- 密度 [g/cm3]: 1.27
- 吸水率 [%]: 1.2
- 缺口沖擊強度: 0.534
- 拉伸強度 [MPa]: 58.6
- 彎曲模量 [MPa]: 1.21
- 硬度: 100.0
- 熱變形溫度 [℃]: 221.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.27 g/cc | 0.0459 lb/in3 | ASTM D792 |
| Water Absorption | 1.2 % @Time 86400 sec | 1.2 % @Time 24.0 hour | ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.032 cm/cm @Thickness 3.17 mm | 0.032 in/in @Thickness 0.125 in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 100 | 100 | ASTM D785 |
| Tensile Strength, Yield | 58.6 MPa | 8500 psi | ASTM D638 |
| Elongation at Break | 300 % | 300 % | ASTM D638 |
| Flexural Strength | 62.1 MPa | 9000 psi | ASTM D790 |
| Flexural Modulus | 1.21 GPa | 175 ksi | ASTM D790 |
| Izod Impact, Notched | 0.534 J/cm @Thickness 3.17 mm, Temperature -40.0 °C | 1.00 ft-lb/in @Thickness 0.125 in, Temperature -40.0 °F | ASTM D256 |
| 2.94 J/cm @Thickness 3.17 mm, Temperature 22.8 °C | 5.50 ft-lb/in @Thickness 0.125 in, Temperature 73.0 °F | ASTM D256 | |
| Izod Impact, Unnotched | NB @Thickness 3.17 mm | NB @Thickness 0.125 in | ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | ASTM D257 |
| Dielectric Strength | 21.7 kV/mm | 550 kV/in | Method A (Short-Time); ASTM D149 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 79.2 μm/m-°C | 44.0 μin/in-°F | ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 221 °C | 430 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 160 °C | 320 °F | Unannealed; ASTM D648 |