- 密度 [g/cm3]: 1.14
- 吸水率 [%]: 0.5
- 缺口沖擊強度: 0.32
- 拉伸強度 [MPa]: 81.4
- 斷裂伸長率 [%]: 75.8
- 彎曲強度 [MPa]: 48.3
- 彎曲模量 [MPa]: 0.621
- 硬度: 100.0
- 熱變形溫度 [℃]: 232.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.14 - 1.39 g/cc | 0.0412 - 0.0502 lb/in3 | Average value: 1.22 g/cc Grade Count:47 |
| Filler Content | 5.00 - 25.0 % | 5.00 - 25.0 % | Average value: 14.5 % Grade Count:11 |
| Water Absorption | 0.500 - 1.00 % | 0.500 - 1.00 % | Average value: 0.894 % Grade Count:25 |
| Additive Loading | 10.0 % | 10.0 % | Average value: 10.0 % Grade Count:4 |
| Linear Mold Shrinkage | 0.00100 - 0.0300 cm/cm | 0.00100 - 0.0300 in/in | Average value: 0.0115 cm/cm Grade Count:45 |
| Linear Mold Shrinkage, 6.35 mm section | 0.0100 - 0.0170 cm/cm | 0.0100 - 0.0170 in/in | Average value: 0.0132 cm/cm Grade Count:9 |
| Linear Mold Shrinkage, Transverse | 0.00500 - 0.0240 cm/cm | 0.00500 - 0.0240 in/in | Average value: 0.0182 cm/cm Grade Count:6 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 100 - 120 | 100 - 120 | Average value: 113 Grade Count:8 |
| Tensile Strength, Ultimate | 48.3 - 128 MPa | 7000 - 18500 psi | Average value: 87.6 MPa Grade Count:42 |
| Tensile Strength, Yield | 81.4 - 110 MPa | 11800 - 16000 psi | Average value: 95.0 MPa Grade Count:6 |
| Elongation at Break | 1.60 - 10.0 % | 1.60 - 10.0 % | Average value: 5.62 % Grade Count:38 |
| Elongation at Yield | 3.50 - 8.40 % | 3.50 - 8.40 % | Average value: 5.77 % Grade Count:10 |
| Modulus of Elasticity | 2.41 - 11.0 GPa | 350 - 1600 ksi | Average value: 4.87 GPa Grade Count:39 |
| Flexural Yield Strength | 75.8 - 207 MPa | 11000 - 30000 psi | Average value: 130 MPa Grade Count:46 |
| Flexural Modulus | 0.621 - 8.20 GPa | 90.0 - 1190 ksi | Average value: 3.90 GPa Grade Count:46 |
| Izod Impact, Notched | 0.320 - 1.44 J/cm | 0.599 - 2.70 ft-lb/in | Average value: 0.595 J/cm Grade Count:37 |
| Izod Impact, Unnotched | 2.14 - 11.2 J/cm | 4.00 - 21.0 ft-lb/in | Average value: 5.45 J/cm Grade Count:29 |
| Izod Impact, Notched (ISO) | 4.00 - 5.80 kJ/m2 | 1.90 - 2.76 ft-lb/in2 | Average value: 4.82 kJ/m2 Grade Count:4 |
| Izod Impact, Unnotched (ISO) | 37.0 - 48.6 kJ/m2 | 17.6 - 23.1 ft-lb/in2 | Average value: 40.9 kJ/m2 Grade Count:3 |
| Charpy Impact Unnotched | 2.00 - 5.00 J/cm2 | 9.52 - 23.8 ft-lb/in2 | Average value: 3.86 J/cm2 Grade Count:9 |
| Charpy Impact, Notched | 0.400 - 1.50 J/cm2 | 1.90 - 7.14 ft-lb/in2 | Average value: 0.538 J/cm2 Grade Count:8 |
| Coefficient of Friction | 0.130 - 0.550 | 0.130 - 0.550 | Average value: 0.251 Grade Count:8 |
| Coefficient of Friction, Static | 0.110 - 0.570 | 0.110 - 0.570 | Average value: 0.276 Grade Count:10 |
| K (wear) Factor | 26.2 - 46.3 x 10-8 mm3/N-M | 13.0 - 23.0 x 10-10 in3-min/ft-lb-hr | Average value: 39.6 x 10-8 mm3/N-M Grade Count:3 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 100000 - 1.00e+17 ohm-cm | 100000 - 1.00e+17 ohm-cm | Average value: 5.60e+15 ohm-cm Grade Count:24 |
| Surface Resistance | 1.00e+13 - 1.00e+14 ohm | 1.00e+13 - 1.00e+14 ohm | Average value: 1.90e+13 ohm Grade Count:10 |
| Insulation Resistance | 1.00e+12 ohm | 1.00e+12 ohm | Average value: 1.00e+12 ohm Grade Count:9 |
| Dielectric Strength | 17.7 - 19.7 kV/mm | 450 - 500 kV/in | Average value: 18.2 kV/mm Grade Count:4 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 28.8 - 67.0 μm/m-°C | 16.0 - 37.2 μin/in-°F | Average value: 55.7 μm/m-°C Grade Count:9 |
| Melting Point | 255 - 262 °C | 491 - 504 °F | Average value: 257 °C Grade Count:5 |
| Maximum Service Temperature, Air | 90.0 - 160 °C | 194 - 320 °F | Average value: 134 °C Grade Count:10 |
| Deflection Temperature at 0.46 MPa (66 psi) | 232 - 249 °C | 450 - 480 °F | Average value: 240 °C Grade Count:15 |
| Deflection Temperature at 1.8 MPa (264 psi) | 70.0 - 246 °C | 158 - 475 °F | Average value: 174 °C Grade Count:40 |
| Vicat Softening Point | 260 °C | 500 °F | Average value: 260 °C Grade Count:6 |
| Flammability, UL94 | HB | HB | Grade Count:25 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 70.0 - 300 °C | 158 - 572 °F | Average value: 268 °C Grade Count:21 |
| Nozzle Temperature | 280 - 300 °C | 536 - 572 °F | Average value: 290 °C Grade Count:9 |
| Melt Temperature | 274 - 315 °C | 525 - 599 °F | Average value: 295 °C Grade Count:29 |
| Mold Temperature | 65.6 - 120 °C | 150 - 248 °F | Average value: 90.8 °C Grade Count:40 |
| Drying Temperature | 70.0 - 105 °C | 158 - 221 °F | Average value: 84.6 °C Grade Count:30 |
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | Average value: 3.88 hour Grade Count:17 |
| Moisture Content | 0.180 - 0.200 % | 0.180 - 0.200 % | Average value: 0.199 % Grade Count:21 |
| Dew Point | -30.0 - -17.8 °C | -22.0 - 0.000 °F | Average value: -18.6 °C Grade Count:15 |
| Injection Pressure | 68.9 - 124 MPa | 10000 - 18000 psi | Average value: 100 MPa Grade Count:24 |
| Back Pressure | 0.172 - 0.345 MPa | 24.9 - 50.0 psi | Average value: 0.259 MPa Grade Count:5 |