- 熔體流動速率 [g/10min]: 1.0
- 密度 [g/cm3]: 1.17
- 吸水率 [%]: 0.2
- 缺口沖擊強度: 0.27
- 拉伸強度 [MPa]: 40.0
- 斷裂伸長率 [%]: 11.5
- 彎曲強度 [MPa]: 25.9
- 彎曲模量 [MPa]: 2.50
- 硬度: 111.0
- 熱變形溫度 [℃]: 177.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.17 - 1.60 g/cc | 0.0423 - 0.0578 lb/in3 | Average value: 1.28 g/cc Grade Count:222 |
| Filler Content | 14.0 - 40.0 % | 14.0 - 40.0 % | Average value: 18.1 % Grade Count:49 |
| Water Absorption | 0.200 - 8.00 % | 0.200 - 8.00 % | Average value: 2.56 % Grade Count:115 |
| Moisture Absorption at Equilibrium | 0.170 - 7.00 % | 0.170 - 7.00 % | Average value: 2.18 % Grade Count:44 |
| Water Absorption at Saturation | 0.00900 - 8.00 % | 0.00900 - 8.00 % | Average value: 6.47 % Grade Count:17 |
| Additive Loading | 20.0 % | 20.0 % | Average value: 20.0 % Grade Count:3 |
| Viscosity | 200 - 2000 cP @Temperature 275 - 275 °C | 200 - 2000 cP @Temperature 527 - 527 °F | Average value: 1070 cP Grade Count:1 |
| 200 - 2000 cP @Shear Rate 10.0 - 1000 1/s | 200 - 2000 cP @Shear Rate 10.0 - 1000 1/s | Average value: 1070 cP Grade Count:1 | |
| Viscosity Measurement | 0.190 - 150 | 0.190 - 150 | Average value: 81.9 Grade Count:25 |
| Viscosity Test | 140 - 150 cm3/g | 140 - 150 cm3/g | Average value: 147 cm3/g Grade Count:13 |
| Linear Mold Shrinkage | 0.000 - 0.0220 cm/cm | 0.000 - 0.0220 in/in | Average value: 0.00635 cm/cm Grade Count:179 |
| Linear Mold Shrinkage, 6.35 mm section | 0.00600 - 0.00800 cm/cm | 0.00600 - 0.00800 in/in | Average value: 0.00667 cm/cm Grade Count:6 |
| Linear Mold Shrinkage, Transverse | 0.000 - 0.0137 cm/cm | 0.000 - 0.0137 in/in | Average value: 0.00919 cm/cm Grade Count:54 |
| Melt Flow | 1.00 - 157 g/10 min | 1.00 - 157 g/10 min | Average value: 57.6 g/10 min Grade Count:38 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 71.0 - 102 | 71.0 - 102 | Average value: 89.6 Grade Count:12 |
| Hardness, Rockwell R | 111 - 122 | 111 - 122 | Average value: 118 Grade Count:61 |
| Hardness, Shore D | 73.0 - 85.0 | 73.0 - 85.0 | Average value: 80.0 Grade Count:6 |
| Ball Indentation Hardness | 90.0 - 190 MPa | 13100 - 27600 psi | Average value: 150 MPa Grade Count:9 |
| Tensile Strength, Ultimate | 25.9 - 175 MPa | 3760 - 25400 psi | Average value: 112 MPa Grade Count:158 |
| 37.0 - 160 MPa @Temperature -40.0 - 120 °C | 5370 - 23200 psi @Temperature -40.0 - 248 °F | Average value: 65.6 MPa Grade Count:6 | |
| 40.0 - 80.0 MPa @Temperature 130 - 175 °C | 5800 - 11600 psi @Temperature 266 - 347 °F | Average value: 65.6 MPa Grade Count:4 | |
| 40.0 - 80.0 MPa @Time 1.80e+7 - 7.20e+7 sec | 5800 - 11600 psi @Time 5000 - 20000 hour | Average value: 65.6 MPa Grade Count:4 | |
| 5.00 - 163 MPa @Strain 0.270 - 12.0 % | 725 - 23600 psi @Strain 0.270 - 12.0 % | Average value: 65.6 MPa Grade Count:2 | |
| 5.00 - 163 MPa @Temperature -40.0 - 230 °C | 725 - 23600 psi @Temperature -40.0 - 446 °F | Average value: 65.6 MPa Grade Count:2 | |
| Tensile Strength, Yield | 40.0 - 162 MPa | 5800 - 23500 psi | Average value: 111 MPa Grade Count:72 |
| 74.0 - 74.0 MPa @Temperature 80.0 - 80.0 °C | 10700 - 10700 psi @Temperature 176 - 176 °F | Average value: 74.0 MPa Grade Count:1 | |
| Elongation at Break | 1.00 - 21.0 % | 1.00 - 21.0 % | Average value: 4.27 % Grade Count:183 |
| 2.60 - 2.60 % @Temperature -40.0 - 80.0 °C | 2.60 - 2.60 % @Temperature -40.0 - 176 °F | Average value: 2.60 % Grade Count:2 | |
| Elongation at Yield | 2.00 - 13.0 % | 2.00 - 13.0 % | Average value: 4.89 % Grade Count:31 |
| 7.40 - 7.40 % @Temperature 80.0 - 80.0 °C | 7.40 - 7.40 % @Temperature 176 - 176 °F | Average value: 7.40 % Grade Count:1 | |
| Modulus of Elasticity | 2.90 - 10.9 GPa | 421 - 1580 ksi | Average value: 6.04 GPa Grade Count:126 |
| 4.97 - 4.97 GPa @Temperature 80.0 - 80.0 °C | 721 - 721 ksi @Temperature 176 - 176 °F | Average value: 4.97 GPa Grade Count:1 | |
| Flexural Yield Strength | 11.5 - 1680 MPa | 1670 - 244000 psi | Average value: 179 MPa Grade Count:174 |
| 75.0 - 200 MPa @Temperature -40.0 - 90.0 °C | 10900 - 29000 psi @Temperature -40.0 - 194 °F | Average value: 136 MPa Grade Count:3 | |
| Flexural Modulus | 2.50 - 12.4 GPa | 363 - 1800 ksi | Average value: 5.51 GPa Grade Count:193 |
| 2.10 - 6.20 GPa @Temperature -40.0 - 120 °C | 305 - 899 ksi @Temperature -40.0 - 248 °F | Average value: 3.45 GPa Grade Count:7 | |
| Compressive Yield Strength | 103 - 207 MPa | 15000 - 30000 psi | Average value: 157 MPa Grade Count:13 |
| Shear Modulus | 0.333 - 1.745 GPa @Temperature -50.0 - 250 °C | 48.3 - 253.1 ksi @Temperature -58.0 - 482 °F | Average value: 0.907 GPa Grade Count:1 |
| Izod Impact, Notched | 0.270 - 2.16 J/cm | 0.506 - 4.04 ft-lb/in | Average value: 0.774 J/cm Grade Count:116 |
| 0.500 - 0.950 J/cm @Temperature -40.0 - -20.0 °C | 0.937 - 1.78 ft-lb/in @Temperature -40.0 - -4.00 °F | Average value: 0.796 J/cm Grade Count:5 | |
| 1.0678 - 1.0678 J/cm @Temperature -40.0 - -40.0 °C | 2.0004 - 2.0004 ft-lb/in @Temperature -40.0 - -40.0 °F | Average value: 0.796 J/cm Grade Count:2 | |
| 1.0678 - 1.0678 J/cm @Thickness 3.17 - 3.17 mm | 2.0004 - 2.0004 ft-lb/in @Thickness 0.125 - 0.125 in | Average value: 0.796 J/cm Grade Count:2 | |
| Izod Impact, Unnotched | 3.20 - 60.0 J/cm | 6.00 - 112 ft-lb/in | Average value: 8.85 J/cm Grade Count:34 |
| Izod Impact, Notched (ISO) | 3.50 - 19.0 kJ/m2 | 1.67 - 9.04 ft-lb/in2 | Average value: 8.34 kJ/m2 Grade Count:47 |
| 3.00 - 21.0 kJ/m2 @Temperature -40.0 - -30.0 °C | 1.43 - 9.99 ft-lb/in2 @Temperature -40.0 - -22.0 °F | Average value: 8.15 kJ/m2 Grade Count:15 | |
| Izod Impact, Unnotched (ISO) | 30.0 - 90.0 kJ/m2 | 14.3 - 42.8 ft-lb/in2 | Average value: 56.0 kJ/m2 Grade Count:10 |
| 30.0 - 75.0 kJ/m2 @Temperature -40.0 - -30.0 °C | 14.3 - 35.7 ft-lb/in2 @Temperature -40.0 - -22.0 °F | Average value: 43.6 kJ/m2 Grade Count:9 | |
| Charpy Impact Unnotched | 1.80 J/cm2 - NB | 8.57 ft-lb/in2 - NB | Average value: 5.41 J/cm2 Grade Count:90 |
| 2.00 - 8.00 J/cm2 @Temperature -40.0 - -20.0 °C | 9.52 - 38.1 ft-lb/in2 @Temperature -40.0 - -4.00 °F | Average value: 4.16 J/cm2 Grade Count:52 | |
| Charpy Impact, Notched | 0.300 - 2.40 J/cm2 | 1.43 - 11.4 ft-lb/in2 | Average value: 0.919 J/cm2 Grade Count:88 |
| 0.250 - 10.0 J/cm2 @Temperature -40.0 - 30.0 °C | 1.19 - 47.6 ft-lb/in2 @Temperature -40.0 - 86.0 °F | Average value: 0.938 J/cm2 Grade Count:50 | |
| Puncture Energy | 1.70 - 2.30 J | 1.25 - 1.70 ft-lb | Average value: 1.97 J Grade Count:3 |
| 0.700 - 1.50 J @Temperature -30.0 - -30.0 °C | 0.516 - 1.11 ft-lb @Temperature -22.0 - -22.0 °F | Average value: 1.23 J Grade Count:2 | |
| 1.50 - 1.50 J @Temperature -30.0 - -30.0 °C | 1.11 - 1.11 ft-lb @Temperature -22.0 - -22.0 °F | Average value: 1.23 J Grade Count:1 | |
| 1.50 - 1.50 J @Load <=58.9 kg | 1.11 - 1.11 ft-lb @Load <=130 lb | Average value: 1.23 J Grade Count:1 | |
| Tensile Creep Modulus, 1 hour | 3700 - 4900 MPa | 537000 - 711000 psi | Average value: 4550 MPa Grade Count:4 |
| Tensile Creep Modulus, 1000 hours | 1500 - 3510 MPa | 218000 - 509000 psi | Average value: 2620 MPa Grade Count:7 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 0.100 - 1.00e+17 ohm-cm | 0.100 - 1.00e+17 ohm-cm | Average value: 2.98e+15 ohm-cm Grade Count:116 |
| Surface Resistance | 0.0100 - 7.20e+15 ohm | 0.0100 - 7.20e+15 ohm | Average value: 1.59e+14 ohm Grade Count:69 |
| Static Decay | 2.00 sec | 2.00 sec | Average value: 2.00 sec Grade Count:5 |
| Dielectric Constant | 2.60 - 11.0 | 2.60 - 11.0 | Average value: 4.31 Grade Count:50 |
| Dielectric Strength | 17.3 - 90.0 kV/mm | 440 - 2290 kV/in | Average value: 33.7 kV/mm Grade Count:78 |
| Dissipation Factor | 0.00140 - 0.300 | 0.00140 - 0.300 | Average value: 0.0644 Grade Count:47 |
| Dielectric Loss Index | 0.0150 - 0.150 | 0.0150 - 0.150 | Average value: 0.0825 Grade Count:4 |
| Arc Resistance | 0.000 - 135 sec | 0.000 - 135 sec | Average value: 107 sec Grade Count:8 |
| Comparative Tracking Index | 225 - 600 V | 225 - 600 V | Average value: 508 V Grade Count:75 |
| Hot Wire Ignition, HWI | 2.00 - 30.0 sec | 2.00 - 30.0 sec | Average value: 8.83 sec Grade Count:7 |
| High Amp Arc Ignition, HAI | 0.000 - 120 arcs | 0.000 - 120 arcs | Average value: 40.0 arcs Grade Count:7 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 0.300 - 500 μm/m-°C | 0.167 - 278 μin/in-°F | Average value: 54.2 μm/m-°C Grade Count:66 |
| CTE, linear, Transverse to Flow | 0.700 - 111 μm/m-°C | 0.389 - 61.7 μin/in-°F | Average value: 77.5 μm/m-°C Grade Count:17 |
| Specific Heat Capacity | 1.30 - 1.80 J/g-°C | 0.311 - 0.430 BTU/lb-°F | Average value: 1.55 J/g-°C Grade Count:4 |
| Thermal Conductivity | 0.330 - 0.432 W/m-K | 2.29 - 3.00 BTU-in/hr-ft2-°F | Average value: 0.388 W/m-K Grade Count:12 |
| Melting Point | 218 - 265 °C | 424 - 509 °F | Average value: 255 °C Grade Count:108 |
| Maximum Service Temperature, Air | 65.0 - 240 °C | 149 - 464 °F | Average value: 158 °C Grade Count:24 |
| Deflection Temperature at 0.46 MPa (66 psi) | 177 - 265 °C | 350 - 509 °F | Average value: 246 °C Grade Count:113 |
| Deflection Temperature at 1.8 MPa (264 psi) | 121 - 260 °C | 250 - 500 °F | Average value: 234 °C Grade Count:186 |
| Deflection Temperature at 8.0 MPa | 70.0 - 238 °C | 158 - 460 °F | Average value: 104 °C Grade Count:5 |
| Vicat Softening Point | 160 - 255 °C | 320 - 491 °F | Average value: 236 °C Grade Count:52 |
| Decomposition Temperature | 300 - 310 °C | 572 - 590 °F | Average value: 303 °C Grade Count:7 |
| UL RTI, Electrical | 65.0 - 140 °C | 149 - 284 °F | Average value: 128 °C Grade Count:10 |
| UL RTI, Mechanical with Impact | 65.0 - 125 °C | 149 - 257 °F | Average value: 110 °C Grade Count:4 |
| UL RTI, Mechanical without Impact | 65.0 - 140 °C | 149 - 284 °F | Average value: 119 °C Grade Count:4 |
| Flammability, UL94 | HB - V-0 | HB - V-0 | Grade Count:133 |
| Oxygen Index | 22.0 - 34.0 % | 22.0 - 34.0 % | Average value: 27.2 % Grade Count:25 |
| Glow Wire Test | 649 - 960 °C | 1200 - 1760 °F | Average value: 757 °C Grade Count:46 |
| Shrinkage | 0.100 - 0.200 % @Temperature 120 - 120 °C | 0.100 - 0.200 % @Temperature 248 - 248 °F | Average value: 0.150 % Grade Count:1 |
| 0.100 - 0.200 % @Time 14400 - 14400 sec | 0.100 - 0.200 % @Time 4.00 - 4.00 hour | Average value: 0.150 % Grade Count:1 | |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 70.0 - 310 °C | 158 - 590 °F | Average value: 218 °C Grade Count:17 |
| Feed Temperature | 20.0 - 270 °C | 68.0 - 518 °F | Average value: 184 °C Grade Count:15 |
| Nozzle Temperature | 250 - 295 °C | 482 - 563 °F | Average value: 278 °C Grade Count:13 |
| Die Temperature | 250 - 315 °C | 482 - 599 °F | Average value: 279 °C Grade Count:3 |
| Melt Temperature | 179 - 320 °C | 354 - 608 °F | Average value: 279 °C Grade Count:114 |
| Mold Temperature | 40.0 - 121 °C | 104 - 250 °F | Average value: 84.3 °C Grade Count:117 |
| Drying Temperature | 70.0 - 130 °C | 158 - 266 °F | Average value: 83.4 °C Grade Count:88 |
| Dry Time | 2.00 - 12.0 hour | 2.00 - 12.0 hour | Average value: 4.04 hour Grade Count:62 |
| 2.00 - 4.00 hour @Temperature 71.1 - 79.4 °C | 2.00 - 4.00 hour @Temperature 160 - 175 °F | Average value: 3.00 hour Grade Count:4 | |
| Moisture Content | 0.0300 - 2.10 % | 0.0300 - 2.10 % | Average value: 0.186 % Grade Count:73 |
| Dew Point | -17.8 °C | 0.000 °F | Average value: -17.8 °C Grade Count:20 |
| Injection Pressure | 4.96 - 150 MPa | 720 - 21800 psi | Average value: 84.5 MPa Grade Count:55 |
| Hold Pressure | 50.0 - 100 MPa | 7250 - 14500 psi | Average value: 73.0 MPa Grade Count:5 |
| Back Pressure | 0.000 - 58.8 MPa | 0.000 - 8530 psi | Average value: 12.7 MPa Grade Count:11 |
| Shot Size | 30.0 - 80.0 % | 30.0 - 80.0 % | Average value: 55.0 % Grade Count:4 |
| Screw Speed | 20.0 - 100 rpm | 20.0 - 100 rpm | Average value: 50.0 rpm Grade Count:8 |