- 熔體流動速率 [g/10min]: 3.0
- 密度 [g/cm3]: 1.2
- 吸水率 [%]: 0.5
- 缺口沖擊強度: 0.2
- 拉伸強度 [MPa]: 70.0
- 斷裂伸長率 [%]: 78.0
- 彎曲強度 [MPa]: 52.0
- 彎曲模量 [MPa]: 2.50
- 硬度: 115.0
- 熱變形溫度 [℃]: 140.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.20 - 1.32 g/cc | 0.0434 - 0.0477 lb/in3 | Average value: 1.26 g/cc Grade Count:23 |
| Filler Content | 15.0 - 20.0 % | 15.0 - 20.0 % | Average value: 18.8 % Grade Count:6 |
| Water Absorption | 0.500 - 7.70 % | 0.500 - 7.70 % | Average value: 2.13 % Grade Count:11 |
| Moisture Absorption at Equilibrium | 2.00 - 2.50 % | 2.00 - 2.50 % | Average value: 2.18 % Grade Count:5 |
| Viscosity Measurement | 1.34 - 145 | 1.34 - 145 | Average value: 49.3 Grade Count:3 |
| Linear Mold Shrinkage | 0.00200 - 0.0250 cm/cm | 0.00200 - 0.0250 in/in | Average value: 0.0118 cm/cm Grade Count:23 |
| Linear Mold Shrinkage, Transverse | 0.0110 - 0.0141 cm/cm | 0.0110 - 0.0141 in/in | Average value: 0.0132 cm/cm Grade Count:4 |
| Melt Flow | 3.00 - 25.0 g/10 min | 3.00 - 25.0 g/10 min | Average value: 10.3 g/10 min Grade Count:3 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 115 - 122 | 115 - 122 | Average value: 119 Grade Count:6 |
| Tensile Strength, Ultimate | 52.0 - 93.0 MPa | 7540 - 13500 psi | Average value: 70.5 MPa Grade Count:17 |
| 40.0 - 100 MPa @Temperature -40.0 - 80.0 °C | 5800 - 14500 psi @Temperature -40.0 - 176 °F | Average value: 71.0 MPa Grade Count:1 | |
| Tensile Strength, Yield | 70.0 - 95.0 MPa | 10200 - 13800 psi | Average value: 83.1 MPa Grade Count:6 |
| Elongation at Break | 1.00 - 52.0 % | 1.00 - 52.0 % | Average value: 12.4 % Grade Count:19 |
| Modulus of Elasticity | 1.80 - 6.60 GPa | 261 - 957 ksi | Average value: 4.11 GPa Grade Count:12 |
| Flexural Yield Strength | 78.0 - 245 MPa | 11300 - 35500 psi | Average value: 124 MPa Grade Count:18 |
| 57.0 - 160 MPa @Temperature -40.0 - 80.0 °C | 8270 - 23200 psi @Temperature -40.0 - 176 °F | Average value: 113 MPa Grade Count:1 | |
| Flexural Modulus | 2.50 - 6.60 GPa | 363 - 957 ksi | Average value: 4.04 GPa Grade Count:18 |
| 1.60 - 6.40 GPa @Temperature -40.0 - 80.0 °C | 232 - 928 ksi @Temperature -40.0 - 176 °F | Average value: 4.28 GPa Grade Count:1 | |
| Izod Impact, Notched | 0.200 - 1.55 J/cm | 0.375 - 2.90 ft-lb/in | Average value: 0.546 J/cm Grade Count:14 |
| 0.350 - 0.450 J/cm @Temperature -40.0 - -40.0 °C | 0.656 - 0.843 ft-lb/in @Temperature -40.0 - -40.0 °F | Average value: 0.400 J/cm Grade Count:1 | |
| Izod Impact, Notched (ISO) | 6.00 - 11.0 kJ/m2 | 2.86 - 5.23 ft-lb/in2 | Average value: 8.13 kJ/m2 Grade Count:3 |
| 8.00 - 8.00 kJ/m2 @Temperature -30.0 - -30.0 °C | 3.81 - 3.81 ft-lb/in2 @Temperature -22.0 - -22.0 °F | Average value: 8.00 kJ/m2 Grade Count:1 | |
| Charpy Impact Unnotched | 3.70 J/cm2 - NB | 17.6 ft-lb/in2 - NB | Average value: 6.18 J/cm2 Grade Count:6 |
| 0.600 - 4.30 J/cm2 @Temperature -30.0 - -20.0 °C | 2.86 - 20.5 ft-lb/in2 @Temperature -22.0 - -4.00 °F | Average value: 1.97 J/cm2 Grade Count:3 | |
| Charpy Impact, Notched | 0.300 - 1.50 J/cm2 | 1.43 - 7.14 ft-lb/in2 | Average value: 0.923 J/cm2 Grade Count:7 |
| 0.100 - 1.20 J/cm2 @Temperature -30.0 - -20.0 °C | 0.476 - 5.71 ft-lb/in2 @Temperature -22.0 - -4.00 °F | Average value: 0.500 J/cm2 Grade Count:4 | |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+10 - 1.00e+15 ohm-cm | 1.00e+10 - 1.00e+15 ohm-cm | Average value: 4.72e+14 ohm-cm Grade Count:13 |
| Surface Resistance | 1.00e+10 - 1.00e+15 ohm | 1.00e+10 - 1.00e+15 ohm | Average value: 1.70e+14 ohm Grade Count:6 |
| Dielectric Constant | 3.70 - 6.00 | 3.70 - 6.00 | Average value: 4.38 Grade Count:4 |
| Dielectric Strength | 16.0 - 90.0 kV/mm | 406 - 2290 kV/in | Average value: 40.1 kV/mm Grade Count:8 |
| Comparative Tracking Index | 450 - 600 V | 450 - 600 V | Average value: 540 V Grade Count:5 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 52.2 - 70.0 μm/m-°C | 29.0 - 38.9 μin/in-°F | Average value: 60.1 μm/m-°C Grade Count:3 |
| Melting Point | 255 - 262 °C | 491 - 504 °F | Average value: 258 °C Grade Count:10 |
| Maximum Service Temperature, Air | 80.0 - 220 °C | 176 - 428 °F | Average value: 140 °C Grade Count:3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 140 - 250 °C | 284 - 482 °F | Average value: 219 °C Grade Count:16 |
| Deflection Temperature at 1.8 MPa (264 psi) | 75.0 - 230 °C | 167 - 446 °F | Average value: 138 °C Grade Count:17 |
| Vicat Softening Point | 200 - 260 °C | 392 - 500 °F | Average value: 233 °C Grade Count:4 |
| Flammability, UL94 | HB - V-0 | HB - V-0 | Grade Count:16 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 270 - 310 °C | 518 - 590 °F | Average value: 293 °C Grade Count:3 |
| Melt Temperature | 250 - 310 °C | 482 - 590 °F | Average value: 283 °C Grade Count:13 |
| Mold Temperature | 49.0 - 120 °C | 120 - 248 °F | Average value: 85.8 °C Grade Count:15 |
| Drying Temperature | 71.0 - 110 °C | 160 - 230 °F | Average value: 86.4 °C Grade Count:11 |
| Dry Time | 2.00 - 6.00 hour | 2.00 - 6.00 hour | Average value: 3.81 hour Grade Count:8 |
| Moisture Content | 0.150 - 0.200 % | 0.150 - 0.200 % | Average value: 0.190 % Grade Count:5 |
| Injection Pressure | 30.0 - 124 MPa | 4350 - 18000 psi | Average value: 87.0 MPa Grade Count:5 |