- 熔體流動速率 [g/10min]: 1.0
- 密度 [g/cm3]: 1.03
- 吸水率 [%]: 0.4
- 缺口沖擊強度: 0.534
- 拉伸強度 [MPa]: 37.0
- 斷裂伸長率 [%]: 20.0
- 彎曲強度 [MPa]: 28.0
- 彎曲模量 [MPa]: 0.0700
- 硬度: 82.0
- 熱變形溫度 [℃]: 80.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.03 - 1.46 g/cc | 0.0372 - 0.0527 lb/in3 | Average value: 1.11 g/cc Grade Count:244 |
| Water Absorption | 0.400 - 8.00 % | 0.400 - 8.00 % | Average value: 1.88 % Grade Count:114 |
| Moisture Absorption at Equilibrium | 0.170 - 3.10 % | 0.170 - 3.10 % | Average value: 2.06 % Grade Count:40 |
| Water Absorption at Saturation | 5.50 - 9.00 % | 5.50 - 9.00 % | Average value: 7.08 % Grade Count:15 |
| Viscosity Measurement | 0.980 - 145 | 0.980 - 145 | Average value: 49.8 Grade Count:12 |
| Linear Mold Shrinkage | 0.00150 - 0.0350 cm/cm | 0.00150 - 0.0350 in/in | Average value: 0.0153 cm/cm Grade Count:199 |
| Linear Mold Shrinkage, 6.35 mm section | 0.0180 - 0.0280 cm/cm | 0.0180 - 0.0280 in/in | Average value: 0.0220 cm/cm Grade Count:4 |
| Linear Mold Shrinkage, Transverse | 0.00800 - 0.0302 cm/cm | 0.00800 - 0.0302 in/in | Average value: 0.0178 cm/cm Grade Count:35 |
| Melt Flow | 1.00 - 2.00 g/10 min | 1.00 - 2.00 g/10 min | Average value: 1.81 g/10 min Grade Count:10 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 60.0 - 93.0 | 60.0 - 93.0 | Average value: 76.4 Grade Count:14 |
| Hardness, Rockwell R | 82.0 - 120 | 82.0 - 120 | Average value: 109 Grade Count:91 |
| Hardness, Shore D | 70.0 - 81.0 | 70.0 - 81.0 | Average value: 73.7 Grade Count:6 |
| Ball Indentation Hardness | 100 - 160 MPa | 14500 - 23200 psi | Average value: 125 MPa Grade Count:7 |
| Tensile Strength, Ultimate | 28.0 - 331 MPa | 4060 - 48000 psi | Average value: 60.3 MPa Grade Count:146 |
| Tensile Strength, Yield | 37.0 - 162 MPa | 5370 - 23500 psi | Average value: 62.4 MPa Grade Count:110 |
| Elongation at Break | 1.00 - 260 % | 1.00 - 260 % | Average value: 56.1 % Grade Count:201 |
| Elongation at Yield | 2.00 - 210 % | 2.00 - 210 % | Average value: 24.1 % Grade Count:50 |
| Modulus of Elasticity | 0.600 - 41.4 GPa | 87.0 - 6000 ksi | Average value: 3.11 GPa Grade Count:71 |
| Flexural Yield Strength | 20.0 - 507 MPa | 2900 - 73500 psi | Average value: 85.1 MPa Grade Count:188 |
| 15.0 - 15.0 MPa @Temperature 90.0 - 90.0 °C | 2180 - 2180 psi @Temperature 194 - 194 °F | Average value: 15.0 MPa Grade Count:1 | |
| Flexural Modulus | 0.0700 - 36.2 GPa | 10.2 - 5250 ksi | Average value: 2.67 GPa Grade Count:222 |
| 0.300 - 0.300 GPa @Temperature 90.0 - 90.0 °C | 43.5 - 43.5 ksi @Temperature 194 - 194 °F | Average value: 0.300 GPa Grade Count:1 | |
| Compressive Yield Strength | 30.3 - 100 MPa | 4400 - 14500 psi | Average value: 63.5 MPa Grade Count:6 |
| Shear Strength | 41.0 - 57.0 MPa | 5950 - 8270 psi | Average value: 49.0 MPa Grade Count:4 |
| Izod Impact, Notched | 0.534 - 5340 J/cm | 1.00 - 10000 ft-lb/in | Average value: 5.04 J/cm Grade Count:160 |
| 0.300 - 5.339 J/cm @Temperature -40.0 - -40.0 °C | 0.562 - 10.00 ft-lb/in @Temperature -40.0 - -40.0 °F | Average value: 1.51 J/cm Grade Count:5 | |
| 0.5339 - 2.6695 J/cm @Temperature -40.0 - 72.8 °C | 1.000 - 5.0011 ft-lb/in @Temperature -40.0 - 163 °F | Average value: 1.51 J/cm Grade Count:18 | |
| 0.5339 - 2.6695 J/cm @Thickness 3.17 - 3.17 mm | 1.000 - 5.0011 ft-lb/in @Thickness 0.125 - 0.125 in | Average value: 1.51 J/cm Grade Count:18 | |
| Izod Impact, Unnotched | 0.430 J/cm - NB | 0.806 ft-lb/in - NB | Average value: 11.2 J/cm Grade Count:38 |
| Izod Impact, Notched (ISO) | 10.0 kJ/m2 - NB | 4.76 ft-lb/in2 - NB | Average value: 48.8 kJ/m2 Grade Count:43 |
| 12.0 - 90.0 kJ/m2 @Temperature -40.0 - -20.0 °C | 5.71 - 42.8 ft-lb/in2 @Temperature -40.0 - -4.00 °F | Average value: 28.6 kJ/m2 Grade Count:18 | |
| Izod Impact, Unnotched (ISO) | 96.0 kJ/m2 - NB | 45.7 ft-lb/in2 - NB | Average value: 97.0 kJ/m2 Grade Count:8 |
| NB - NB @Temperature -30.0 - -30.0 °C | NB - NB @Temperature -22.0 - -22.0 °F | Grade Count:5 | |
| Charpy Impact Unnotched | 9.00 J/cm2 - NB | 42.8 ft-lb/in2 - NB | Average value: 16.0 J/cm2 Grade Count:46 |
| 4.40 J/cm2 - NB @Temperature -40.0 - -20.0 °C | 20.9 ft-lb/in2 - NB @Temperature -40.0 - -4.00 °F | Average value: 8.63 J/cm2 Grade Count:28 | |
| Charpy Impact, Notched | 0.450 J/cm2 - NB | 2.14 ft-lb/in2 - NB | Average value: 3.83 J/cm2 Grade Count:56 |
| 0.450 - 6.50 J/cm2 @Temperature -30.0 - -20.0 °C | 2.14 - 30.9 ft-lb/in2 @Temperature -22.0 - -4.00 °F | Average value: 2.09 J/cm2 Grade Count:31 | |
| Gardner Impact | 36.2 - 38.0 J | 26.7 - 28.0 ft-lb | Average value: 36.8 J Grade Count:3 |
| 12.2024 - 12.2024 J @Temperature -40.0 - -40.0 °C | 9.00001 - 9.00001 ft-lb @Temperature -40.0 - -40.0 °F | Average value: 12.2 J Grade Count:1 | |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00 - 1.00e+16 ohm-cm | 1.00 - 1.00e+16 ohm-cm | Average value: 1.02e+15 ohm-cm Grade Count:101 |
| Surface Resistance | 1.00 - 1.00e+16 ohm | 1.00 - 1.00e+16 ohm | Average value: 2.63e+14 ohm Grade Count:59 |
| Dielectric Constant | 2.70 - 10.0 | 2.70 - 10.0 | Average value: 3.84 Grade Count:52 |
| Dielectric Strength | 9.84 - 120 kV/mm | 250 - 3050 kV/in | Average value: 34.5 kV/mm Grade Count:80 |
| Dissipation Factor | 0.00670 - 0.200 | 0.00670 - 0.200 | Average value: 0.0358 Grade Count:19 |
| Dielectric Loss Index | 0.0130 - 0.130 | 0.0130 - 0.130 | Average value: 0.0469 Grade Count:9 |
| Arc Resistance | 95.0 - 125 sec | 95.0 - 125 sec | Average value: 120 sec Grade Count:6 |
| Comparative Tracking Index | 550 - 600 V | 550 - 600 V | Average value: 593 V Grade Count:37 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 27.0 - 140 μm/m-°C | 15.0 - 78.0 μin/in-°F | Average value: 73.4 μm/m-°C Grade Count:61 |
| CTE, linear, Transverse to Flow | 110 - 120 μm/m-°C | 61.1 - 66.7 μin/in-°F | Average value: 118 μm/m-°C Grade Count:5 |
| Thermal Conductivity | 0.230 - 0.280 W/m-K | 1.60 - 1.94 BTU-in/hr-ft2-°F | Average value: 0.251 W/m-K Grade Count:5 |
| Melting Point | 249 - 275 °C | 480 - 527 °F | Average value: 258 °C Grade Count:134 |
| Maximum Service Temperature, Air | 65.0 - 200 °C | 149 - 392 °F | Average value: 120 °C Grade Count:22 |
| Deflection Temperature at 0.46 MPa (66 psi) | 80.0 - 259 °C | 176 - 498 °F | Average value: 202 °C Grade Count:137 |
| Deflection Temperature at 1.8 MPa (264 psi) | 43.0 - 252 °C | 109 - 485 °F | Average value: 84.2 °C Grade Count:215 |
| Vicat Softening Point | 154 - 252 °C | 309 - 486 °F | Average value: 207 °C Grade Count:29 |
| UL RTI, Electrical | 65.0 - 130 °C | 149 - 266 °F | Average value: 97.8 °C Grade Count:6 |
| UL RTI, Mechanical with Impact | 65.0 - 120 °C | 149 - 248 °F | Average value: 85.6 °C Grade Count:6 |
| UL RTI, Mechanical without Impact | 65.0 - 120 °C | 149 - 248 °F | Average value: 87.8 °C Grade Count:6 |
| Flammability, UL94 | HB - 5VB | HB - 5VB | Grade Count:117 |
| Oxygen Index | 20.0 - 24.5 % | 20.0 - 24.5 % | Average value: 21.4 % Grade Count:6 |
| Glow Wire Test | 550 - 650 °C | 1020 - 1200 °F | Average value: 629 °C Grade Count:11 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 260 - 310 °C | 500 - 590 °F | Average value: 284 °C Grade Count:18 |
| Feed Temperature | 60.0 - 90.0 °C | 140 - 194 °F | Average value: 72.0 °C Grade Count:5 |
| Nozzle Temperature | 250 - 304 °C | 482 - 580 °F | Average value: 278 °C Grade Count:22 |
| Melt Temperature | 220 - 310 °C | 428 - 590 °F | Average value: 278 °C Grade Count:85 |
| Mold Temperature | 26.7 - 107 °C | 80.0 - 225 °F | Average value: 75.7 °C Grade Count:91 |
| Drying Temperature | 60.0 - 130 °C | 140 - 266 °F | Average value: 80.1 °C Grade Count:66 |
| Dry Time | 1.00 - 6.00 hour | 1.00 - 6.00 hour | Average value: 3.43 hour Grade Count:59 |
| 2.00 - 6.00 hour @Temperature 71.1 - 80.0 °C | 2.00 - 6.00 hour @Temperature 160 - 176 °F | Average value: 3.11 hour Grade Count:9 | |
| Moisture Content | 0.0300 - 2.00 % | 0.0300 - 2.00 % | Average value: 0.209 % Grade Count:43 |
| Dew Point | -17.8 °C | 0.000 °F | Average value: -17.8 °C Grade Count:4 |
| Injection Pressure | 4.96 - 138 MPa | 720 - 20000 psi | Average value: 58.0 MPa Grade Count:45 |
| Hold Pressure | 50.0 - 100 MPa | 7250 - 14500 psi | Average value: 75.0 MPa Grade Count:4 |
| Back Pressure | 0.000 - 58.8 MPa | 0.000 - 8530 psi | Average value: 2.94 MPa Grade Count:39 |
| Shot Size | 30.0 - 80.0 % | 30.0 - 80.0 % | Average value: 55.0 % Grade Count:11 |
| Screw Speed | 20.0 - 120 rpm | 20.0 - 120 rpm | Average value: 66.9 rpm Grade Count:37 |