- 密度 [g/cm3]: 1.22
- 吸水率 [%]: 0.3
- 缺口沖擊強度: 0.427
- 拉伸強度 [MPa]: 118.0
- 斷裂伸長率 [%]: 89.0
- 彎曲強度 [MPa]: 68.0
- 彎曲模量 [MPa]: 3.03
- 硬度: 108.0
- 熱變形溫度 [℃]: 216.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.22 - 1.78 g/cc | 0.0441 - 0.0643 lb/in3 | Average value: 1.46 g/cc Grade Count:106 |
| Filler Content | 5.00 - 40.0 % | 5.00 - 40.0 % | Average value: 23.8 % Grade Count:66 |
| Water Absorption | 0.300 - 6.00 % | 0.300 - 6.00 % | Average value: 0.959 % Grade Count:66 |
| Water Absorption at Saturation | 0.800 - 5.50 % | 0.800 - 5.50 % | Average value: 3.08 % Grade Count:4 |
| Additive Loading | 15.0 - 50.0 % | 15.0 - 50.0 % | Average value: 28.8 % Grade Count:6 |
| Linear Mold Shrinkage | 0.000300 - 0.0200 cm/cm | 0.000300 - 0.0200 in/in | Average value: 0.00421 cm/cm Grade Count:103 |
| Linear Mold Shrinkage, 6.35 mm section | 0.00300 - 0.0140 cm/cm | 0.00300 - 0.0140 in/in | Average value: 0.00721 cm/cm Grade Count:33 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 108 - 120 | 108 - 120 | Average value: 118 Grade Count:29 |
| Tensile Strength, Ultimate | 68.0 - 250 MPa | 9860 - 36300 psi | Average value: 143 MPa Grade Count:102 |
| Tensile Strength, Yield | 118 - 179 MPa | 17100 - 26000 psi | Average value: 153 MPa Grade Count:4 |
| Elongation at Break | 1.00 - 7.00 % | 1.00 - 7.00 % | Average value: 3.25 % Grade Count:87 |
| Elongation at Yield | 2.50 - 5.00 % | 2.50 - 5.00 % | Average value: 3.54 % Grade Count:17 |
| Modulus of Elasticity | 3.45 - 15.5 GPa | 500 - 2250 ksi | Average value: 8.66 GPa Grade Count:100 |
| Flexural Yield Strength | 89.0 - 320 MPa | 12900 - 46400 psi | Average value: 211 MPa Grade Count:106 |
| Flexural Modulus | 3.03 - 14.8 GPa | 440 - 2150 ksi | Average value: 7.75 GPa Grade Count:104 |
| Compressive Yield Strength | 68.9 - 165 MPa | 10000 - 23900 psi | Average value: 114 MPa Grade Count:20 |
| Shear Strength | 76.0 - 79.0 MPa | 11000 - 11500 psi | Average value: 77.0 MPa Grade Count:3 |
| Izod Impact, Notched | 0.427 - 2.14 J/cm | 0.800 - 4.01 ft-lb/in | Average value: 0.969 J/cm Grade Count:84 |
| Izod Impact, Unnotched | 3.74 - 13.3 J/cm | 7.00 - 25.0 ft-lb/in | Average value: 7.80 J/cm Grade Count:74 |
| Charpy Impact Unnotched | 4.50 J/cm2 - NB | 21.4 ft-lb/in2 - NB | Average value: 6.04 J/cm2 Grade Count:16 |
| 2.70 - 6.00 J/cm2 @Temperature -40.0 - -30.0 °C | 12.8 - 28.6 ft-lb/in2 @Temperature -40.0 - -22.0 °F | Average value: 4.42 J/cm2 Grade Count:10 | |
| Charpy Impact, Notched | 0.350 - 1.50 J/cm2 | 1.67 - 7.14 ft-lb/in2 | Average value: 1.14 J/cm2 Grade Count:11 |
| 0.300 - 0.300 J/cm2 @Temperature -40.0 - -40.0 °C | 1.43 - 1.43 ft-lb/in2 @Temperature -40.0 - -40.0 °F | Average value: 0.300 J/cm2 Grade Count:1 | |
| Coefficient of Friction | 0.130 - 0.620 | 0.130 - 0.620 | Average value: 0.239 Grade Count:15 |
| Coefficient of Friction, Static | 0.110 - 0.520 | 0.110 - 0.520 | Average value: 0.193 Grade Count:15 |
| K (wear) Factor | 24.2 - 50.4 x 10-8 mm3/N-M | 12.0 - 25.0 x 10-10 in3-min/ft-lb-hr | Average value: 34.2 x 10-8 mm3/N-M Grade Count:3 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+13 - 1.00e+16 ohm-cm | 1.00e+13 - 1.00e+16 ohm-cm | Average value: 1.53e+15 ohm-cm Grade Count:62 |
| Surface Resistance | 1.00e+12 - 1.00e+15 ohm | 1.00e+12 - 1.00e+15 ohm | Average value: 6.40e+13 ohm Grade Count:19 |
| Insulation Resistance | 1.00e+12 ohm | 1.00e+12 ohm | Average value: 1.00e+12 ohm Grade Count:17 |
| Dielectric Constant | 3.70 - 4.20 | 3.70 - 4.20 | Average value: 3.79 Grade Count:18 |
| Dielectric Strength | 18.1 - 19.7 kV/mm | 460 - 500 kV/in | Average value: 19.5 kV/mm Grade Count:18 |
| Dissipation Factor | 0.0130 - 0.0200 | 0.0130 - 0.0200 | Average value: 0.0158 Grade Count:18 |
| Arc Resistance | 100 - 120 sec | 100 - 120 sec | Average value: 112 sec Grade Count:9 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 19.8 - 55.8 μm/m-°C | 11.0 - 31.0 μin/in-°F | Average value: 34.2 μm/m-°C Grade Count:29 |
| Thermal Conductivity | 0.220 - 0.519 W/m-K | 1.53 - 3.60 BTU-in/hr-ft2-°F | Average value: 0.383 W/m-K Grade Count:26 |
| Melting Point | 249 - 275 °C | 480 - 527 °F | Average value: 256 °C Grade Count:6 |
| Maximum Service Temperature, Air | 90.0 - 160 °C | 194 - 320 °F | Average value: 133 °C Grade Count:19 |
| Deflection Temperature at 0.46 MPa (66 psi) | 216 - 268 °C | 420 - 514 °F | Average value: 247 °C Grade Count:46 |
| Deflection Temperature at 1.8 MPa (264 psi) | 199 - 254 °C | 390 - 489 °F | Average value: 238 °C Grade Count:86 |
| Vicat Softening Point | 200 - 250 °C | 392 - 482 °F | Average value: 243 °C Grade Count:16 |
| Flammability, UL94 | HB - V-0 | HB - V-0 | Grade Count:76 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 271 - 293 °C | 520 - 560 °F | Average value: 286 °C Grade Count:53 |
| Nozzle Temperature | 280 - 300 °C | 536 - 572 °F | Average value: 290 °C Grade Count:17 |
| Melt Temperature | 260 - 310 °C | 500 - 590 °F | Average value: 294 °C Grade Count:63 |
| Mold Temperature | 65.6 - 121 °C | 150 - 250 °F | Average value: 90.7 °C Grade Count:98 |
| Drying Temperature | 75.0 - 107 °C | 167 - 225 °F | Average value: 85.2 °C Grade Count:59 |
| Dry Time | 4.00 hour | 4.00 hour | Average value: 4.00 hour Grade Count:30 |
| Moisture Content | 0.200 % | 0.200 % | Average value: 0.200 % Grade Count:37 |
| Dew Point | -17.8 °C | 0.000 °F | Average value: -17.8 °C Grade Count:37 |
| Injection Pressure | 68.9 - 124 MPa | 10000 - 18000 psi | Average value: 100 MPa Grade Count:72 |