- 密度 [g/cm3]: 1.14
- 吸水率 [%]: 0.4
- 缺口沖擊強度: 0.534
- 拉伸強度 [MPa]: 152.0
- 斷裂伸長率 [%]: 72.4
- 彎曲強度 [MPa]: 45.5
- 彎曲模量 [MPa]: 2.07
- 硬度: 112.0
- 熱變形溫度 [℃]: 191.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.14 - 1.50 g/cc | 0.0412 - 0.0542 lb/in3 | Average value: 1.25 g/cc Grade Count:32 |
| Filler Content | 15.0 - 20.0 % | 15.0 - 20.0 % | Average value: 18.0 % Grade Count:10 |
| Water Absorption | 0.400 - 2.50 % | 0.400 - 2.50 % | Average value: 0.850 % Grade Count:18 |
| Moisture Absorption at Equilibrium | 0.400 - 2.50 % | 0.400 - 2.50 % | Average value: 1.86 % Grade Count:5 |
| Water Absorption at Saturation | 6.00 - 8.00 % | 6.00 - 8.00 % | Average value: 6.83 % Grade Count:3 |
| Additive Loading | 15.0 - 20.0 % | 15.0 - 20.0 % | Average value: 18.3 % Grade Count:3 |
| Linear Mold Shrinkage | 0.000500 - 0.0220 cm/cm | 0.000500 - 0.0220 in/in | Average value: 0.00407 cm/cm Grade Count:30 |
| Linear Mold Shrinkage, 6.35 mm section | 0.00250 - 0.0280 cm/cm | 0.00250 - 0.0280 in/in | Average value: 0.00646 cm/cm Grade Count:7 |
| Linear Mold Shrinkage, Transverse | 0.00190 - 0.0110 cm/cm | 0.00190 - 0.0110 in/in | Average value: 0.00638 cm/cm Grade Count:5 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 112 - 125 | 112 - 125 | Average value: 118 Grade Count:13 |
| Ball Indentation Hardness | 160 - 270 MPa | 23200 - 39200 psi | Average value: 223 MPa Grade Count:3 |
| Tensile Strength, Ultimate | 45.5 - 230 MPa | 6600 - 33400 psi | Average value: 176 MPa Grade Count:26 |
| Tensile Strength, Yield | 152 - 230 MPa | 22000 - 33400 psi | Average value: 183 MPa Grade Count:6 |
| Elongation at Break | 1.00 - 10.0 % | 1.00 - 10.0 % | Average value: 3.10 % Grade Count:31 |
| Modulus of Elasticity | 2.21 - 18.6 GPa | 320 - 2700 ksi | Average value: 13.4 GPa Grade Count:24 |
| Flexural Yield Strength | 72.4 - 330 MPa | 10500 - 47900 psi | Average value: 256 MPa Grade Count:25 |
| Flexural Modulus | 2.07 - 16.2 GPa | 300 - 2350 ksi | Average value: 12.0 GPa Grade Count:28 |
| Compressive Yield Strength | 40.0 - 172 MPa | 5800 - 25000 psi | Average value: 119 MPa Grade Count:4 |
| Izod Impact, Notched | 0.534 - 1.92 J/cm | 1.00 - 3.60 ft-lb/in | Average value: 0.902 J/cm Grade Count:24 |
| Izod Impact, Unnotched | 5.34 - 14.9 J/cm | 10.0 - 28.0 ft-lb/in | Average value: 7.34 J/cm Grade Count:15 |
| Charpy Impact Unnotched | 2.60 - 7.20 J/cm2 | 12.4 - 34.3 ft-lb/in2 | Average value: 4.32 J/cm2 Grade Count:7 |
| 2.50 - 4.10 J/cm2 @Temperature -40.0 - -20.0 °C | 11.9 - 19.5 ft-lb/in2 @Temperature -40.0 - -4.00 °F | Average value: 3.03 J/cm2 Grade Count:3 | |
| Charpy Impact, Notched | 0.600 - 1.60 J/cm2 | 2.86 - 7.61 ft-lb/in2 | Average value: 0.906 J/cm2 Grade Count:7 |
| 0.400 - 0.500 J/cm2 @Temperature -40.0 - -20.0 °C | 1.90 - 2.38 ft-lb/in2 @Temperature -40.0 - -4.00 °F | Average value: 0.450 J/cm2 Grade Count:2 | |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 10.0 - 1.00e+16 ohm-cm | 10.0 - 1.00e+16 ohm-cm | Average value: 4.17e+14 ohm-cm Grade Count:24 |
| Surface Resistance | 20.0 - 1.00e+7 ohm | 20.0 - 1.00e+7 ohm | Average value: 1.14e+6 ohm Grade Count:11 |
| Dielectric Constant | 3.60 - 3.70 | 3.60 - 3.70 | Average value: 3.63 Grade Count:3 |
| Dielectric Strength | 2.50 - 20.0 kV/mm | 63.5 - 508 kV/in | Average value: 15.5 kV/mm Grade Count:4 |
| Dissipation Factor | 0.0160 - 0.0200 | 0.0160 - 0.0200 | Average value: 0.0187 Grade Count:3 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 18.0 - 72.0 μm/m-°C | 10.0 - 40.0 μin/in-°F | Average value: 39.5 μm/m-°C Grade Count:14 |
| Thermal Conductivity | 0.430 - 0.692 W/m-K | 2.98 - 4.80 BTU-in/hr-ft2-°F | Average value: 0.537 W/m-K Grade Count:3 |
| Melting Point | 221 - 262 °C | 430 - 504 °F | Average value: 253 °C Grade Count:9 |
| Maximum Service Temperature, Air | 115 - 240 °C | 239 - 464 °F | Average value: 163 °C Grade Count:3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 191 - 260 °C | 375 - 500 °F | Average value: 248 °C Grade Count:14 |
| Deflection Temperature at 1.8 MPa (264 psi) | 64.4 - 259 °C | 148 - 498 °F | Average value: 241 °C Grade Count:27 |
| Vicat Softening Point | 230 - 254 °C | 446 - 489 °F | Average value: 245 °C Grade Count:3 |
| Flammability, UL94 | HB - V-0 | HB - V-0 | Grade Count:24 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 270 - 300 °C | 518 - 572 °F | Average value: 284 °C Grade Count:8 |
| Melt Temperature | 260 - 300 °C | 500 - 572 °F | Average value: 286 °C Grade Count:12 |
| Mold Temperature | 60.0 - 110 °C | 140 - 230 °F | Average value: 85.8 °C Grade Count:20 |
| Drying Temperature | 79.4 - 100 °C | 175 - 212 °F | Average value: 80.7 °C Grade Count:11 |
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | Average value: 3.71 hour Grade Count:7 |
| Moisture Content | 0.150 - 0.200 % | 0.150 - 0.200 % | Average value: 0.194 % Grade Count:9 |
| Dew Point | -17.8 °C | 0.000 °F | Average value: -17.8 °C Grade Count:7 |
| Injection Pressure | 68.9 - 124 MPa | 10000 - 18000 psi | Average value: 102 MPa Grade Count:15 |