- 熔體流動(dòng)速率 [g/10min]: 1.0
- 密度 [g/cm3]: 1.07
- 吸水率 [%]: 0.3
- 缺口沖擊強(qiáng)度: 0.3
- 拉伸強(qiáng)度 [MPa]: 10.3
- 斷裂伸長(zhǎng)率 [%]: 27.6
- 彎曲強(qiáng)度 [MPa]: 34.5
- 彎曲模量 [MPa]: 0.255
- 硬度: 82.0
- 熱變形溫度 [℃]: 100.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.07 - 1.85 g/cc | 0.0387 - 0.0668 lb/in3 | Average value: 1.32 g/cc Grade Count:313 |
| Water Absorption | 0.300 - 8.50 % | 0.300 - 8.50 % | Average value: 1.08 % Grade Count:231 |
| Moisture Absorption at Equilibrium | 0.250 - 2.80 % | 0.250 - 2.80 % | Average value: 1.95 % Grade Count:28 |
| Water Absorption at Saturation | 5.10 - 8.50 % | 5.10 - 8.50 % | Average value: 7.85 % Grade Count:6 |
| Viscosity Measurement | 0.400 - 240 | 0.400 - 240 | Average value: 51.1 Grade Count:8 |
| Linear Mold Shrinkage | 0.00100 - 0.0335 cm/cm | 0.00100 - 0.0335 in/in | Average value: 0.00819 cm/cm Grade Count:297 |
| Linear Mold Shrinkage, Transverse | 0.00480 - 0.0240 cm/cm | 0.00480 - 0.0240 in/in | Average value: 0.0107 cm/cm Grade Count:44 |
| Melt Flow | 1.00 - 5.00 g/10 min | 1.00 - 5.00 g/10 min | Average value: 2.83 g/10 min Grade Count:15 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 55.0 - 119 | 55.0 - 119 | Average value: 79.4 Grade Count:31 |
| Hardness, Rockwell R | 82.0 - 122 | 82.0 - 122 | Average value: 114 Grade Count:190 |
| Tensile Strength, Ultimate | 34.5 - 300 MPa | 5000 - 43500 psi | Average value: 104 MPa Grade Count:107 |
| 30.0 - 55.0 MPa @Temperature 60.0 - 120 °C | 4350 - 7980 psi @Temperature 140 - 248 °F | Average value: 38.8 MPa Grade Count:2 | |
| Tensile Strength, Yield | 10.3 - 252 MPa | 1500 - 36500 psi | Average value: 123 MPa Grade Count:215 |
| 144.79 - 144.79 MPa @Temperature 93.3 - 93.3 °C | 21000 - 21000 psi @Temperature 200 - 200 °F | Average value: 145 MPa Grade Count:1 | |
| Elongation at Break | 1.00 - 300 % | 1.00 - 300 % | Average value: 23.2 % Grade Count:276 |
| Elongation at Yield | 3.00 - 90.0 % | 3.00 - 90.0 % | Average value: 19.5 % Grade Count:32 |
| Modulus of Elasticity | 1.30 - 28.0 GPa | 189 - 4060 ksi | Average value: 7.95 GPa Grade Count:49 |
| Flexural Yield Strength | 27.6 - 420 MPa | 4000 - 60900 psi | Average value: 167 MPa Grade Count:285 |
| 35.0 - 35.0 MPa @Temperature 90.0 - 90.0 °C | 5080 - 5080 psi @Temperature 194 - 194 °F | Average value: 35.0 MPa Grade Count:1 | |
| Flexural Modulus | 0.255 - 36.2 GPa | 37.0 - 5250 ksi | Average value: 6.39 GPa Grade Count:290 |
| 0.700 - 15.1685 GPa @Temperature 60.0 - 120 °C | 102 - 2200.03 ksi @Temperature 140 - 248 °F | Average value: 3.70 GPa Grade Count:4 | |
| Compressive Yield Strength | 30.3 - 110 MPa | 4400 - 16000 psi | Average value: 57.0 MPa Grade Count:3 |
| Poissons Ratio | 0.350 | 0.350 | Average value: 0.350 Grade Count:3 |
| Shear Strength | 50.0 - 76.5 MPa | 7250 - 11100 psi | Average value: 61.7 MPa Grade Count:5 |
| Izod Impact, Notched | 0.300 - 10.1 J/cm | 0.562 - 19.0 ft-lb/in | Average value: 1.55 J/cm Grade Count:266 |
| 0.200 - 0.280 J/cm @Temperature -40.0 - -20.0 °C | 0.375 - 0.525 ft-lb/in @Temperature -40.0 - -4.00 °F | Average value: 1.20 J/cm Grade Count:2 | |
| 0.5339 - 2.6695 J/cm @Temperature -40.0 - -40.0 °C | 1.000 - 5.0011 ft-lb/in @Temperature -40.0 - -40.0 °F | Average value: 1.20 J/cm Grade Count:16 | |
| 0.5339 - 2.6695 J/cm @Thickness 3.17 - 3.17 mm | 1.000 - 5.0011 ft-lb/in @Thickness 0.125 - 0.125 in | Average value: 1.20 J/cm Grade Count:16 | |
| Izod Impact, Unnotched | 3.20 - 5340 J/cm | 6.00 - 10000 ft-lb/in | Average value: 9.28 J/cm Grade Count:76 |
| Izod Impact, Notched (ISO) | 3.50 - 861 kJ/m2 | 1.67 - 410 ft-lb/in2 | Average value: 40.2 kJ/m2 Grade Count:29 |
| 3.50 - 17.0 kJ/m2 @Temperature -40.0 - -30.0 °C | 1.67 - 8.09 ft-lb/in2 @Temperature -40.0 - -22.0 °F | Average value: 9.13 kJ/m2 Grade Count:22 | |
| Izod Impact, Unnotched (ISO) | 30.0 - 100 kJ/m2 | 14.3 - 47.6 ft-lb/in2 | Average value: 68.2 kJ/m2 Grade Count:13 |
| 25.0 - 90.0 kJ/m2 @Temperature -30.0 - -30.0 °C | 11.9 - 42.8 ft-lb/in2 @Temperature -22.0 - -22.0 °F | Average value: 62.5 kJ/m2 Grade Count:12 | |
| Charpy Impact Unnotched | 1.30 J/cm2 - NB | 6.19 ft-lb/in2 - NB | Average value: 8.00 J/cm2 Grade Count:25 |
| 0.800 J/cm2 - NB @Temperature -40.0 - -20.0 °C | 3.81 ft-lb/in2 - NB @Temperature -40.0 - -4.00 °F | Average value: 5.82 J/cm2 Grade Count:20 | |
| Charpy Impact, Notched | 0.350 - 2.00 J/cm2 | 1.67 - 9.52 ft-lb/in2 | Average value: 1.04 J/cm2 Grade Count:19 |
| 0.200 - 1.40 J/cm2 @Temperature -40.0 - -20.0 °C | 0.952 - 6.66 ft-lb/in2 @Temperature -40.0 - -4.00 °F | Average value: 0.889 J/cm2 Grade Count:18 | |
| Puncture Energy | 2.00 - 2.00 J @Temperature -30.0 - -30.0 °C | 1.48 - 1.48 ft-lb @Temperature -22.0 - -22.0 °F | Average value: 2.00 J Grade Count:1 |
| Coefficient of Friction | 0.100 - 0.280 | 0.100 - 0.280 | Average value: 0.225 Grade Count:11 |
| Coefficient of Friction, Static | 0.0900 - 0.220 | 0.0900 - 0.220 | Average value: 0.170 Grade Count:11 |
| K (wear) Factor | 16.1 - 38.3 x 10-8 mm3/N-M | 8.00 - 19.0 x 10-10 in3-min/ft-lb-hr | Average value: 31.3 x 10-8 mm3/N-M Grade Count:11 |
| Limiting Pressure Velocity | 0.596 - 1.54 MPa-m/sec | 17000 - 44000 psi-ft/min | Average value: 0.690 MPa-m/sec Grade Count:8 |
| Taber Abrasion, mg/1000 Cycles | 5.00 - 7.00 | 5.00 - 7.00 | Average value: 6.00 Grade Count:4 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00 - 1.00e+17 ohm-cm | 1.00 - 1.00e+17 ohm-cm | Average value: 2.87e+15 ohm-cm Grade Count:220 |
| Surface Resistance | 1.00 - 1.00e+16 ohm | 1.00 - 1.00e+16 ohm | Average value: 3.04e+14 ohm Grade Count:90 |
| Dielectric Constant | 3.20 - 13.0 | 3.20 - 13.0 | Average value: 4.42 Grade Count:22 |
| Dielectric Strength | 15.7 - 120 kV/mm | 400 - 3050 kV/in | Average value: 23.5 kV/mm Grade Count:194 |
| Dissipation Factor | 0.0100 - 0.320 | 0.0100 - 0.320 | Average value: 0.0686 Grade Count:5 |
| Arc Resistance | 95.0 - 185 sec | 95.0 - 185 sec | Average value: 127 sec Grade Count:6 |
| Comparative Tracking Index | 225 - 600 V | 225 - 600 V | Average value: 445 V Grade Count:41 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 7.20 - 146 μm/m-°C | 4.00 - 81.0 μin/in-°F | Average value: 46.2 μm/m-°C Grade Count:196 |
| Specific Heat Capacity | 1.67 J/g-°C | 0.399 BTU/lb-°F | Average value: 1.67 J/g-°C Grade Count:4 |
| Thermal Conductivity | 0.200 - 0.260 W/m-K | 1.39 - 1.80 BTU-in/hr-ft2-°F | Average value: 0.224 W/m-K Grade Count:8 |
| Melting Point | 232 - 263 °C | 450 - 505 °F | Average value: 259 °C Grade Count:86 |
| Maximum Service Temperature, Air | 80.0 - 210 °C | 176 - 410 °F | Average value: 146 °C Grade Count:7 |
| Deflection Temperature at 0.46 MPa (66 psi) | 100 - 263 °C | 212 - 505 °F | Average value: 241 °C Grade Count:206 |
| Deflection Temperature at 1.8 MPa (264 psi) | 57.2 - 260 °C | 135 - 500 °F | Average value: 190 °C Grade Count:290 |
| Vicat Softening Point | 150 - 255 °C | 302 - 491 °F | Average value: 243 °C Grade Count:40 |
| Flammability, UL94 | HB - 5VB | HB - 5VB | Grade Count:177 |
| Flammability Test | 1.00 | 1.00 | Average value: 1.00 Grade Count:4 |
| Oxygen Index | 26.0 - 31.0 % | 26.0 - 31.0 % | Average value: 28.3 % Grade Count:7 |
| Glow Wire Test | 650 - 960 °C | 1200 - 1760 °F | Average value: 839 °C Grade Count:29 |
| Shrinkage | 0.200 - 0.400 % @Temperature 120 - 120 °C | 0.200 - 0.400 % @Temperature 248 - 248 °F | Average value: 0.300 % Grade Count:1 |
| 0.200 - 0.400 % @Time 14400 - 14400 sec | 0.200 - 0.400 % @Time 4.00 - 4.00 hour | Average value: 0.300 % Grade Count:1 | |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 260 - 300 °C | 500 - 572 °F | Average value: 283 °C Grade Count:27 |
| Feed Temperature | 60.0 - 270 °C | 140 - 518 °F | Average value: 86.3 °C Grade Count:24 |
| Nozzle Temperature | 250 - 295 °C | 482 - 563 °F | Average value: 276 °C Grade Count:7 |
| Melt Temperature | 238 - 320 °C | 460 - 608 °F | Average value: 281 °C Grade Count:77 |
| Mold Temperature | 26.7 - 110 °C | 80.0 - 230 °F | Average value: 80.6 °C Grade Count:103 |
| Drying Temperature | 71.1 - 107 °C | 160 - 225 °F | Average value: 79.1 °C Grade Count:84 |
| Dry Time | 2.00 - 6.00 hour | 2.00 - 6.00 hour | Average value: 3.25 hour Grade Count:71 |
| 2.00 - 6.00 hour @Temperature 79.4 - 80.0 °C | 2.00 - 6.00 hour @Temperature 175 - 176 °F | Average value: 3.06 hour Grade Count:16 | |
| Moisture Content | 0.0300 - 2.20 % | 0.0300 - 2.20 % | Average value: 0.210 % Grade Count:70 |
| Injection Pressure | 4.96 - 138 MPa | 720 - 20000 psi | Average value: 42.2 MPa Grade Count:39 |
| Hold Pressure | 50.0 - 100 MPa | 7250 - 14500 psi | Average value: 75.0 MPa Grade Count:21 |
| Back Pressure | 0.000 - 1.72 MPa | 0.000 - 250 psi | Average value: 0.534 MPa Grade Count:50 |
| Shot Size | 30.0 - 80.0 % | 30.0 - 80.0 % | Average value: 55.0 % Grade Count:17 |
| Screw Speed | 20.0 - 140 rpm | 20.0 - 140 rpm | Average value: 72.0 rpm Grade Count:48 |