- 熔體流動速率 [g/10min]: 1.0
- 密度 [g/cm3]: 1.45
- 吸水率 [%]: 0.3
- 缺口沖擊強度: 1.01
- 拉伸強度 [MPa]: 130.0
- 斷裂伸長率 [%]: 216
- 彎曲強度 [MPa]: 37.4
- 彎曲模量 [MPa]: 7.90
- 硬度: 98.0
- 熱變形溫度 [℃]: 240.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.45 - 1.78 g/cc | 0.0524 - 0.0643 lb/in3 | Average value: 1.57 g/cc Grade Count:116 |
| Filler Content | 45.0 - 50.0 % | 45.0 - 50.0 % | Average value: 49.2 % Grade Count:19 |
| Water Absorption | 0.300 - 4.30 % | 0.300 - 4.30 % | Average value: 1.83 % Grade Count:68 |
| Moisture Absorption at Equilibrium | 0.170 - 2.00 % | 0.170 - 2.00 % | Average value: 1.15 % Grade Count:34 |
| Water Absorption at Saturation | 0.200 - 7.00 % | 0.200 - 7.00 % | Average value: 3.61 % Grade Count:9 |
| Viscosity | 20.0 - 450 cP @Temperature 280 - 300 °C | 20.0 - 450 cP @Temperature 536 - 572 °F | Average value: 197 cP Grade Count:1 |
| 20.0 - 450 cP @Shear Rate 10.0 - 1000 1/s | 20.0 - 450 cP @Shear Rate 10.0 - 1000 1/s | Average value: 197 cP Grade Count:1 | |
| Viscosity Measurement | 0.560 - 145 | 0.560 - 145 | Average value: 118 Grade Count:14 |
| Viscosity Test | 131 - 150 cm3/g | 131 - 150 cm3/g | Average value: 139 cm3/g Grade Count:8 |
| Maximum Moisture Content | 0.0900 - 0.900 | 0.0900 - 0.900 | Average value: 0.360 Grade Count:3 |
| Linear Mold Shrinkage | 0.00100 - 0.0200 cm/cm | 0.00100 - 0.0200 in/in | Average value: 0.00329 cm/cm Grade Count:92 |
| Linear Mold Shrinkage, 6.35 mm section | 0.00400 cm/cm | 0.00400 in/in | Average value: 0.00400 cm/cm Grade Count:4 |
| Linear Mold Shrinkage, Transverse | 0.00150 - 0.0116 cm/cm | 0.00150 - 0.0116 in/in | Average value: 0.00698 cm/cm Grade Count:34 |
| Melt Flow | 1.00 - 40.0 g/10 min | 1.00 - 40.0 g/10 min | Average value: 19.5 g/10 min Grade Count:17 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 80.0 - 100 | 80.0 - 100 | Average value: 93.7 Grade Count:5 |
| Hardness, Rockwell R | 98.0 - 125 | 98.0 - 125 | Average value: 120 Grade Count:33 |
| Ball Indentation Hardness | 131 - 340 MPa | 19000 - 49300 psi | Average value: 307 MPa Grade Count:10 |
| Tensile Strength, Ultimate | 37.4 - 299 MPa | 5420 - 43400 psi | Average value: 201 MPa Grade Count:70 |
| 95.0 - 342.669 MPa @Temperature -40.0 - 149 °C | 13800 - 49700.1 psi @Temperature -40.0 - 300 °F | Average value: 112 MPa Grade Count:6 | |
| 90.0 - 125 MPa @Temperature 130 - 175 °C | 13100 - 18100 psi @Temperature 266 - 347 °F | Average value: 112 MPa Grade Count:2 | |
| 90.0 - 125 MPa @Time 1.80e+7 - 7.20e+7 sec | 13100 - 18100 psi @Time 5000 - 20000 hour | Average value: 112 MPa Grade Count:2 | |
| 12.62 - 299.36 MPa @Strain 0.220 - 6.93 % | 1830 - 43419 psi @Strain 0.220 - 6.93 % | Average value: 112 MPa Grade Count:1 | |
| 12.62 - 299.36 MPa @Temperature -20.0 - 220 °C | 1830 - 43419 psi @Temperature -4.00 - 428 °F | Average value: 112 MPa Grade Count:1 | |
| Tensile Strength, Yield | 130 - 265 MPa | 18900 - 38400 psi | Average value: 211 MPa Grade Count:46 |
| 131 - 131 MPa @Temperature 93.3 - 93.3 °C | 19000 - 19000 psi @Temperature 200 - 200 °F | Average value: 131 MPa Grade Count:1 | |
| Elongation at Break | 1.00 - 5.00 % | 1.00 - 5.00 % | Average value: 2.43 % Grade Count:95 |
| 1.80 - 2.70 % @Temperature -40.0 - 149 °C | 1.80 - 2.70 % @Temperature -40.0 - 300 °F | Average value: 2.25 % Grade Count:3 | |
| Elongation at Yield | 1.00 - 3.70 % | 1.00 - 3.70 % | Average value: 2.63 % Grade Count:13 |
| Modulus of Elasticity | 10.2 - 18.7 GPa | 1480 - 2710 ksi | Average value: 15.7 GPa Grade Count:73 |
| 5.818 - 19.788 GPa @Temperature -40.0 - 200 °C | 843.8 - 2870.0 ksi @Temperature -40.0 - 392 °F | Average value: 11.0 GPa Grade Count:5 | |
| Flexural Yield Strength | 216 - 425 MPa | 31300 - 61600 psi | Average value: 326 MPa Grade Count:86 |
| 175 - 455.054 MPa @Temperature -40.0 - 149 °C | 25400 - 66000.1 psi @Temperature -40.0 - 300 °F | Average value: 264 MPa Grade Count:6 | |
| Flexural Modulus | 7.90 - 17.2 GPa | 1150 - 2500 ksi | Average value: 13.8 GPa Grade Count:92 |
| 6.50 - 19.0985 GPa @Temperature -40.0 - 149 °C | 943 - 2770.04 ksi @Temperature -40.0 - 300 °F | Average value: 9.85 GPa Grade Count:9 | |
| Shear Modulus | 0.100 - 3.00 GPa @Temperature 0.000 - 350 °C | 14.5 - 435 ksi @Temperature 32.0 - 662 °F | Average value: 1.34 GPa Grade Count:1 |
| Izod Impact, Notched | 1.01 - 6.51 J/cm | 1.90 - 12.2 ft-lb/in | Average value: 1.94 J/cm Grade Count:57 |
| 1.10 - 7.36782 J/cm @Temperature -40.0 - 149 °C | 2.06 - 13.8029 ft-lb/in @Temperature -40.0 - 300 °F | Average value: 2.61 J/cm Grade Count:4 | |
| Izod Impact, Unnotched | 9.61 - 70.0 J/cm | 18.0 - 131 ft-lb/in | Average value: 15.3 J/cm Grade Count:23 |
| Izod Impact, Notched (ISO) | 12.0 - 25.0 kJ/m2 | 5.71 - 11.9 ft-lb/in2 | Average value: 15.7 kJ/m2 Grade Count:20 |
| 11.0 - 15.0 kJ/m2 @Temperature -30.0 - -30.0 °C | 5.23 - 7.14 ft-lb/in2 @Temperature -22.0 - -22.0 °F | Average value: 13.0 kJ/m2 Grade Count:6 | |
| Izod Impact, Unnotched (ISO) | 54.0 - 103 kJ/m2 | 25.7 - 49.0 ft-lb/in2 | Average value: 86.8 kJ/m2 Grade Count:4 |
| 47.0 - 96.0 kJ/m2 @Temperature -30.0 - -30.0 °C | 22.4 - 45.7 ft-lb/in2 @Temperature -22.0 - -22.0 °F | Average value: 80.8 kJ/m2 Grade Count:4 | |
| Charpy Impact Unnotched | 5.20 J/cm2 - NB | 24.7 ft-lb/in2 - NB | Average value: 8.56 J/cm2 Grade Count:48 |
| 4.60 J/cm2 - NB @Temperature -40.0 - 30.0 °C | 21.9 ft-lb/in2 - NB @Temperature -40.0 - 86.0 °F | Average value: 7.93 J/cm2 Grade Count:32 | |
| Charpy Impact, Notched | 0.500 - 4.70 J/cm2 | 2.38 - 22.4 ft-lb/in2 | Average value: 1.88 J/cm2 Grade Count:49 |
| 0.350 - 4.50 J/cm2 @Temperature -40.0 - 30.0 °C | 1.67 - 21.4 ft-lb/in2 @Temperature -40.0 - 86.0 °F | Average value: 1.38 J/cm2 Grade Count:29 | |
| Dart Drop, Total Energy | 9.99 - 23.5 J @Temperature -20.0 - -20.0 °C | 7.37 - 17.3 ft-lb @Temperature -4.00 - -4.00 °F | Average value: 16.7 J Grade Count:1 |
| 9.99 - 23.5 J @Thickness 3.18 - 3.18 mm | 7.37 - 17.3 ft-lb @Thickness 0.125 - 0.125 in | Average value: 16.7 J Grade Count:1 | |
| Puncture Energy | 2.80 - 23.8 J @Temperature -30.0 - -30.0 °C | 2.07 - 17.6 ft-lb @Temperature -22.0 - -22.0 °F | Average value: 9.80 J Grade Count:2 |
| Tensile Creep Modulus, 1000 hours | 5400 - 8000 MPa | 783000 - 1.16e+6 psi | Average value: 7360 MPa Grade Count:5 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+10 - 1.00e+17 ohm-cm | 1.00e+10 - 1.00e+17 ohm-cm | Average value: 3.06e+15 ohm-cm Grade Count:60 |
| Surface Resistance | 1.00e+10 - 1.00e+16 ohm | 1.00e+10 - 1.00e+16 ohm | Average value: 3.30e+14 ohm Grade Count:35 |
| Dielectric Constant | 3.50 - 14.0 | 3.50 - 14.0 | Average value: 4.99 Grade Count:25 |
| Dielectric Strength | 1.97 - 90.0 kV/mm | 50.0 - 2290 kV/in | Average value: 34.3 kV/mm Grade Count:46 |
| Dissipation Factor | 0.00900 - 0.320 | 0.00900 - 0.320 | Average value: 0.0815 Grade Count:17 |
| Arc Resistance | 93.0 - 135 sec | 93.0 - 135 sec | Average value: 116 sec Grade Count:6 |
| Comparative Tracking Index | 350 - 600 V | 350 - 600 V | Average value: 534 V Grade Count:38 |
| Hot Wire Ignition, HWI | 1.00 - 30.0 sec | 1.00 - 30.0 sec | Average value: 17.1 sec Grade Count:4 |
| High Amp Arc Ignition, HAI | 1.00 - 120 arcs | 1.00 - 120 arcs | Average value: 90.3 arcs Grade Count:4 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 0.0500 - 500 μm/m-°C | 0.0278 - 278 μin/in-°F | Average value: 31.3 μm/m-°C Grade Count:41 |
| CTE, linear, Transverse to Flow | 0.500 - 88.0 μm/m-°C | 0.278 - 48.9 μin/in-°F | Average value: 47.1 μm/m-°C Grade Count:14 |
| Specific Heat Capacity | 1.30 J/g-°C | 0.311 BTU/lb-°F | Average value: 1.30 J/g-°C Grade Count:6 |
| Thermal Conductivity | 0.350 - 0.533 W/m-K | 2.43 - 3.70 BTU-in/hr-ft2-°F | Average value: 0.387 W/m-K Grade Count:9 |
| Melting Point | 220 - 325 °C | 428 - 617 °F | Average value: 265 °C Grade Count:66 |
| Maximum Service Temperature, Air | 100 - 250 °C | 212 - 482 °F | Average value: 180 °C Grade Count:25 |
| Deflection Temperature at 0.46 MPa (66 psi) | 240 - 263 °C | 464 - 505 °F | Average value: 255 °C Grade Count:55 |
| Deflection Temperature at 1.8 MPa (264 psi) | 210 - 285 °C | 410 - 545 °F | Average value: 253 °C Grade Count:97 |
| Deflection Temperature at 8.0 MPa | 175 - 249 °C | 347 - 480 °F | Average value: 213 °C Grade Count:12 |
| Vicat Softening Point | 200 - 260 °C | 392 - 500 °F | Average value: 244 °C Grade Count:22 |
| Decomposition Temperature | 310 °C | 590 °F | Average value: 310 °C Grade Count:6 |
| UL RTI, Electrical | 115 - 120 °C | 239 - 248 °F | Average value: 119 °C Grade Count:5 |
| UL RTI, Mechanical with Impact | 110 - 130 °C | 230 - 266 °F | Average value: 114 °C Grade Count:3 |
| UL RTI, Mechanical without Impact | 115 - 130 °C | 239 - 266 °F | Average value: 121 °C Grade Count:3 |
| Flammability, UL94 | HB - V-0 | HB - V-0 | Grade Count:64 |
| Oxygen Index | 23.0 - 32.0 % | 23.0 - 32.0 % | Average value: 27.3 % Grade Count:10 |
| Glow Wire Test | 649 - 960 °C | 1200 - 1760 °F | Average value: 750 °C Grade Count:15 |
| Shrinkage | 0.100 - 0.100 % @Temperature 120 - 120 °C | 0.100 - 0.100 % @Temperature 248 - 248 °F | Average value: 0.100 % Grade Count:1 |
| 0.100 - 0.100 % @Time 14400 - 14400 sec | 0.100 - 0.100 % @Time 4.00 - 4.00 hour | Average value: 0.100 % Grade Count:1 | |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 70.0 - 310 °C | 158 - 590 °F | Average value: 156 °C Grade Count:26 |
| Feed Temperature | 20.0 - 275 °C | 68.0 - 527 °F | Average value: 78.2 °C Grade Count:14 |
| Nozzle Temperature | 270 - 304 °C | 518 - 580 °F | Average value: 285 °C Grade Count:9 |
| Die Temperature | 300 - 320 °C | 572 - 608 °F | Average value: 311 °C Grade Count:8 |
| Melt Temperature | 143 - 325 °C | 290 - 617 °F | Average value: 291 °C Grade Count:52 |
| Mold Temperature | 50.0 - 124 °C | 122 - 255 °F | Average value: 88.2 °C Grade Count:55 |
| Drying Temperature | 70.0 - 121 °C | 158 - 250 °F | Average value: 81.7 °C Grade Count:45 |
| Dry Time | 2.00 - 12.0 hour | 2.00 - 12.0 hour | Average value: 3.72 hour Grade Count:37 |
| 2.00 - 4.00 hour @Temperature 79.4 - 79.4 °C | 2.00 - 4.00 hour @Temperature 175 - 175 °F | Average value: 3.00 hour Grade Count:2 | |
| Moisture Content | 0.0300 - 0.200 % | 0.0300 - 0.200 % | Average value: 0.150 % Grade Count:33 |
| Dew Point | -30.0 - -17.8 °C | -22.0 - 0.000 °F | Average value: -24.6 °C Grade Count:7 |
| Injection Pressure | 4.96 - 150 MPa | 720 - 21800 psi | Average value: 86.5 MPa Grade Count:25 |
| Hold Pressure | 50.0 - 100 MPa | 7250 - 14500 psi | Average value: 70.8 MPa Grade Count:9 |
| Back Pressure | 0.345 - 58.8 MPa | 50.0 - 8530 psi | Average value: 13.6 MPa Grade Count:11 |
| Screw Speed | 20.0 - 100 rpm | 20.0 - 100 rpm | Average value: 41.3 rpm Grade Count:11 |
| Hot-Working Temperature | 300 - 315 °C | 572 - 599 °F | Average value: 308 °C Grade Count:4 |