96.1 μm/m-°C Grade Count:11 |
| 123 - 158 μm/m-°C @Temperature 55.0 - 160 °C | 68.3 - 87.8 μin/in-°F @Temperature 131 - 320 °F | Average value: 143 μm/m-°C Grade Count:6 | |
| Melting Point | 250 - 265 °C | 482 - 509 °F | Average value: 258 °C Grade Count:96 |
| Maximum Service Temperature, Air | 65.0 - 240 °C | 149 - 464 °F | Average value: 112 °C Grade Count:9 |
| Deflection Temperature at 0.46 MPa (66 psi) | 204 - 262 °C | 400 - 504 °F | Average value: 249 °C Grade Count:104 |
| Deflection Temperature at 1.8 MPa (264 psi) | 60.0 - 257 °C | 140 - 495 °F | Average value: 230 °C Grade Count:177 |
| Vicat Softening Point | 200 - 261 °C | 392 - 502 °F | Average value: 237 °C Grade Count:19 |
| UL RTI, Electrical | 65.0 - 140 °C | 149 - 284 °F | Average value: 122 °C Grade Count:10 |
| UL RTI, Mechanical with Impact | 65.0 - 125 °C | 149 - 257 °F | Average value: 104 °C Grade Count:10 |
| UL RTI, Mechanical without Impact | 65.0 - 140 °C | 149 - 284 °F | Average value: 117 °C Grade Count:10 |
| Flammability, UL94 | HB - V-0 | HB - V-0 | Grade Count:119 |
| Oxygen Index | 21.0 - 34.0 % | 21.0 - 34.0 % | Average value: 27.8 % Grade Count:8 |
| Glow Wire Test | 650 - 960 °C | 1200 - 1760 °F | Average value: 717 °C Grade Count:17 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 221 - 310 °C | 430 - 590 °F | Average value: 284 °C Grade Count:19 |
| Feed Temperature | 60.0 - 270 °C | 140 - 518 °F | Average value: 136 °C Grade Count:6 |
| Nozzle Temperature | 250 - 295 °C | 482 - 563 °F | Average value: 275 °C Grade Count:17 |
| Melt Temperature | 230 - 320 °C | 446 - 608 °F | Average value: 280 °C Grade Count:72 |
| Mold Temperature | 26.7 - 121 °C | 80.0 - 250 °F | Average value: 83.7 °C Grade Count:82 |
| Drying Temperature | 71.1 - 130 °C | 160 - 266 °F | Average value: 80.8 °C Grade Count:58 |
| Dry Time | 2.00 - 12.0 hour | 2.00 - 12.0 hour | Average value: 3.71 hour Grade Count:50 |
| 2.00 - 6.00 hour @Temperature 79.4 - 80.0 °C | 2.00 - 6.00 hour @Temperature 175 - 176 °F | Average value: 3.20 hour Grade Count:5 | |
| Moisture Content | 0.0300 - 2.30 % | 0.0300 - 2.30 % | Average value: 0.241 % Grade Count:39 |
| Dew Point | -17.8 °C | 0.000 °F | Average value: -17.8 °C Grade Count:12 |
| Injection Pressure | 4.96 - 140 MPa | 720 - 20300 psi | Average value: 80.3 MPa Grade Count:45 |
| Hold Pressure | 50.0 - 140 MPa | 7250 - 20300 psi | Average value: 80.6 MPa Grade Count:4 |
| Back Pressure | 0.000 - 58.8 MPa | 0.000 - 8530 psi | Average value: 5.83 MPa Grade Count:18 |
| Shot Size | 30.0 - 80.0 % | 30.0 - 80.0 % | Average value: 51.7 % Grade Count:6 |
| Screw Speed | 20.0 - 120 rpm | 20.0 - 120 rpm | Average value: 62.4 rpm Grade Count:18 |